Delustering polypropylene composite material and preparation method thereof

A polypropylene material and composite material technology, applied in the field of thermoplastic resin composite materials, can solve the problems of affecting material properties and anti-aging ability, reducing the practicability of polypropylene materials, affecting rigidity and other problems, achieving good extinction ability, reducing gloss, Highly uniform effect

Inactive Publication Date: 2014-03-26
GUANGDONG KINGFA TECH CO LTD
View PDF6 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There have been some reports on reducing the glossiness of polypropylene (PP) composite materials. The Chinese patent application No. CN201010591416.7 mentioned a method to maintain low glossiness by adding styrene-acrylonitrile (SAN) copolymers, but The compatibility of SAN and PP is poor, which will easily lead to material delamination, affecting the performance and anti-aging ability of the material itself
The Chinese patent application No. 201110144142.1 realizes the matting effect by adding rubber powder, but the rigidity of polypropylene itself is poor, and adding too much rubber powder will further affect its rigidity and reduce the practicability of the polypropylene material itself

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1-3, polypropylene is the homopolymer PP produced by Taiwan Fuju, and the trade name is PP6331; the toughening agent is POE7256, American Dow; the compatibilizer is SBS T161B, Baling Petrochemical; the organic matting agent is HIPSPH88H, Taiwan Chimei, 8250 Taiwan Taihua, SEBS YH503, Baling Petrochemical; matting agent silica, 1250 mesh; antioxidant 1076, Swiss Ciba, antioxidant 168, Swiss Ciba; inorganic filler talcum powder, 1250 mesh.

[0021] Compatibilizer, organic matting agent, inorganic matting agent and inorganic filler are first mixed at low speed for 10 minutes and then extruded by twin-screw to granulate into matting masterbatch. , 190°C in the fourth zone, 180°C in the fifth zone, 180°C in the sixth zone, 190°C in the seventh zone, 200°C in the eighth zone, 210°C in the ninth zone, and the speed of the main engine is 300-400 rpm. The matt polypropylene composite material can be obtained by mixing the matt masterbatch with PP, toughener and antioxida...

Embodiment 4

[0029] Example 4, a matting polypropylene composite material, using the difference in refractive index of the organic matting agent and the synergistic effect of the matting agent to make the polypropylene material have matting properties; its formula is calculated by mass fraction and its components: 60% polypropylene, toughened 20% additive, 5% compatibilizer, 5% organic matting agent, 0.5% inorganic matting agent, 2% antioxidant, 7.5% inorganic filler.

[0030] The polypropylene is homopolypropylene, and its melt flow index is 10-15 g / min under the test condition of 230° C. / 2.16 kg.

[0031] The toughening agent is ethylene-vinyl acetate copolymer (EVA).

[0032] The compatibilizer is styrene-butadiene-styrene block copolymer (SBS).

[0033] The organic matting agent is polystyrene (PS).

[0034] The inorganic matting agent is silicon dioxide, and its powder should have an average particle diameter of 5 μm.

[0035] The antioxidant is antioxidant 168.

[0036] The inorg...

Embodiment 5

[0038]Example 5, a matting polypropylene composite material, using the difference in refractive index of the organic matting agent and the synergistic effect of the matting agent to make the polypropylene material have matting properties; its formula is calculated by mass fraction and its components: 80% polypropylene, toughened 2% agent, 5% compatibilizer, 5% organic matting agent, 0.5% inorganic matting agent, 0.1% antioxidant, 7.4% inorganic filler.

[0039] The polypropylene is homopolypropylene, and its melt flow index is 10-15 g / min under the test condition of 230° C. / 2.16 kg.

[0040] The toughening agent is polyolefin elastomer (POE).

[0041] The compatibilizer is maleic anhydride grafted SBS (MAH-SBS).

[0042] The organic matting agent is high impact polystyrene (HIPS).

[0043] The inorganic matting agent is mica powder, and its powder should have an average particle size of 10 μm.

[0044] The antioxidant is antioxidant 1010.

[0045] The inorganic filler is t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt flow indexaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a delustering polypropylene composite material and a preparation method thereof. The dulling polypropylene composite material comprises the following components in mass percent: 60-80% of polypropylene, 2-20% of flexibilizer, 5-20% of compatilizer, 5-25% of organic delustering agent, 0.5-5% of inorganic delustering agent, 0.1-2% of antioxidant and 2-20% of inorganic filler. The dispersion effect of delustering components in the polypropylene is strengthened through preparing master batch, the polypropylene, the delustering agent, the inorganic filler and part of compatilizer are firstly co-blended and then extruded through a dual-screw extruder to prepare the delustering master batch, and then the delustering master batch is co-blended with polypropylene and other components, and then extruded to prepare the delustering polypropylene composite material. The delustering polypropylene composite material is excellent in delustering performance, suitable for injection molding of various delustering products, can be applied to indoor decoration and automotive upholstery and can be used for preventing glare from generating in daily life.

Description

technical field [0001] The invention relates to the field of thermoplastic resin composite materials in polymer material technology, in particular to a matting polypropylene composite material and a preparation method thereof. Background technique [0002] Polypropylene is a general-purpose thermoplastic widely used in daily life, commonly known as "pleated glue". Because of its low price, excellent performance, and good formability, it is often prepared into various electrical housings, containers, and automotive interiors by injection molding. With the popularity of automobiles, consumers and automobile manufacturers are paying more and more attention to the quality of automotive interior parts. If the interior parts used in the cab have a high gloss, strong reflections and glare will occur in areas with strong sunlight Phenomenon, affect the driver's normal driving and comfort, so automotive interior parts require lower gloss. Among the materials used for daily househol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L25/06C08L51/04C08K3/36C08K3/34B29C47/92B29C48/92
CPCB29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895C08L23/12B29B9/06B29C2948/9258C08J3/226C08J2323/12C08K2201/003C08K2201/014C08L2205/02C08L2205/025C08L2205/035C08L2205/08C08L23/0815C08L53/02C08L51/04C08L53/025C08K13/02C08K3/36C08K3/34C08L23/0853C08L25/06C08K2003/265C08L51/006C08L51/06C08L23/06
Inventor 黄兴周小舟
Owner GUANGDONG KINGFA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com