A kind of negative ion polyester fiber and preparation method thereof

A polyester fiber and negative ion technology, applied in the field of negative ion polyester fiber and its preparation, can solve the problems of poor durability and washing resistance, limited fiber use range, increased uncertainty of post-spinning aids, etc., and achieve good performance , easy industrial production, high spinnability effect

Active Publication Date: 2016-01-20
芯安健康科技广东有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The current anion fibers are mainly post-processing and finishing. The post-finishing process is generally to disperse the anion powder in the liquid, and then attach it to the surface of the polyester fiber through a coupling agent. There are many defects in this product: the first is Poor durability and washing resistance; secondly, the downstream use of fibers is limited; finishing processing increases the uncertainty of the use of post-spinning auxiliaries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of anion polyester fiber, the raw material configuration of this anion polyester fiber comprises according to parts by weight: 75 parts of polyester fiber chips and 25 parts of anion master batches, the raw material configuration of said anion master batches includes according to parts by weight: polyester 75 parts of fiber slices, 22.8 parts of ultra-dispersed anion powder, 1 part of phthalate ester, 1 part of pentaerythritol stearate, 0.1 part of tris[2.4-di-tert-butylphenyl] phosphite and tetrakis [β-(3, 0.1 part of 5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester.

[0022] The preparation method of a kind of negative ion polyester fiber that prepares component according to above-mentioned parts by weight is as follows:

[0023] 1 part of the phthalate and 22.8 parts of the ultra-dispersed anion powder are mixed uniformly in a high-speed mixer at a temperature of 75 degrees Celsius, and then 75 parts of the polyester fiber chips and 1 part of...

Embodiment 2

[0025] A kind of anion polyester fiber, the raw material configuration of this anion polyester fiber comprises according to parts by weight: 80 parts of polyester fiber chips and 20 parts of anion master batches, the raw material configuration of said anion master batches includes according to parts by weight: polyester 81.6 parts of fiber slices, 14 parts of super-dispersed anion powder, 2 parts of phthalate ester, 2 parts of pentaerythritol stearate, 0.2 parts of tris[2.4-di-tert-butylphenyl] phosphite and tetrakis[β-(3, 0.2 parts of 5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester.

[0026] The preparation method of a kind of negative ion polyester fiber that prepares component according to above-mentioned parts by weight is as follows:

[0027] 2 parts of the phthalate ester and 14 parts of the super-dispersed anion powder are mixed uniformly in a high-speed mixer at a temperature of 80 degrees Celsius, and then 81.6 parts of the polyester fiber chips, 2 ...

Embodiment 3

[0029] A kind of anion polyester fiber, the raw material configuration of this anion polyester fiber comprises according to parts by weight: 85 parts of polyester fiber chips and 15 parts of anion master batches, the raw material configuration of said anion master batches includes according to parts by weight: polyester 87 parts of fiber slices, 6 parts of ultra-dispersed anion powder, 3 parts of phthalate ester, 3 parts of pentaerythritol stearate, 0.5 part of tris[2.4-di-tert-butylphenyl] phosphite and tetrakis[β-(3, 0.5 parts of 5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester.

[0030] The preparation method of a kind of negative ion polyester fiber that prepares component according to above-mentioned parts by weight is as follows:

[0031] 3 parts of the phthalate ester and 6 parts of the super-dispersed anion powder are mixed uniformly in a high-speed mixer at a temperature of 85 degrees Celsius, and then 87 parts of the polyester fiber chips and 3 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a negative ion polyester fiber and a preparation method thereof. The negative ion polyester fiber is prepared from the following raw materials in parts by weight: 70-90 parts of polyester fiber chip and 10-30 parts of negative ion master batch, wherein the negative ion master batch is prepared from the following raw materials in parts by weight: 75-94 parts of polyester fiber chip, 5-34 parts of ultra-disperse negative ion powder, 0.5-5 parts of phthalic ester, 0.5-5 parts of pentaerythritol stearic acid ester, 0.05-1 part of tris-(2,4-ditertbutyl-pheny)-phosphite and 0.05-1 part of tetra [beta-(3,5-ditertbutyl-4-hydroxy phenyl) propionate] pentaerythritol ester. The negative ion polyester fiber disclosed by the invention has good usability, high spinnability and great advantages for the spinning of fine denier and the negative ion fiber with high occurrence quantity, and is high in occurrence quantity of negative ions and wide in application range; the preparation method of the negative ion polyester fiber is simple to operate and facilitates industrial production.

Description

technical field [0001] The invention belongs to the technical field of polymer compounds, and in particular relates to an anion polyester fiber and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET), also known as polyester Polyethyeneterephthalate, is a polymer compound that is prepared by polycondensation of terephthalic acid (PTA) and ethylene glycol (EG). The technology of PET polyester spinning is known and common polyester fibers are abundantly available on the market. With the gradual improvement of living standards and the continuous deterioration of the natural environment, people have an increasingly strong desire for health, environmental protection and health care. It is under such conditions that the concept of negative ion health has begun to appear in the public's field of vision. [0003] Negative ions are called "air vitamins" in the medical field, and their main functions are as follows: [0004] 1. It affects the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10
Inventor 邓思东
Owner 芯安健康科技广东有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More