Spun silk softening agent preparation method

A silk softener and quality technology, applied in the field of silk softener preparation, can solve the problems of unsatisfactory effect and large environmental pollution, and achieve the effects of less environmental pollution, good bulkiness and good softness performance

Inactive Publication Date: 2014-04-30
CHANGSHU MIAOQUAN SHENGDA AUX FACTORY
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing silk softener mainly uses aminocarboxyl silicone oil emulsion, and aminocarboxyl silicone oil emulsion is mainly synthesized by anion chemical industry, which contains a lot of anions and soap inside, so it pollutes the environment more
Moreover, due to the material characteristics of spun silk, the effect of general softeners on spun silk is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A preparation method of silk softener, comprising the steps of:

[0014] 1) Mix 130 parts by mass of octamethyltetrasiloxane with 43 parts by mass of polyethoxylated fatty alcohol, add sodium hydroxide to adjust the pH value to 11, raise the temperature to 140°C at 5°C / min, and react for 8 hours. Cool down to 50°C at 2°C / min, add dropwise 24 parts by mass of ascorbic acid to adjust the pH value down to 5, and obtain the first mixed solution;

[0015] 2) Mix 300 parts by mass of dimethyldisiloxane with 850 parts by mass of purified water, add sodium hydroxide to adjust the pH value to 12, raise the temperature to 70°C at 1°C / min, react for 12 hours, and react at 5°C / min Raise the temperature to 125°C and react for 6 hours to obtain the second mixed solution;

[0016] 3) Mix the first mixed solution with the second mixed solution, add sodium hydroxide to adjust the pH value to 11, raise the temperature to 90°C at 5°C / min, react for 6 hours, and cool down to room temperat...

Embodiment 2

[0019] A preparation method of silk softener, comprising the steps of:

[0020] 1) Mix 130 parts by mass of octamethyltetrasiloxane with 43 parts by mass of polyethoxylated fatty alcohol, add sodium hydroxide to adjust the pH value to 11, raise the temperature to 140°C at 5°C / min, and react for 8 hours. Cool down to 50°C at 2°C / min, add dropwise 24 parts by mass of ascorbic acid to adjust the pH value down to 5, and obtain the first mixed solution;

[0021] 2) Mix 300 parts by mass of dimethyldisiloxane with 850 parts by mass of purified water, add sodium hydroxide to adjust the pH value to 12, raise the temperature to 70°C at 1°C / min, react for 12 hours, and react at 5°C / min Raise the temperature to 125°C and react for 6 hours to obtain the second mixed solution;

[0022] 3) Mix the first mixed solution with the second mixed solution, add sodium hydroxide to adjust the pH value to 11, raise the temperature to 90°C at 5°C / min, react for 6 hours, and cool down to room temperat...

Embodiment 3

[0025] A preparation method of silk softener, comprising the steps of:

[0026] 1) Mix 130 parts by mass of octamethyltetrasiloxane with 43 parts by mass of polyethoxylated fatty alcohol, add sodium hydroxide to adjust the pH value to 11, raise the temperature to 140°C at 5°C / min, and react for 8 hours. Cool down to 50°C at 2°C / min, add dropwise 24 parts by mass of ascorbic acid to adjust the pH value down to 5, and obtain the first mixed solution;

[0027] 2) Mix 300 parts by mass of dimethyldisiloxane with 850 parts by mass of purified water, add sodium hydroxide to adjust the pH value to 12, raise the temperature to 70°C at 1°C / min, react for 12 hours, and react at 5°C / min Raise the temperature to 125°C and react for 6 hours to obtain the second mixed solution;

[0028] 3) Mix the first mixed solution with the second mixed solution, add sodium hydroxide to adjust the pH value to 11, raise the temperature to 90°C at 5°C / min, react for 6 hours, and cool down to room temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a spun silk softening agent preparation method, which comprises: 1) mixing 130 parts by mass of octamethyl tetrasiloxane and 43 parts by mass of polyethoxylated fatty alcohol, adding sodium hydroxide to adjust the pH value to 11, heating at a speed of 5 DEG C/min to achieve a temperature of 140 DEG C, carrying out a reaction for 8 h, cooling at a speed of 2 DEG C/min to achieve a temperature of 50 DEG C, and adding 24 parts by mass of ascorbic acid in a dropwise manner to adjust the pH value to 5 to obtain a first mixed solution; 2) obtaining a second mixed solution; 3) mixing the first mixed solution and the second mixed solution, adding sodium hydroxide to adjust the pH value to 11, heating to achieve a temperature of 90 DEG C, carrying out a reaction for 6 h, and cooling at a speed of 1 DEG C/min to achieve a room temperature; and 4) adding 1-2 parts by mass of ethylene glycol monostearate, 1 part by mass of hydroxypropyl methyl cellulose, 1 part by mass of sodium carbonate, 15 parts by mass of an amino silane coupling agent and 16 parts by mass of citric acid, and uniformly stirring to obtain the spun silk softening agent. The prepared spun silk softening agent is the non-ionic softening agent and has low environmental pollution, wherein the treated spun silk has characteristics of good bulkiness and good softness.

Description

technical field [0001] The invention relates to a preparation method of silk softener. Background technique [0002] The existing silk softener mainly uses aminocarboxyl silicone oil emulsion, and aminocarboxyl silicone oil emulsion is mainly synthesized by anion chemical industry, contains a large amount of anions and soap inside, so it pollutes the environment more. And because of the material properties of spun silk, the effect of general softening agents on spun silk is not ideal. Contents of the invention [0003] The object of the present invention is to provide a preparation method of a spun silk softener. The spun silk softener prepared by the method is non-ionic, has little environmental pollution, and the treated spun silk has good bulkiness and softness. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of preparation method of silk softening agent, comprising the steps: [0005] 1) Mix 130 parts...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/647D06M13/192D06M13/50D06M13/224D06M15/09D06M11/76C08G77/46D06M101/10
Inventor 严佳
Owner CHANGSHU MIAOQUAN SHENGDA AUX FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap