A kind of UV curable ink with good toughness and preparation method thereof

A technology with ultraviolet light and good toughness, which is applied in ink, household utensils, applications, etc. It can solve problems such as shedding, affecting product quality, and cracking on the ink film surface, and achieves the effects of improving toughness, product quality, and good adhesion

Active Publication Date: 2016-04-13
浦江大众印刷材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The test found that for a substrate that needs to be overprinted more than 3 times to reflect its unique printing effect, if the existing ink is used for printing, after the ink is printed on the surface of the substrate and cured, when the substrate is squeezed or bent, the ink will disappear. The surface of the film usually has obvious cracks and falls off, which affects the product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] specific implementation plan

[0011] The present invention will be described in detail below through specific examples.

[0012] A UV-curable ink with good toughness is prepared from the following raw materials in parts by weight (kg): organic pigment 1, polyurethane acrylate 30, hydroxyethyl methacrylate 30, isobornyl methacrylate 14, 2- Hydroxy acrylic resin 10, 1-hydroxycyclohexyl phenylacetone 6, rose essential oil 1, coumarone 4, accelerator DM1, octadecyltrimethylammonium chloride 3, auxiliary agent 4;

[0013] The additives are prepared from the following raw materials in parts by weight (kg): 0.2 nanometer diatomite powder, 0.2 nanometer mica powder, silane coupling agent KH-5502, morpholine 1, neopentyl glycol 3, antioxidant 10351, crosslinking agent TAC2, tripropylene glycol diacrylate 10, propylene glycol methyl ether acetate 5, propyl gallate 2, coix seed oil 1; the preparation method is to mix the materials, heat to 60-70°C, and stir React for 30-40 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a UV-curing printing ink with high flexibility and a preparation method thereof. The UV-curing printing ink is characterized by being prepared from the following raw materials in parts by weight: 1-3 parts of an organic pigment, 30-35 parts of urethane acrylate, 30-35 parts of hydroxyethyl methylacrylate, 14-18 parts of isobornyl methacrylate, 10-12 parts of 2-hydroxyl acrylic resin, 6-9 parts of 1-hydroxycyclohexyl phenyl ketone, 1-2 parts of rose essential oil, 4-5 parts of coumarone, 1-2 parts of an accelerator DM, 3-4 parts of octadecyl trimethyl ammonium chloride, and 4-5 parts of an assistant. The assistant improves the flexibility of printing ink, enables the printing ink to be uniformly dispersed, and maintains the stability of the printing ink. A favorable adhesive force of an overprint ink film is ensured while the flexibility of the cured film is improved, and the quality of the product is improved.

Description

technical field [0001] The invention relates to an ink and a preparation method thereof, in particular to an ultraviolet curable ink with good toughness and a preparation method thereof. Background technique [0002] At present, in the screen printing process, the thickness of the ink film after solidification is thicker than that of other printing methods. Generally, the thickness of the ink film for a single printing is 20-40 μm. In order to ensure good ink on the surface of the substrate Adhesion, the total thickness of the ink overprinted on the surface of the substrate should not exceed 100 μm, that is, the ink can generally be overprinted up to 3 times on the substrate. [0003] The test found that for a substrate that needs to be overprinted more than 3 times to reflect its unique printing effect, if the existing ink is used for printing, after the ink is printed on the surface of the substrate and cured, when the substrate is squeezed or bent, the ink will disappear....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/101C09D11/03
Inventor 陈可夏陈可亮潮建平
Owner 浦江大众印刷材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com