Electrothermal film and preparation method thereof

A technology of electric heating film and parts by weight, applied in the direction of electric heating devices, ohmic resistance heating, electrical components, etc., can solve the problems of low thermal efficiency, affecting service life, electromagnetic radiation hazards, etc., and achieve improved conductivity, thermal stability, and thermal efficiency high effect

Inactive Publication Date: 2014-01-22
TIANJIN WANGDONG NEW MATERIAL RES DEV
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The heating tools that people use now are generally resistance wires, etc. This heating tool has the hazards of electromagnetic radiation during the heating process. In addition, the heating and heat dissipation area of ​​the resistance wire is small, and the thermal efficiency is low; in addition, the resistance wire is made of metals such as copper and aluminum. It is easy to cause waste of metal, and the resistance wire is heated for a long time, which is prone to oxidation and affects the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrothermal film and preparation method thereof
  • Electrothermal film and preparation method thereof
  • Electrothermal film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An electrothermal film is prepared from components comprising the following parts by weight:

[0032]

[0033] The preparation method of the above-mentioned electrothermal film comprises the following steps:

[0034] (1) Weigh the above-mentioned components according to weight and volume;

[0035] (2) 10gSnCl 4 ·5H 2 O was added to 48ml of absolute ethanol, stirred to make it evenly mixed;

[0036] (3) Add 0.4gSbCl 3 , 0.2gTiCl 4 , 0.3gFeCl 3 and 0.2gBiCl 3 Add to a mixed solution of 16ml of isopropanol, 32ml of methanol and 10ml of 10M hydrochloric acid, stir to mix evenly;

[0037] (4) Mix the mixed solution obtained in step (2) and step (3), and stir evenly to obtain the electric heating film stock solution.

[0038] (5) Clean the surface of the substrate purple sand with alcohol and heat it to 500°C.

[0039] (6) Heat the electrothermal film stock solution obtained in step (4) to 50°C, spray the heated electrothermal film stock solution onto the surface ...

Embodiment 2

[0043] An electrothermal film is prepared from components comprising the following parts by weight:

[0044]

[0045] The preparation method of the above-mentioned electrothermal film comprises the following steps:

[0046] (1) Weigh the above-mentioned components according to weight and volume;

[0047] (2) 9gSnCl 4 ·5H 2 O was added to 64ml of absolute ethanol, stirred to make it evenly mixed;

[0048] (3) Add 0.5gSbCl 3 , 0.4gTiCl 4 , 0.5gFeCl 3 , 0.3g BiCl 3 and 0.1gBr 2 Add to a mixed solution of 24ml of isopropanol, 32ml of methanol and 10ml of 10M hydrochloric acid, stir to mix evenly;

[0049] (4) Mix the mixed solution obtained in step (2) and step (3), and stir evenly to obtain the electric heating film stock solution.

[0050] (5) Clean the surface of the substrate quartz glass with alcohol and heat it to 600°C.

[0051] (6) Heat the electrothermal film stock solution obtained in step (4) to 50°C, spray the heated electrothermal film stock solution on t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an electrothermal film and a preparation method thereof. The electrothermal film is prepared from the following components in parts by weight: 85 to 100 parts of stannic chloride, 3 to 6 parts of antimony butter, 2 to 4 parts of titanium tetrachloride, 2 to 5 parts of ferric trichloride, 1 to 3 parts of bismuth trichloride, 10 to 15 parts of hydrochloric acid, 20 to 30 parts of isopropyl alcohol, 20 to 40 parts of methanol and 50 to 80 parts of absolute ethyl alcohol. All the components are weighed and mixed to obtain a stock solution of the electrothermal film; the stock solution of the electrothermal film is sprayed to the surface of a base material by adopting the metal salt solution spray pyrolysis method. The electrothermal film and the preparation method thereof have the advantages and the active effects that the electrothermal film is high in heating efficiency; the film forming speed can reach 80nm/min; the preparation method is suitable for manufacturing of a large-area film and large-scale production.

Description

technical field [0001] The invention belongs to the technical field of electric heating film, and in particular relates to an electric heating film and a preparation method thereof. Background technique [0002] With the rapid development of science and technology, communication tools, computers and a large number of household appliances have entered our lives. While enjoying the convenience and comfort brought by modernization, we are also threatened by the deteriorating electromagnetic environment. The heating tools that people use now are generally resistance wires, etc. This heating tool has the hazards of electromagnetic radiation during the heating process. In addition, the heating and heat dissipation area of ​​the resistance wire is small, and the thermal efficiency is low; in addition, the resistance wire is made of metals such as copper and aluminum. It is easy to cause waste of metal, and the resistance wire is heated for a long time, which is prone to oxidation a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/10H05B3/20
Inventor 孙甫
Owner TIANJIN WANGDONG NEW MATERIAL RES DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap