Production method of high-temperature resistant washable quilting fabric

A production method and high-temperature-resistant technology, applied to chemical instruments and methods, layered products, lamination devices, etc., can solve the problems of uneven glue application, large gaps, poor washing resistance, etc., and achieve simple production methods and easy to use The effect of long life and good performance

Inactive Publication Date: 2014-06-18
QINGDAO TONGGUANWANG IND
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current composite fabrics are mainly combined by glue and quilting. The glue is prone to problems such as uneven glue application and air bubbles; the quilted fabric has the characteristics of neat stitches, beautiful overall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] The production method of the high temperature resistant and washable quilted cloth of the present embodiment comprises the following steps:

[0017] 1) Suture line preparation for quilted cloth: use aramid thread as the suture line;

[0018] 2) Selection of quilted fabric: quilted fabric includes brushed fabric and needle-punched cotton;

[0019] 3) Fabric finishing: wash the brushed cloth with cold and hot water, and then coat it to obtain a coated fabric layer;

[0020] 4) Composite layering: After finishing the napped fabric, lay the needle-punched cotton evenly on the napped fabric for laying. The thickness of the needle-punched cotton is translucent;

[0021] 5) Cutting, hemming, and sparse quilting of the above-mentioned layered fabrics to obtain quilted fabrics;

[0022] 6) Select the waterproof layer film, the waterproof layer film is preferably TPU film;

[0023] 7) Lamination of the waterproof layer film, preheating the glue coating of the waterproof layer ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of high-temperature resistant washable quilting fabric. According to the production method, aramid yarm is taken as suture line; quilting fabric is made from nap cloth and semitransparent acupuncture cotton; the nap cloth is washed with cold water and hot water, and is subjected to coating treatment so as to obtain coated fabric; the coated fabric is subjected to finish, and then is coated with the acupuncture cotton uniformly; the processed coated fabric is subjected to cutting, edge coating, and sparse quilting so as to obtain common quilting cloth; TPU thin film is used for preparing a waterproof layer preferably, is subjected to gluing preheat, and is subjected to hotpressing with the obtained common quilting cloth using a combination machine; and finished products are obtained after cooling. The production method is simple, and is suitable for batch production; the acupuncture cotton is semitransparent, and is capable of helping the suture line to immobilize effectively; the high-temperature resistant washable quilting fabric is beautiful in appearance, is capable of resisting washing and high temperature, can be washed for 50 times with water at a temperature of 90 DEG C, and still possesses excellent performance.

Description

[0001] technical field [0002] The invention belongs to the technical field of cloth processing, and in particular relates to a production method of high-temperature-resistant and washable quilted cloth. Background technique [0003] The current composite fabrics are mainly combined by glue and quilting. The glue is prone to problems such as uneven glue application and air bubbles; the quilted fabric has the characteristics of neat stitches, beautiful overall effect, and good hand feeling, but Due to the large gaps between the quilting lines, the quilted fabric is more troublesome to wash, high temperature resistance, and poor washing resistance, which shortens the service life of the fabric. Contents of the invention [0004] In order to overcome the above-mentioned technical problems in cloth processing in the prior art, the object of the present invention is to provide a production method of high temperature and washable quilted cloth, which has simple process, beautif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B38/18B32B37/12B32B37/06
Inventor 宋礼华
Owner QINGDAO TONGGUANWANG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap