Two-step preparation method of acrylamide copolymer

An acrylamide copolymer, acrylamide technology, applied in chemical instruments and methods, drilling compositions, etc., can solve the problems of large amount of stabilizer and low use efficiency, and achieve good antioxidant performance and high apparent viscosity. , the effect of good oil displacement effect

Active Publication Date: 2014-05-14
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this invention, due to the physical blending between the dithioamine-based metal salt small-molecule stabilizer and HPAM, there will be a chromatographic separation effect between the small-molecule stabilizer and the polymer oil displacement agent during actual use. , resulting in a large amount of stabilizer and low efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-step preparation method of acrylamide copolymer
  • Two-step preparation method of acrylamide copolymer
  • Two-step preparation method of acrylamide copolymer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] In a preferred embodiment of the present invention, the preparation method of the acrylamide copolymer comprises the following steps:

[0049] (1) Mix acrylamide, 2-acrylamido-2-methylpropanesulfonic acid and allylthiourea with deionized water to make acrylamide, 2-acrylamido-2-methylpropanesulfonic acid and a solution with a total concentration of allylthiourea of ​​20 to 30% by weight (that is, the first monomer mixture solution), the temperature of the solution is controlled at -10 to 20°C, and the pH is adjusted to 4 to 12 with an inorganic basic compound (preferably 6-9), to obtain acrylamide, 2-acrylamido-2-methylpropanesulfonate and allylthiourea monomer solution (ie, the second monomer mixture solution);

[0050](2) Pump the monomer solution of acrylamide, 2-acrylamido-2-methylpropanesulfonate and allylthiourea obtained in step (1) into the polymerization kettle, add water-soluble azo initiator and Amine reducing agent, pass high-purity nitrogen to remove oxyge...

Embodiment 1

[0068] This example is used to illustrate the acrylamide copolymer and its preparation method according to the present invention.

[0069] Add 869.56 kg (12.233 kmol) of acrylamide, 1647.86 kg (7.951 kmol) of 2-acrylamido-2-methylpropanesulfonic acid and 23.68 kg (2.038 mol) of allylthiourea into the batching kettle, and 5929 kg of deionized Water, under stirring, control the temperature of the solution with frozen brine to -7°C, and add sodium hydroxide to adjust the pH to 6. Pump the monomer solution into the polymerization tank, add 12.706 grams of water-soluble azo initiator 2,2'-azo(2-amidinopropane) dihydrochloride and reducing agent N,N,N',N' -Tetramethylethylenediamine 12.706 grams, through high-purity nitrogen deoxygenation 0.5h, add 12.706 grams of sodium bisulfite and ammonium persulfate 12.706 grams, continue to pass nitrogen until the thermocouple in the polymerization kettle starts to heat up, and the reaction time is 10 hours to obtain Acrylamide copolymer (ie,...

Embodiment 2

[0073] This example is used to illustrate the acrylamide copolymer and its preparation method according to the present invention.

[0074] Add 1,530 kg of acrylamide, 45.752 kg of 2-acrylamido-2-methylpropanesulfonic acid, 38.477 kg of allyl sulfide, 6,457 kg of deionized water into the batching kettle, and control the temperature of the solution with frozen brine to 15°C under stirring , adding sodium hydroxide to adjust the pH to 9. Pump the monomer solution into the polymerization tank, add 807.11 grams of water-soluble azo initiator 2,2'-azo(2-amidinopropane) dihydrochloride and reducing agent N,N,N',N' -Tetramethylethylenediamine 807.11 grams, through high-purity nitrogen deoxygenation 0.5h, add 807.11 grams of sodium bisulfite and ammonium persulfate 807.11 grams, continue to pass nitrogen until the thermocouple in the polymerization kettle starts to heat up, and the reaction time is 2 hours, to obtain Acrylamide copolymer. Open the ball valve at the bottom of the reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear viscosityaaaaaaaaaa
shear viscosityaaaaaaaaaa
shear viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a two-step preparation method of an acrylamide copolymer. The two-step preparation method is characterized in that by initiation of a novel low-temperature oxidation-reduction composite initiation system, acrylamide (AM), 2-acrylamide-2-methylpro panesulfonic acid (AMPS) and allylthiourea undergo an aqueous solution adiabatic polymerization reaction, rubber bricks are subjected to primary granulation, the rubber granules are subjected to hydrolysis, the hydrolysis product is subjected to secondary granulation, and the granules are dried, crushed and screened so that the acrylamide copolymer is obtained. The acrylamide copolymer has good high-temperature oxidation resistance. The invention discloses the oxidation-resistant polyacrylamide oil-displacement agent and the preparation method thereof.

Description

technical field [0001] The invention relates to a method for preparing an acrylamide copolymer. Background technique [0002] The development of petroleum engineering and technology requires maximizing the recovery of existing oil fields. As the main polymer oil displacement agent, partially hydrolyzed polyacrylamide (HPAM) has been popularized and applied on a large scale in conventional oil reservoir EOB technology, and has played an important role in stabilizing and increasing oilfield production. With the reduction of reserves in conventional oil reservoirs, the application of HPAM in high-temperature and high-salt reservoirs faces many difficulties, mainly reflected in the combination of high temperature, high salinity and dissolved oxygen conditions in the development of high-temperature and high-salt reservoirs, which makes HPAM The viscosity of the solution is greatly reduced, resulting in insignificant HPAM flooding effect. Studies have shown that when the tempera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/56C08F220/58C08F228/02C08F8/12C09K8/588
Inventor 伊卓黄凤兴杜凯刘希林蔚然
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com