Flame-retardant wallpaper base paper and preparation method thereof

A technology for base paper and wallpaper, applied in the field of flame retardant wallpaper base paper and its preparation, can solve the problems of unsustainable flame retardant effect of wallpaper base paper, reduced flame retardant performance, yellowing and darkening of whiteness, etc., and achieves outstanding market competition. strength, improve surface strength, reduce the effect of lost paper

Active Publication Date: 2014-03-05
ZIBO OU MU SPECIAL PAPER
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flame retardant effect of the wallpaper base paper obtained by the existing method is not durable, and the whiteness is too low
Often when the base paper just produced is tested, the wallpaper base paper can have a good flame retardant effect and hi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant wallpaper base paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiments 1 to 5 are specific implementations of the flame-retardant wallpaper base paper of the present invention and its preparation method, wherein embodiment 1 is the best embodiment.

[0028] Example 1

[0029] In this example, the proportion of components is 65 parts by weight of softwood pulp fiber, 18 parts of chemical fiber is polyethylene terephthalate fiber, 10 parts of acrylic latex, and the flame retardant trishydroxymethyl phosphorus oxide (THPO) 2 parts, the modifier is dimethyl tin oxide and dibutyl tin dichloride mixed according to the mass ratio of 1:1, 0.2 parts of cationic polyacrylamide, 0.2 parts of wet strength agent PAE, fluorescent whitening agent BBU 0.08 parts.

[0030] The preparation method of the present embodiment is as follows:

[0031] a) Mix wood pulp fiber and chemical fiber in proportion, use a pulper to finely grind and decompose and beat, the beating degree is 29°SR, and the beating concentration is controlled at 3%;

[0032] ...

Embodiment 2

[0037] In this example, the component distribution ratio is 70 parts of hardwood pulp fiber, 17 parts of nylon fiber, 15 parts of acrylic latex, 3 parts of flame retardant diphenyl phosphate (BDP), and 1 part of dimethyl tin oxide as a modifier , 0.1 part of dry strength agent chitosan, 0.5 part of wet strength agent PAE, 0.2 part of fluorescent whitening agent BA-L.

[0038] The preparation method of the present embodiment is as follows:

[0039] a) Mix wood pulp fiber and chemical fiber in proportion, use a pulper to finely grind and decompose and beat, the beating degree is 30°SR, and the beating concentration is controlled at 2%;

[0040] b) Add dry strength agent, wet strength agent PAE and 1 part of water to the pulper for batching, adjust the pH value to 7 to form a mixed fiber slurry, and make and dry the base paper by fourdrinier paper machine semi-finished products;

[0041] c) Mix and stir the flame retardant and the modifier according to the mass ratio to obtain ...

Embodiment 3

[0045]In this embodiment, the component distribution ratio is in parts by weight, 70 parts of softwood pulp fibers and hardwood pulp fibers are mixed in a mass ratio of 3:1, 15 parts of chemical fibers are nylon fibers, 10 parts of acrylic latex, and the flame retardant trimethylol Phosphorus oxide (THPO) 3 parts, modifier is 1 part of dibutyl tin dichloride, dry strength agent guar gum 0.5 part, wet strength agent PAE 0.1 part, and fluorescent whitening agent BBU and fluorescent whitening agent Mix 0.15 parts of BA-L according to the mass ratio of 1:1.

[0046] The preparation method of the present embodiment is as follows:

[0047] a) Mix wood pulp fiber and chemical fiber in proportion, use a pulper to finely grind, decompose and beat, the beating degree is 32°SR, and the beating concentration is controlled at 3%;

[0048] b) Add dry strength agent, wet strength agent PAE and 2 parts of water to the pulper for batching, adjust the pH value to 8 to form a mixed fiber slurry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to flame-retardant wallpaper base paper and a preparation method thereof and belongs to processing of flame-retardant nonwoven wallpaper base paper. The flame-retardant wallpaper base paper is prepared through the following components in parts by weight: 65 to 70 parts of wood pulp cellulose, 15 to 20 parts of chemical fibers, 10 to 15 parts of rubber latex, 1 to 3 parts of fire retardant, 1 to 3 parts of modifier, 0.1 to 0.5 parts of dry strength agent, 0.1 to 0.5 parts of wet strength agent and 0.05 to 0.2 parts of fluorescent agent. The preparation method comprises the following steps: uniformly mixing the flame retardant and the modifier at a mass ratio, thereby obtaining a modified flame-retardant solution; immediately adding the modified flame-retardant solution into crylic acid rubber latex, and uniformly mixing, thereby obtaining an a glue applying solution; soaking a base paper semifinished product in the glue applying solution, thereby obtaining the flame-retardant wallpaper base paper with stable flame-retardant property and low cost. The flame-retardant wallpaper base paper is high in whiteness and good in flame-retardant property, the flame-retardant property of the flame-retardant wallpaper base paper can reach a B1 fire-retardant standard, the high flame-retardant property can be maintained after the base paper is used for a long time, and the base paper unlikely turns yellow after being used for a long time.

Description

technical field [0001] The invention belongs to the field of flame-retardant non-woven wallpaper base paper materials, and in particular relates to a flame-retardant wallpaper base paper and a preparation method thereof. Background technique [0002] Wallpaper is the most commonly used material in wall decoration at present. When the socket leaks electricity or there is an open flame, the flame retardant effect of the wall wallpaper base paper can prevent the spread of the fire. Wallpaper base paper is the main base material for the production of flame-retardant wallpaper. It can be coated with a flame-retardant adhesive layer on the wallpaper base paper for coloring, printing, and embossing to make exquisite flame-retardant wallpaper. However, the existing flame-retardant wallpapers cannot be flame-retardant on both sides. Often, the side coated with the flame-retardant adhesive layer can be flame-retardant against open flames, but the side of the base paper of the wallpap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/20D21H21/14D21H21/18D21H21/20D21H21/30D21H23/24
Inventor 李安东李文海李建峰丁福瑞
Owner ZIBO OU MU SPECIAL PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap