Method for regulating and controlling preparation of calcium carbonate micro-nanospheres through calcium lignosulfonate

A technology of calcium lignosulfonate and calcium carbonate, applied in the direction of calcium carbonate/strontium/barium, etc., which can solve the problems of complex preparation process, high cost of organic matter source, and difficult control of reaction conditions

Inactive Publication Date: 2014-05-07
ZHEJIANG SCI-TECH UNIV
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the problems of complex preparation process, high cost of organic matter sources, and uneasy control of reaction conditions in the preparation of calcium carbonate crystal particles with specific shape and size, at the same time, resource utilization of sulphite pulping waste liquor has opened up new opportunities for calcium lignosulfonate A new way of high-value utilization, the purpose of the present invention is to provide a method for preparing calcium carbonate micro-nano balls by using calcium lignosulfonate regulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for regulating and controlling preparation of calcium carbonate micro-nanospheres through calcium lignosulfonate
  • Method for regulating and controlling preparation of calcium carbonate micro-nanospheres through calcium lignosulfonate
  • Method for regulating and controlling preparation of calcium carbonate micro-nanospheres through calcium lignosulfonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1) Under the action of mechanical stirring, dissolve the calcium lignosulfonate derived from coniferous wood in distilled water, and adjust the pH value with NaOH solution to form an organic solution of calcium lignosulfonate at 40 g / L and pH 11;

[0021] 2) Under the action of mechanical stirring, add 10mL of 0.5mol / L CaCl with pH=7 to 10mL of calcium lignosulfonate organic matter solution obtained in step 1) 2 solution, forming calcium lignosulfonate-CaCl 2 mixed growth system;

[0022] 3) Under the condition of stirring speed of 150r / min and 30℃, 0.5mol / L Na with pH=7 2 CO 3 The solution was added dropwise to the calcium lignosulfonate-CaCl obtained in step 2) 2 Mixed growth system, Na 2 CO 3 solution with calcium lignosulfonate-CaCl 2 The volume ratio of the mixed growth system is 1:2. After the dropwise addition, cool the above solution to 25°C at room temperature, let it stand for crystallization for 24 hours, and vacuum filter the reaction system to obtain ...

Embodiment 2

[0024] 1) Under the action of mechanical stirring, dissolve the calcium lignosulfonate derived from broad-leaved wood in distilled water, and adjust the pH value with NaOH solution to form a 30g / L, pH9 calcium lignosulfonate organic matter solution;

[0025] 2) Under the action of mechanical stirring, add 10mL of 0.5mol / L CaCl with pH=7 to 10mL of calcium lignosulfonate organic matter solution obtained in step 1) 2 solution, forming calcium lignosulfonate-CaCl 2 mixed growth system;

[0026] 3) Under the condition of stirring speed of 150r / min and 40℃, 0.5mol / L Na with pH=7 2 CO 3 The solution was added dropwise to the calcium lignosulfonate-CaCl obtained in step 2) 2 Mixed growth system, Na 2 CO 3 solution with calcium lignosulfonate-CaCl 2 The volume ratio of the mixed growth system is 1:1. After the dropwise addition, cool the above solution to 25°C at room temperature, let it stand for crystallization for 24 hours, and vacuum filter the reaction system to obtain crys...

Embodiment 3

[0028] 1) Dissolve calcium lignosulfonate from Poaceae in distilled water under the action of mechanical stirring, and adjust the pH value with NaOH solution to form a 20g / L, pH7 calcium lignosulfonate organic solution;

[0029] 2) Under the action of mechanical stirring, add 10mL of 0.5mol / L CaCl with pH=7 to 10mL of calcium lignosulfonate organic matter solution obtained in step 1) 2 solution, forming calcium lignosulfonate-CaCl 2 mixed growth system;

[0030] 3) Under the condition of stirring speed of 150r / min and 50℃, 0.5mol / L Na with pH=7 2 CO 3 The solution was added dropwise to the calcium lignosulfonate-CaCl obtained in step 2) 2 Mixed growth system, Na 2 CO 3 solution with calcium lignosulfonate-CaCl 2The volume ratio of the mixed growth system is 2:1. After the dropwise addition, cool the above solution to 25°C at room temperature, let it stand for crystallization for 24 hours, and vacuum filter the reaction system to obtain crystals, which are washed with dis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for regulating and controlling preparation of calcium carbonate micro-nanospheres through calcium lignosulfonate. The method is characterized by taking calcium lignosulfonate as an organic substrate on the basis of a biological mineralization principle, and changing such technological parameters as calcium lignosulfonate concentration, concentration ratio of Ca<2+> to CO3<2->, system temperature, system pH value and the like, so as to regulate and control regulation of calcium carbonate micro-nanospheres differing in morphology and size, thus meeting application demands in various technological fields. The technology disclosed by the invention is rapid, efficient and environmentally friendly; and the prepared calcium carbonate micro-nanospheres differing in morphology and size, which take calcium lignosulfonate as an organic regulating and control substrate in raw materials thereof, can be widely applied to such industries as paper making, rubber, plastic and the like, and the calcium carbonate micro-nanospheres have important environmental benefit and economic value.

Description

technical field [0001] The invention relates to a method for regulating and preparing calcium carbonate micro-nano pellets, in particular to a method for regulating and preparing calcium carbonate micro-nano pellets by using calcium lignosulfonate, which belongs to the technical field of pulp and papermaking engineering. Background technique [0002] Calcium carbonate is one of the most abundant inorganic minerals on the earth, and is widely used in papermaking, rubber, plastics, coatings, ceramics, cosmetics and other industrial fields. Calcium carbonate belongs to polymorphic crystals. Calcite, aragonite and vaterite are the types of calcium carbonate in nature. In addition, there is amorphous calcium carbonate, of which the calcite type is the most stable. Under normal circumstances, the carbonization method obtains cubic calcite calcium carbonate crystals. [0003] Different industries have different requirements for the form of calcium carbonate. A series of parameter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01F11/18
Inventor 张勇姚菊明马东旭杨梦梦
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com