A technology of epoxy resin and adhesive, which is applied in the direction of epoxy resin glue, adhesive, non-polymer adhesive additives, etc., can solve the problem that the viscosity and heat resistance are difficult to coordinate, so as to improve toughness and flame retardancy sexual effect

Inactive Publication Date: 2014-02-19
苏州威仕薄膜科技有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the combination of many resins and curing agents requires flame-retardant properties, and it is difficult to coordinate the viscosity and heat resistance. Theref

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An improved epoxy resin adhesive, comprising the following components in parts by weight: 65 parts of epoxy resin, 20 parts of aromatic amine curing agent, 5 parts of imidazole curing accelerator, 25 parts of nitrile rubber, 1 part of coupling agent 15 parts of diluent, 10 parts of phosphorus flame retardant, 5 parts of flexibilizer, 10 parts of calcium carbonate filler and appropriate amount of organic solvent.

[0015] Nitrile rubber is hydroxyl-terminated nitrile rubber.

[0016] The aromatic amine curing agent is diaminodiphenylmethane (DDM).

[0017] The imidazole curing accelerator is 2-methylimidazole.

[0018] The phosphorus-containing flame retardant is polyphosphate amine.

[0019] Coupling agents include γ-glycidoxypropyltrimethoxysilane.

[0020] Flexible and nonylphenol.

[0021] The organic solvent is ethanol.

Embodiment 2

[0023] An improved epoxy resin adhesive, comprising the following components in parts by weight: 75 parts of epoxy resin, 25 parts of aromatic amine curing agent, 10 parts of imidazole curing accelerator, 30 parts of nitrile rubber, 1.5 parts of coupling agent 20 parts, 20 parts of diluent, 15 parts of phosphorus flame retardant, 8 parts of flexibilizer, 12 parts of calcium carbonate filler and appropriate amount of organic solvent.

[0024] Nitrile rubber is hydroxyl-terminated nitrile rubber.

[0025] The aromatic amine curing agent is diaminodiphenyl sulfone (DDS).

[0026] The imidazole curing accelerators are 2-ethyl-4-methylimidazole and 2-phenylimidazole.

[0027] The phosphorus-containing flame retardant is tricresyl phosphate.

[0028] Coupling agents include γ-glycidoxypropyltrimethoxysilane.

[0029] Flexible and nonylphenol.

[0030] The organic solvent is acetone.

Embodiment 3

[0032] An improved epoxy resin adhesive, comprising the following components in parts by weight: 85 parts of epoxy resin, 30 parts of aromatic amine curing agent, 15 parts of imidazole curing accelerator, 35 parts of nitrile rubber, 2.5 parts of coupling agent 25 parts of diluent, 20 parts of phosphorus flame retardant, 10 parts of flexibilizer, 15 parts of calcium carbonate filler and appropriate amount of organic solvent.

[0033] Nitrile rubber is hydroxyl-terminated nitrile rubber.

[0034] The aromatic amine curing agent is 3,3-dichloro-4,4-diaminodiphenylmethane (MOCA).

[0035] The imidazole curing accelerators are 2-phenylimidazole and 2-phenyl-4-methylimidazole.

[0036] The phosphorus-containing flame retardant is polyphosphate amine.

[0037] Coupling agents include γ-glycidoxypropyltrimethoxysilane.

[0038] Flexible and nonylphenol.

[0039] The organic solvent is ethyl acetate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an improved epoxy resin adhesive which comprises the following components in parts by weight: 65-85 parts of epoxy resin, 20-30 parts of aromatic amine curing agent, 5-15 parts of imidazole curing accelerator, 25-35 parts of nitrile rubber, 1-2.5 parts of coupling agent, 15-25 parts of diluent, 10-20 parts of phosphorus based flame retardant, 5-10 parts of plasticizer, 10-15 parts of calcium carbonate filler and an appropriate amount of organic solvent. According to the improved epoxy resin adhesive, the tenacity of the epoxy resin adhesive can be improved by means of the addition of the hydroxyl-terminated nitrile rubber. The phosphorus-containing flame retardant can influence the glue overflow amount and the shelf life and improve the flame retardance of the adhesive; the tenacity can be improved by the plasticizer. Therefore, the epoxy resin adhesive has favourable flame retardance and tenacity and relatively high viscosity.

Description

Technical field: [0001] The invention relates to an epoxy resin composition, in particular to an epoxy resin adhesive. Background technique: [0002] With the rapid development of industries such as automobiles and electronics, the selection of epoxy resin materials used in the automobile and electronics industries is particularly important. At present, the combination of many resins and curing agents requires flame-retardant properties, and it is difficult to coordinate the viscosity and heat resistance. Therefore, in order to meet market considerations, it is currently necessary to provide an epoxy resin adhesive with good Flame retardant, heat resistance and viscosity properties. Invention content: [0003] The object of the present invention is to provide an improved epoxy resin adhesive, which has good toughness, flame retardancy, heat resistance and viscosity. [0004] In order to achieve the above object, an improved epoxy resin adhesive of the present invention i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/00C09J115/00C09J11/04C09J11/06
Inventor 孙加元
Owner 苏州威仕薄膜科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap