High-definition transparent PVC (polyvinyl chloride) film and preparation method thereof

A PVC resin and transparent technology, applied in the field of high-definition transparent PVC film and its preparation, can solve the problems of stretching, toughness, cold resistance and heat resistance not reaching the standard, reducing the transparency of PVC, easy yellowing and discoloration of PVC, etc. Good effect, improving and improving surface tension, soft and plump touch

Active Publication Date: 2014-04-30
DONGGUAN IUIU HOUSEHOLD PROD
View PDF4 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reason is that PVC is prone to yellowing and discoloration during the production process, so it can only be packaged with a colored exterior
With the development of the market, people hope to use pure transparent PVC materials as the base material of table mats, but the traditional PVC materials reduce the transparency of PVC due to the addition of various additives, but the tensile strength of pure PVC materials Degree, toughness and cold and heat resistance can not meet the standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Weigh 100 parts of PVC resin, 2 parts of PVC stabilizer, 2 parts of non-toxic plasticizer, 37 parts of plasticizer, 6 parts of liquid flame retardant, and 0.015 parts of ultramarine toner, and prepare PVC film according to the following steps:

[0051] Step 1: Gradually add the weighed materials when the high-speed mixer is running at a low speed, and then run at a high speed for 380s, the low speed is 60 rpm, and the high speed is 1200 rpm, the temperature rises to 100 ° C, and it is automatically discharged to the refrigerator. Cold mixing in the mixer for 400s, cooled by natural water temperature, and then sent to the middle barrel to mix evenly, and the material is loose.

[0052] Step 2: Put the mixed material in step 1 into the planetary extruder, set the die temperature of the screw feeding at 150°C, and the screw temperature is 5°C lower than the barrel temperature, and then flow into the rolling mill for gelation Send it to the filter for filtration, and pass t...

Embodiment 2

[0059] Weigh 100 parts of PVC resin, 2 parts of PVC stabilizer, 2 parts of non-toxic plasticizer, 33 parts of plasticizer, 10 parts of cold-resistant agent, and 0.015 parts of ultramarine toner, and prepare PVC film according to the following steps:

[0060] Step 1: Gradually add the weighed materials when the high-speed mixer is running at a low speed, and then run at a high speed for 380s, the low speed is 100 rpm, and the high speed is 1000 rpm, the temperature rises to 120 ° C, and it is automatically discharged to the refrigerator. Cold mixing in the mixer for 600s, cooled by natural water temperature, and then sent to the middle barrel to mix evenly, and the material is loose.

[0061] Step 2: Put the mixed material in step 1 into the planetary extruder, set the die temperature of the screw feeding at 170°C, the screw temperature is 5-10°C lower than the barrel temperature, and then flow into the roller machine for glue After melting, it is sent to the filter for filtrat...

Embodiment 3

[0068] Weigh 100 parts of PVC resin, 2 parts of PVC stabilizer, 2 parts of non-toxic plasticizer, 48 parts of plasticizer (DOTP), 0.012 parts of ultramarine toner, and prepare PVC film according to the following steps:

[0069] Step 1: Gradually add the weighed materials when the high-speed mixer is running at a low speed, and then run at a high speed for 380s, the low speed is 80 rpm, and the high speed is 1400 rpm, the temperature rises to 130 ° C, and it is automatically discharged to the refrigerator. Cold mixing in the mixer for 600s, cooled by natural water temperature, and then sent to the middle barrel to mix evenly, and the material is loose.

[0070] Step 2: Put the mixed material in step 1 into the planetary extruder, set the die temperature of the screw feeding at 150°C, and the screw temperature is 10°C lower than the barrel temperature, and then flow into the rolling mill for gelation Send it to the filter for filtration, and pass through 20 mesh, 60 mesh, 120 me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparation of furnace decoration PVC (polyvinyl chloride) films and particularly to a high-definition transparent PVC film and a preparation method of the high-definition transparent PVC film. The PVC film is prepared from the following raw materials in parts by weight: 100 parts of a PVC resin, 1-4 parts of a PVC stabilizer, 1-4 parts of a non-toxic plasticizer, 30-50 parts of a plasticizer, 0-6 parts of a liquid fire retardant, 0-10 parts of an anti-freezing agent, and 0.01-0.02 part of ultramarine toner, the materials are added into a high-speed mixer to be fully mixed, the well mixed materials are conveyed to a planet machine to be pre-plasticized, then the pre-plasticized materials are conveyed to a filter to be repeatedly plasticated, filtered and plasticized, and then conveyed to a calendar for calendaring, the calendared PVC film is cooled in a water tank and unoiled to obtain the PVC film having the advantages of high glossiness, high transparency, excellent thermal endurance and chemical stability and strong tensile strength.

Description

technical field [0001] The invention relates to the technical field of furniture decoration PVC film preparation, in particular to a high-definition transparent PVC film and a preparation method thereof. Background technique [0002] The main component of PVC is polyvinyl chloride, which is light yellow, translucent and shiny. Transparency is better than polyethylene and polypropylene, and worse than polystyrene. Depending on the amount of additives, it can be divided into soft and hard PVC. Soft products are soft and tough, and feel sticky. The hardness of hard products is higher than that of low-density polyethylene. And lower than polypropylene, there will be whitening at the inflection. Common products include plates, pipes, shoe soles, toys, doors and windows, wire sheaths, stationery, etc. It is a polymer material that uses a chlorine atom to replace a hydrogen atom in polyethylene. [0003] The price and cost of PVC are relatively low, and the production process is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K5/1515C08K5/12C08K5/11C08K5/523C08K5/521C08K5/06C08K5/3492C08J5/18B29C47/92B29C69/00B29C43/24B29C55/12B29C71/00B29C48/92
CPCB29C48/44B29C48/92B29C2948/92704B29C2948/92895
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap