Photocatalyst Bi3Sb3Zn2O14 with visible light response

A bi3sb3zn2o14, photocatalyst technology, applied in physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, inorganic chemistry, etc., can solve the problems of limited types of photocatalysts, low light conversion efficiency, poor stability, etc. , to achieve the effects of excellent catalytic performance, simple preparation method and low cost

Active Publication Date: 2014-01-22
东台城东科技创业园管理有限公司
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although photocatalysis research has been carried out for several years, the types of photocatalysts with visible light response reported are still very limited, and there are still problems such as low photoconversion efficiency, poor stability and narrow spectral response range, so the research and development of new photocatalysts with Efficient photocatalysts responsive to visible light are highly desirable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) 99.9% analytically pure chemical raw material Bi 2 o 3 , Sb 2 o 5 and ZnO, by Bi 3 Sb 3 Zn 2 o 14 Chemical formula weighing ingredients.

[0019] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind until fine, take it out and dry it, and pass through a 200-mesh sieve.

[0020] (3) Pre-fire the uniformly mixed powder in step (2) at 770°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then pulverize it with a ball mill to make the particle diameter smaller than 2 μm, and then you can get bismuthate Bi 3 Sb 3 Zn 2 o 14 powder.

[0021] The prepared photocatalyst can remove 98.4% of methyl orange in 120 minutes under the irradiation of visible light with a wavelength greater than 420nm.

Embodiment 2

[0023] (1) 99.9% analytically pure chemical raw material Bi 2 o 3 , Sb 2 o 5 and ZnO, by Bi 3 Sb 3 Zn 2 o 14 Chemical formula weighing ingredients.

[0024] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind until fine, take it out and dry it, and pass through a 200-mesh sieve.

[0025] (3) Pre-fire the uniformly mixed powder in step (2) at 790°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then pulverize it with a ball mill to make the particle diameter smaller than 2 μm, and then you can get bismuthate Bi 3 Sb 3 Zn 2 o 14 powder.

[0026] The prepared photocatalyst can remove 99.2% of methyl orange in 120 minutes under the irradiation of visible light with a wavelength greater than 420nm.

Embodiment 3

[0028] (1) 99.9% analytically pure chemical raw material Bi 2 o 3 , Sb 2 o 5 and ZnO, by Bi 3 Sb 3 Zn 2 o 14 Chemical formula weighing ingredients.

[0029] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind until fine, take it out and dry it, and pass through a 200-mesh sieve.

[0030] (3) Pre-fire the uniformly mixed powder in step (2) at 800°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then use a ball mill to make the particle diameter smaller than 2 μm, and then you can get bismuthate Bi 3 Sb 3 Zn 2 o 14 powder.

[0031] The prepared photocatalyst can remove 98.7% of methyl orange in 120 minutes under the irradiation of visible light with wavelength greater than 420nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bismuthate photocatalyst Bi3Sb3Zn2O14 with visible light response and a preparation method thereof. The chemical composition formula of the bismuthate photocatalyst is Bi3Sb3Zn2O14. The invention also discloses the preparation method of the material. The preparation method is simple and is low in cost. The prepared photocatalyst has excellent catalytic performance, has the function of decomposing harmful chemical substances when irradiated by visible light and has good stability and good application prospect.

Description

technical field [0001] The invention relates to a photocatalyst Bi which responds to visible light 3 Sb 3 Zn 2 o 14 , belongs to the field of inorganic photocatalytic materials. Background technique [0002] With the development of society and economy, people pay more and more attention to energy and ecological environment. Solving the problems of energy shortage and environmental pollution is an urgent need to achieve sustainable development, improve people's quality of life and ensure national security. [0003] Since the late 1970s, people have proposed the use of photocatalysts to decompose organic substances such as pesticides and odorous substances in water and the atmosphere, and self-cleaning of solid surfaces coated with photocatalysts. The principle of photocatalytic reaction is that after the photocatalyst absorbs photons higher than its bandgap energy, holes and electrons are generated, and these holes and electrons undergo oxidation and reduction reactions r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/18C01G30/00
Inventor 方亮匡小军巩美露
Owner 东台城东科技创业园管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap