A kind of CE-containing exhaust valve head material and preparation method thereof

A technology for exhaust valves and heads, which is applied in the field of Ce-containing exhaust valve head materials and its preparation, can solve the problems of not meeting the requirements of the engine, the structure is easy to change, and the type of material is single, so as to improve the compactness The effect of high purity, protection strength, and high lifespan

Active Publication Date: 2015-08-05
HUAWEI TEHCHNOLOGIES CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

3. Must have good wear resistance and service life
[0004] At present, the head material of the exhaust valve is mainly 21-4N, the type of material is very single, the high temperature strength is not high, and the structure is easy to change at a high temperature exceeding 800 degrees, which cannot meet the requirements of some engines.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of CE-containing exhaust valve head material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The specific steps of preparing the Ce-containing exhaust valve head material through low-pressure casting, rolling, and heat treatment are as follows:

[0018] (1) Ingredients, the alloy weight percentage composition of the exhaust valve head material is: C: 0.32%; Si: 0.25%; Mo: 2.0%; Mn: 6.50%; Cr: 15%; W: 0.50%; Ni : 2.0%; Ce: 1.0%; The remaining material is Fe with a purity of 99.8%, and the alloy material is mixed evenly;

[0019] (2) Melting in a vacuum induction furnace at a temperature of 1620°C for 1.5 hours;

[0020] (3) Low-pressure casting is adopted, and the process conditions of low-pressure casting are: filling pressure 0.06MPa, filling speed 50mm / s, filling pressurization 0.01MPa, pressure holding time 10s, rolling 3 times, and the casting is rolled again Forming, rolling three times, the deformation of the last rolling is 45%;

[0021] (4) Heating to 1050°C for 1 hour, then quenching;

[0022] (5) Heating to 800°C for 4 hours and quenching to obtain...

Embodiment 2

[0024] The specific steps of preparing the Ce-containing exhaust valve head material through low-pressure casting, rolling, and heat treatment are as follows:

[0025] (1) Ingredients, the alloy weight percentage composition of the exhaust valve head material is: C: 0.32%; Si: 0.25%; Mo: 2.0%; Mn: 6.50%; Cr: 15%; W: 0.50%; Ni : 2.0%; Ce: 1.0%; The remaining material is Fe with a purity of 99.8%, and the alloy material is mixed evenly;

[0026] (2) Melting in a vacuum induction furnace at a temperature of 1680°C for 1.5 hours;

[0027] (3) Low-pressure casting is adopted, and the process conditions of low-pressure casting are: filling pressure 0.06MPa, filling speed 50mm / s, filling pressurization 0.01MPa, pressure holding time 10s, rolling 3 times, and the casting is rolled again Forming, rolling three times, the deformation of the last rolling is 45%;

[0028] (4) Heating to 1150°C for 0.5 hours, then quenching;

[0029] (5) Heating to 820°C for 3 hours and quenching to obt...

Embodiment 3

[0031] The specific steps of preparing the Ce-containing exhaust valve head material through low-pressure casting, rolling, and heat treatment are as follows:

[0032] (1) Ingredients, the alloy weight percentage composition of the exhaust valve head material is: C: 0.34%; Si: 0.27%; Mo: 1.0%; Mn: 6.60%; Cr: 17.00%; W: 0.80%; Ni : 1.7%; Ce: 0.75%; the remaining material is Fe with a purity of 99.8%, and the alloy material is mixed evenly;

[0033] (2) Melting in a vacuum induction furnace at a temperature of 1620°C for 1.5 hours;

[0034] (3) Low-pressure casting is adopted, and the process conditions of low-pressure casting are: filling pressure 0.06MPa, filling speed 50mm / s, filling pressurization 0.01MPa, pressure holding time 10s, rolling 3 times, and the casting is rolled again Forming, rolling three times, the deformation of the last rolling is 55%;

[0035] (4) Heating to 1100°C for 0.5 hours, then quenching;

[0036] (5) Heating to 800°C for 3 hours and quenching to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Ce-containing exhaust valve head material and a preparation method thereof. The Ce-containing exhaust valve head material comprises the following alloying components in percentage by weight: 0.32-0.40% of C, 0.17-0.37% of Si, 1.0-2.0% of Mo, 6.5-8.0% of Mn, 15-18% of Cr, 0.50-1.0% of W, 1.5-2.5% of Ni, 0.50-1.0% of Ce, at most 0.015 of P, at most 0.015 of S, at most 0.010% of Cu and the balance of Fe. The valve material is prepared by low-pressure casting, rolling and heat treatment. The valve head material has the advantages of excellent heat resistance, high heat stability, high high-temperature strength and long service life.

Description

technical field [0001] The invention belongs to the field of metal materials, in particular to a Ce-containing exhaust valve head material and a preparation method thereof. Background technique [0002] The valve is one of the key parts of the engine, and it is a direct part used to open or close the intake and exhaust passages. The valve is the seal that seals the combustion chamber and controls the gas exchange of the engine during the working process of the engine. It is an important part to ensure the power, economy and reliability of the engine. The valves are divided into intake valves and exhaust valves. The air enters the engine cylinder through the intake valve and is mixed with fuel for combustion. The exhaust gas generated after combustion is discharged from the cylinder through the exhaust valve, so that fresh air enters the cylinder and burns to generate the driving force of the vehicle. Get rid of exhaust gas. The working conditions of the valve are harsh, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/58C22C33/04C21D1/18C21D8/00B22D18/04F01L3/00
Inventor 杨卫国
Owner HUAWEI TEHCHNOLOGIES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com