Silicone rubber and its preparation method

A silicone rubber and rubber technology, applied in the field of silicone rubber and its preparation, can solve the problems of large compression set and low rebound rate.

Active Publication Date: 2016-06-01
MIDGOLD FINE PERFORMANCE MATERIALS SHENZHEN
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of science and technology, higher requirements are put forward for the compression deformation and resilience performance of silicone rubber. In the prior art, silicone rubber generally has a large compression set, a low rebound rate, or both. It can no longer meet the special requirements of some products on the market, such as some high-end automobile shaft seal rings, gaskets, sealing miscellaneous parts, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] In another aspect of the present invention, the present invention proposes a method for preparing silicone rubber. According to an embodiment of the present invention, the method includes: methyl vinyl silicone rubber, calcium stearate, white carbon black, dimethyl Diethoxysilane, calcium carbonate, cerium oxide, ferric isooctanoate organic solution, vinyl MQ silicone resin and quartz powder are mixed to obtain a silicone rubber compound; the silicone rubber compound is mixed with 2,5-dimethyl -2,5-bis(tert-butylperoxy)hexane is mixed to obtain silicone rubber, in which methylvinyl silicone rubber, calcium stearate, silica, dimethyldiethoxysilane , calcium carbonate, cerium oxide, organic solution of ferric isooctanoate, vinyl MQ silicone resin, quartz powder and 2,5-dimethyl-2,5-bis(tert-butylperoxy)hexane: 100 Parts by weight of methyl vinyl silicone rubber; 30-40 parts by weight of white carbon black; 3-6 parts by weight of dimethyldiethoxysilane; 0.10-0.15 parts by ...

Embodiment 1

[0033] Raw material formula:

[0034] 1000g of methyl vinyl silicone rubber, 350g of white carbon black, 50g of dimethyldiethoxysilane, 1.4g of calcium stearate, 250g of quartz powder, 80g of calcium carbonate, 20g of cerium oxide, 1.0 g parts by weight of ferric isooctanoate organic solution, 20 g of vinyl MQ silicone resin, and 15 g of 2,5-dimethyl-2,5-bis(tert-butyl peroxy).

[0035] Preparation:

[0036] Knead methyl vinyl silicone rubber raw rubber and calcium stearate in a kneader for 3 to 5 minutes, then add white carbon black and dimethyldiethoxysilane to the kneader in 4 times, after each addition Stir for 30 minutes; after the white carbon black and diethoxysilane are mixed with the obtained mixture to form, the obtained molding mixture is heated to 150-160 degrees Celsius, and vacuumed, and kept for 2-3 hours; the temperature of the obtained heated material is lowered To 80 degrees Celsius, sequentially add calcium carbonate, cerium oxide, iron isooctanoate organi...

Embodiment 2

[0038] Raw material formula:

[0039] 1000g of methyl vinyl silicone rubber, 350g of white carbon black, 50g of dimethyldiethoxysilane, 1.4g of calcium stearate, 250g of quartz powder, 80g of calcium carbonate, 20g of cerium oxide, 3.0 g parts by weight of ferric isooctanoate organic solution, 20 g of vinyl MQ silicone resin, and 15 g of 2,5-dimethyl-2,5-bis(tert-butyl peroxy).

[0040] Preparation method: with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
deformation rateaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a silicone rubber and a preparation method thereof. The silicone rubber contains, by weight, 100 parts of methyl vinyl silicone rubber, 30 to 40 parts of white carbon black, 3 to 6 parts of dimethyldiethoxylsilane, 0.10 to 0.15 part of calcium stearate, 20 to 30 parts of quartz powder, 6 to 10 parts of calcium carbonate, 1 to 3 parts of cerium oxide, 0.1 to 0.7 part of an iron isocaprylate organic solution, 2 to 5 parts of vinyl MQ silicone resin and 1.5 parts of 2,5-dimethyl-2,5-bis(t-butylperoxy)hexane. According to embodiments in the invention, the silicone rubber has high resilience and low compression set performance at the same time.

Description

technical field [0001] The invention relates to the field of organic synthesis, in particular, the invention relates to a silicone rubber and a preparation method thereof. Background technique [0002] Due to the excellent comprehensive properties of high-temperature vulcanized silicone rubber products, they have been widely used in aviation, electronics, electrical, chemical, instrumentation, automobile and other industries, as well as in various fields of medical care and daily life. With the development of science and technology, higher requirements are put forward for the compression deformation and resilience performance of silicone rubber. In the prior art, silicone rubber generally has a large compression set, a low rebound rate, or both. It can no longer meet the special requirements of some products on the market, such as some high-end automobile shaft seal rings, gaskets, sealing miscellaneous parts, etc. Therefore, reducing the compression set of silicone rubber ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/07C08K13/02C08K3/36C08K5/5419C08K5/098C08K3/26C08K3/22C08K5/14B29C35/02
Inventor 曾稳滔宋斌赵祺
Owner MIDGOLD FINE PERFORMANCE MATERIALS SHENZHEN