Technology for preparing nylon 11 by 11-aminoundecanoic acid normal-pressure melt polymerization

A melt polymerization and undecanoic acid technology, applied in the field of nylon manufacturing, can solve the problems of reducing equipment cost, monomer loss, and equipment requirements, and achieve the effect of reducing equipment cost, reducing equipment requirements, and reducing loss.

Active Publication Date: 2014-04-09
CHINA BLUESTAR CHENGRAND CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims to solve the need to pressurize and melt 11-aminoundecanoic acid in the synthesis of nylon 11 in the prior art, which has high requirements for equipment, high-pressure equipment is needed, and the amino Undecanoic acid will also be taken out with water vapor, causing the problem of monomer loss. A process for preparing nylon 11 by melting and polymerizing 11-aminoundecanoic acid under normal pressure is provided, which can synthesize nylon 11 under normal pressure. Reduced equipment cost and reduced loss of 11-aminoundecanoic acid monomer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology for preparing nylon 11 by 11-aminoundecanoic acid normal-pressure melt polymerization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 11-Amino undecanoic acid atmospheric pressure melt polymerization to prepare nylon 11 process:

[0031] Mix 11-aminoundecanoic acid with a flux, and the flux is one or a variety of organic solvents with a boiling point of 185-220°C in any proportion; under normal pressure, heat the material to melt, and then continue to heat Raise the temperature to 230°C to evaporate the flux and the water generated by the reaction; after the normal pressure melting reaction is completed, continue to maintain the temperature at 230°C, then vacuumize and carry out the vacuum reaction in a vacuum state; stop vacuuming after the vacuum reaction is completed, Return to the normal pressure state, and discharge to obtain nylon 11; in the process of preparing nylon 11 by normal pressure melt polymerization of 11-aminoundecanoic acid, catalysts and auxiliary agents are also added.

Embodiment 2

[0033] 11-Amino undecanoic acid atmospheric pressure melt polymerization to prepare nylon 11 process:

[0034] Mix 11-aminoundecanoic acid with a flux, and the flux is one or a variety of organic solvents with a boiling point of 185-220°C in any proportion; under normal pressure, heat the material to melt, and then continue to heat Raise the temperature to 270°C to evaporate the flux and the water generated by the reaction; after the normal pressure melting reaction is completed, continue to maintain the temperature at 270°C, then vacuumize, and carry out the vacuum reaction in a vacuum state; stop vacuuming after the vacuum reaction is completed, Return to the normal pressure state, and discharge to obtain nylon 11; in the process of preparing nylon 11 by normal pressure melt polymerization of 11-aminoundecanoic acid, catalysts and auxiliary agents are also added.

Embodiment 3

[0036] 11-Amino undecanoic acid atmospheric pressure melt polymerization to prepare nylon 11 process:

[0037]Mix 11-aminoundecanoic acid with a flux, and the flux is one or a variety of organic solvents with a boiling point of 185-220°C in any proportion; under normal pressure, heat the material to melt, and then continue to heat Raise the temperature to 250°C to evaporate the flux and the water generated by the reaction; after the normal pressure melting reaction is completed, continue to maintain the temperature at 250°C, then vacuumize and carry out the vacuum reaction in a vacuum state; stop vacuuming after the vacuum reaction is completed, Return to the normal pressure state, and discharge to obtain nylon 11; in the process of preparing nylon 11 by normal pressure melt polymerization of 11-aminoundecanoic acid, catalysts and auxiliary agents are also added.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a technology for preparing nylon 11 by 11-aminoundecanoic acid normal-pressure melt polymerization. The technology comprises the following steps of mixing 11-aminoundecanoic acid and a fluxing agent which comprises one or more organic solvents having any ratio and multiple boiling points of 185-220 DEG C, carrying out heating under normal pressure so that the mixture is melted, sequentially carrying out heating to a temperature of 230-270 DEG C so that the fluxing agent and reaction product water are evaporated, after the normal-pressure melting reaction, continuously keeping the temperature in a range of 230-270 DEG C, carrying out vacuum pumping, carrying out a vacuum reaction process in vacuum, after the vacuum reaction process, stopping the vacuum pumping, recovering a normal pressure state and discharging nylon 11. The technology can reduce an equipment cost and reduce 11-aminoundecanoic acid monomer loss.

Description

Technical field [0001] The present invention involves a preparation process of Nylon 11. It is more specifically that the invention involves a process of the nylon manufacturing technology of a nylon manufacturing technology. Background technique [0002] Nylon 11 is a kind of soft nylon for long carbon chains. Its sub -armored chain is long and the density of amide is low. Compared with other nylon, it has a very low water absorption, good size stability, mechanical performance, chemical resistance to chemical resistanceHeading insulation performance, low temperature (-40 ° C) resistance is excellent; it has elastic memory benefits. When external force is removed, it can be restored to the original shape.For molding, it is harmless to the human body, which can meet the injection molding and extrusion processing of various melting viscosity range. It is often used in the manufacture of earthquake -resistant oil pipes and hose, such as automotive oil pipes, oil pipes, and clutch h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G69/08C08G69/04
Inventor 沈佶周楠宋升
Owner CHINA BLUESTAR CHENGRAND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com