Simulated wood grain wallboard coated with ultraviolet-resistant coating and preparation method thereof

A technology of anti-ultraviolet coating and imitation wood grain, which is applied in the field of building panels, can solve the problems of long construction period, complicated operation and complicated process, and achieve the effect of light weight, convenient operation and great flexibility

Active Publication Date: 2014-04-23
王东彬
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the exterior wall, which leads to complicated procedures, complicated operations, and long construction periods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Simulated wood grain wallboard coated with ultraviolet-resistant coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An imitation wood-grain wallboard coated with an anti-ultraviolet coating, which includes an imitation wood-grain base 1, an imitation wood-grain forming layer 2 and an anti-ultraviolet coating 3, the outer surface of the imitation wood-grain base 1 contains an imitation wood-grain forming layer 2, A layer of anti-ultraviolet coating 3 is sprayed on the imitation wood grain forming layer 2;

[0029] The imitation wood grain forming layer 2 is a texture layer imitating the texture of pine logs; the anti-ultraviolet coating 3 is a commercially available anti-ultraviolet coating; the imitation wood base layer 1 is composed of 50% (weight) coal gangue fiber Granules, 35% (weight) of polymer fire-resistant modified materials, 10% (weight) of silicon-aluminum clinker and 5% (weight) of stearic acid are mixed and then added with pigments imitating the color of pine logs.

[0030] A kind of preparation method of the imitation wood-grain wallboard that is coated with anti-ultrav...

Embodiment 2

[0038] An imitation wood-grain wallboard coated with an anti-ultraviolet coating, which includes an imitation wood-grain base 1, an imitation wood-grain forming layer 2 and an anti-ultraviolet coating 3, the outer surface of the imitation wood-grain base 1 contains an imitation wood-grain forming layer 2, A layer of anti-ultraviolet coating 3 is sprayed on the imitation wood grain forming layer 2;

[0039] The imitation wood grain forming layer 2 is a texture layer imitating the texture of ebony wood; the described anti-ultraviolet coating 3 is a commercially available anti-ultraviolet coating; the described imitation wood base layer 1 is composed of 75% (weight) coal gangue Fiber particles, 15% (weight) polymer fire-resistant modified materials, 8% (weight) silicon-aluminum clinker and 2% (weight) stearic acid are mixed and then added with pigments imitating the color of ebony wood.

[0040] A kind of preparation method of the imitation wood-grain wallboard that is coated wit...

Embodiment 3

[0048] An imitation wood-grain wallboard coated with an anti-ultraviolet coating, which includes an imitation wood-grain base 1, an imitation wood-grain forming layer 2 and an anti-ultraviolet coating 3, the outer surface of the imitation wood-grain base 1 contains an imitation wood-grain forming layer 2, A layer of anti-ultraviolet coating 3 is sprayed on the imitation wood grain forming layer 2;

[0049] The imitation wood grain forming layer 2 is a texture layer imitating the texture of Fraxinus mandshurica; the described anti-ultraviolet coating 3 is a commercially available anti-ultraviolet coating; the described imitation wood base layer 1 is made of 60% (weight) coal gangue Fiber particles, 20% (weight) polymer fireproof modified material, 15% (weight) silicon-aluminum clinker and 5% (weight) stearic acid are mixed and then added with pigment imitating the color of ash.

[0050] A kind of preparation method of the imitation wood-grain wallboard that is coated with anti-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Areal densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Areal densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a simulated wood grain wallboard coated with an ultraviolet-resistant coating and a preparation method thereof. The simulated wood grain wallboard comprises a simulated wood base layer (1), a simulated wood grain molding layer (2) and an ultraviolet-resistant coating (3), wherein the external surface of the simulated wood base layer (1) comprises the simulated wood grain molding layer (2); the ultraviolet-resistant coating (3) is sprayed on the simulated wood grain molding layer (2); and a simulated wood color pigment is added into the simulated wood base layer (1). The preparation method comprises the following steps: mixing coal gangue fiber particles, high-polymer fireproof modified material, silicon aluminum clinker and stearic acid, respectively adding the simulated wood color pigment according to production needs, drying at 150 DEG C, stirring for 20 minutes, injecting into a mold with simulated wood grains, molding, and spraying the ultraviolet-resistant paint on the external veneer of the product. The preparation method is simple to operate and simplifies the procedure; and the simulated aluminum sheet wallboard has the advantages of beautiful appearance, environmental protection and energy saving.

Description

technical field [0001] The invention belongs to the field of building panels, and in particular relates to a wood-grain-like wallboard coated with an anti-ultraviolet coating and a preparation method thereof. Background technique [0002] With the continuous development of building decoration, people have higher and higher requirements for decoration, especially in the selection of materials, which not only require reasonable price, economical and practical, but also elegant appearance and environmental protection requirements. [0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the outer wall, which leads to complicated procedures, complicated operations, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04C2/288B32B33/00B32B13/04B32B13/02C04B28/06C04B24/24C04B18/04
CPCY02W30/91
Inventor 程凤岐王东彬柳意安胡梁
Owner 王东彬