PVC (Polyvinyl Chloride) diaphragm and manufacturing method thereof

A manufacturing method and technology of PVC resin, applied in the field of PVC diaphragm manufacturing, can solve the problems of expensive reinforcing agent and high production cost, improve melt strength and uniformity, prevent low temperature cracking, slow down melt fracture and seepage out effect

Active Publication Date: 2014-01-29
江苏晨洁家化制造有限公司
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional PVC diaphragm is made by mixing PVC resin with stabilizers, processing aids and reinforcing agents, and then plasticized, extruded, calendered, and peeled off. The strength of PVC diaphragms mainly depends on th...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC (Polyvinyl Chloride) diaphragm and manufacturing method thereof
  • PVC (Polyvinyl Chloride) diaphragm and manufacturing method thereof
  • PVC (Polyvinyl Chloride) diaphragm and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The manufacturing method of the PVC diaphragm of the present invention comprises the following steps in turn: (1) Prepare raw materials according to the following components and weight content, PVC resin: 100 parts; 719 type oxidized polyethylene wax: 1.0 part; auxiliary stabilizer: 0.015 parts ; MBS resin: 3.5 parts; processing aid ACR: 0.9 part; solid internal lubricant: 0.45 part; external lubricant: 0.1 part; polyvinyl chloride resin PX1000: 0.3 part; ultramarine blue pigment: 0.011 part; part; the auxiliary stabilizer is composed of methyl tin and antimony mercaptide, and the weight ratio of the two is 1:4; (2) First, put each raw material into the kneading pot and knead until uniform, and the discharge temperature of the kneading pot is 80°C ;Then let the mixed material enter the cooling pot to cool down and stir, and the temperature of the cold pot is 60°C; then the mixed material is extruded and plasticized into a paste by a screw extruder, and the extrusion temp...

Embodiment 2

[0023] The manufacturing method of the PVC diaphragm of the present invention comprises the following steps in turn: (1) Prepare raw materials according to the following components and weight content, PVC resin: 100 parts; 719 type oxidized polyethylene wax: 1.1 parts; auxiliary stabilizer: 0.016 parts ; MBS resin: 3.7 parts; processing aid ACR: 1.0 part; solid internal lubricant: 0.50 part; external lubricant: 0.15 part; polyvinyl chloride resin PX1000: 0.35 part; ultramarine blue pigment: 0.012 part; parts; the auxiliary stabilizer is composed of methyl tin and antimony mercaptide, and the weight ratio of the two is 1:4; (2) First, put all the raw materials into the kneading pot and knead until uniform, and the discharge temperature of the kneading pot is 85°C ; Then make the mixed material enter the cooling pot to cool down and stir, the temperature of the cold pot is 65 ° C; then the mixed material is extruded and plasticized into a paste by a screw extruder, and the extrus...

Embodiment 3

[0025] The manufacturing method of the PVC diaphragm of the present invention comprises the following steps in turn: (1) Prepare raw materials according to the following components and weight content, PVC resin: 100 parts; 719 type oxidized polyethylene wax: 1.2 parts; auxiliary stabilizer: 0.017 parts ; MBS resin: 4.0 parts; processing aid ACR: 1.1 parts; solid internal lubricant: 0.55 parts; external lubricant: 0.2 parts; polyvinyl chloride resin PX1000: 0.4 parts; ultramarine blue pigment: 0.013 parts; parts; the auxiliary stabilizer is composed of methyl tin and antimony mercaptide, and the weight ratio of the two is 1:4; (2) firstly put each raw material into the kneading pot and knead until uniform, and the discharge temperature of the kneading pot is 90°C ;Then make the mixed material enter the cooling pot to cool down and stir, the temperature of the cooling pot is 70°C; then the mixed material is extruded and plasticized into a paste by the screw extruder, and the extr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Dropping pointaaaaaaaaaa
Acid valueaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a PVC (Polyvinyl Chloride) diaphragm and a manufacturing method thereof. The PVC diaphragm is manufactured by using the raw materials: 100 parts of PVC resin, 1.0-1.2 parts of 719 type oxidized polyethylene wax, 0.015-0.017 part of auxiliary stabilizer, 3.5-4.0 parts of MBS (Methacrylate-Butadiene-Styrene) resin, 0.9-1.1 parts of ACR (Acrylate), 0.45-0.55 part of internal lubricant, 0.1-0.2 part of external lubricant, 0.3-0.4 part of PX1000, 0.011-0.013 part of ultramarine and 0.004-0.005 part of disperse purple, wherein the auxiliary stabilizer is composed of monomethyltin and antimony mercaptide which are in the weight ratio of 1:4. The manufacturing method of the PVC diaphragm comprises the steps: firstly, adding all the raw materials into a kneading pot to knead, and discharging when the temperature is up to 80-90 DEG C; entering a cooling pot, and discharging when the temperature is up to 60-70 DEG C; next, squeezing out the raw materials at the temperature of 120-160 DEG C; then, calendering the raw materials at the temperature of 180-200 DEG C to form a sheet; after stripping, cooling and shaping, cropping and winding. The PVC diaphragm is good in stability, high in strength and low in manufacturing cost.

Description

technical field [0001] The invention relates to a PVC diaphragm, and also relates to a manufacturing method of the PVC diaphragm. Background technique [0002] PVC film has good weather resistance, good flatness, easy affinity with most plastic inks, and has very obvious economy, so it is widely used in signs, panels, guard cards, credit cards and screen printing in the screen printing industry. Various decorative products. The traditional PVC diaphragm is made by mixing PVC resin with stabilizers, processing aids and reinforcing agents, and then plasticized, extruded, calendered, and peeled off. The strength of PVC diaphragms mainly depends on the ratio of reinforcing agents. The price of the reinforcing agent is relatively expensive, resulting in high production costs; and when the reinforcing agent is added to a certain amount, the strength will no longer increase significantly. Contents of the invention [0003] The primary purpose of the present invention is to over...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L51/00C08K5/57C08K5/56B29C69/02B29C47/00B29C43/24
Inventor 尤松
Owner 江苏晨洁家化制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap