Preparation method of composite type protective material for comprehensive toxicant prevention

A protective material and composite technology, which is applied in the field of preparation of composite protective materials, can solve the problems of large limitations in the use of neighborhoods, large limitations of PPC protection spectrum, inconvenient production and use, etc., to overcome application limitations, design Reasonable, the effect of improving the level of use

Inactive Publication Date: 2014-04-16
SHANXI XINHUA CHEM
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, at present, there are few researches on the protection of penetrating poisons at home and abroad, and the PPC protection spectrum put into use is relatively limited, which can only meet the protection of perfluoroisobutylene. In my country, the developed PPC is used in protective equipment At the same time, it is packed in layers with the classic poison protection material, that is, ASZM-T impregnated carbon, so as to achieve the purpose of effective protection against classic poison and penetrating poison at the same time.
This kind of filling method has higher requirements on the design, and at the same time brings a lot of inconvenience to production and use, and the use of the product is very limited in the neighborhood, so it can only be used for collective protective equipment, but for individual protective equipment that belongs to thin layer filling equipment can not be used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of composite type protective material for comprehensive toxicant prevention

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A composite protective material for comprehensive anti-virus, including activated carbon as a carrier and an impregnating agent adsorbed by activated carbon, the impregnating agent includes 8% (weight) Cu, 2% (weight) Mo, 0.7% (weight) Zn, 3% (weight) active ingredient Ag, 8% (weight) polyamine-based compound TEDA.

[0028] The preparation method is as follows:

[0029] (1) Add the impregnating agent of the above active components, that is, calculate the required weights of basic copper carbonate, zinc carbonate, ammonium molybdate and silver nitrate according to the content of the active components, add it into ammonia water, heat and melt to prepare Impregnation solution, keep the temperature of the mixed solution at 70°C, wait until the impregnating agent is fully dissolved, use the same volume impregnation method, mix it with activated carbon evenly, and let it stand for 2 hours;

[0030] (2) The fluidized bed activation method is adopted, the activation temperatur...

Embodiment 2

[0033] A composite protective material for comprehensive anti-virus, comprising activated carbon as a carrier and an impregnating agent adsorbed by activated carbon, the impregnating agent comprising 10% by weight of Cu, 0.5% by weight of Mo, 0.4% by weight Zn, 3% (weight) active ingredient Ag, 5% (weight) polyamine-based compound TEDA.

[0034] The preparation method is as follows:

[0035] (1) Add the impregnating agent of the above active components, that is, calculate the required weights of basic copper carbonate, zinc carbonate, ammonium molybdate and silver nitrate according to the content of the active components, add it into ammonia water, heat and melt to prepare Impregnation solution, keep the temperature of the mixed solution at 80°C, wait until the impregnating agent is fully dissolved, use the same volume impregnation method, mix it with activated carbon evenly, and let it stand for 1.5h;

[0036] (2) The fluidized bed activation method is adopted, the activatio...

Embodiment 3

[0039] A composite protective material for comprehensive anti-virus, including activated carbon (coconut shell crushed carbon) as a carrier and an impregnating agent adsorbed by activated carbon, the impregnating agent includes 7% (weight) of Cu, 1% (weight) of Mo , 1% (weight) of Zn, 0.6% (weight) of active ingredient additive Ag, 10% (weight) of polyamine compound TEDA.

[0040] The preparation method is as follows:

[0041] (1) Add the impregnating agent of the above active components, that is, calculate the required weights of basic copper carbonate, zinc carbonate, ammonium molybdate and silver nitrate according to the content of the active components, add it into ammonia water, heat and melt to prepare Impregnation solution, keep the temperature of the mixed solution at 60°C, wait until the impregnating agent is fully dissolved, use the same volume impregnation method, mix it with activated carbon evenly, and let it stand for 1h;

[0042] (2) The fluidized bed activatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a toxicant prevention material, particularly to a preparation method of a composite type protective material for comprehensive toxicant prevention. The method comprises the steps as follows: (1) the composite type protective material for the comprehensive toxicant prevention comprises activated carbon serving as a carrier and an impregnant adsorbed by the activated carbon, wherein the impregnant comprises 7%-10% (by weight) of Cu, 1%-2% (by weight) of Mo, 0.6%-3% (by weight) of an active component additive Ag, 0.4%-1% (by weight) of Zn and 5%-10% (by weight) of a multi-amine compound TEDA (triethylene diamine); the content of basic cupric carbonate, ammonium molybdate, silver nitrate and zinc carbonate of the impregnant of active components are calculated according to the content of the active components such as the Cu, the Mo, the Ag and the Zn respectively. The method is reasonable in design, and the composite type protective material capable of effectively protecting against various toxicants such as classic toxicants of HCN (hydrogen cyanide) and CNCL (cyanogen chloride), a penetrating toxicant of perfluoroisobutylene and the like, is developed.

Description

technical field [0001] The invention relates to an antivirus material, in particular to a preparation method for a composite antivirus material for comprehensive antivirus. Background technique [0002] Protective impregnated activated carbon has been continuously updated with the development of the situation. After entering the 1990s, penetrating agents represented by perfluoroisobutylene (PFIB) have attracted people's attention. [0003] However, at present, there are few researches on the protection of penetrating poisons at home and abroad, and the PPC protection spectrum put into use is relatively limited, which can only meet the protection of perfluoroisobutylene. In my country, the developed PPC is used in protective equipment At the same time, it is packed in layers with the classic poison protection material, namely ASZM-T impregnated carbon, so as to achieve the purpose of effective protection against classic poison and penetrating poison at the same time. This kin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A62D3/30
Inventor 金彦任赵婷周闯王波裴佩黄英张金凤范斌杰邢浩洋王钢黄振兴
Owner SHANXI XINHUA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com