A production method and technology of inkstone, applied to clay products, printing, office supplies, etc., to achieve cost-saving, solid texture, and considerable economic benefits

Inactive Publication Date: 2014-06-18
惠东存
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Covered out of the pottery stove, without luster

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for making a stone powder inkstone, comprising the following steps:

[0028] (1) First select the relatively pure corner waste in the inkstone for pulverization, then pulverize the auxiliary materials dolomite, coal gangue and quartz stone into fine powder respectively;

[0029] (2) Raw materials: inkstone, dolomite, coal gangue, quartzite, clay, water are added in the ball mill together, the mass parts of each constituent in the described raw material are respectively: inkstone 70 parts, dolomite 8 parts, coal 5 parts of gangue, 7 parts of quartz stone, 20 parts of clay, and 100 parts of water are ground for 70 hours to obtain refined mud (the fineness of which exceeds 400 mesh sieves);

[0030] (3) put the refined mud obtained in step (2) into the pond to dry in the shade, after the refined mud is dehydrated by 70%, place the mud in the cellar, and after sinking for 180 days, make the refined mud into an inkstone shape;

[0031] (4) When the moisture content...

Embodiment 2

[0037] A method for making a stone powder inkstone, comprising the following steps:

[0038] (1) First select the relatively pure corner waste in the inkstone for pulverization, then pulverize the auxiliary materials dolomite, coal gangue and quartz stone into fine powder respectively;

[0039] (2) Raw materials: inkstone, dolomite, coal gangue, quartzite, clay, water are added in the ball mill together, the mass parts of each constituent in the described raw material are respectively: inkstone 70 parts, dolomite 8 parts, coal 5 parts of gangue, 7 parts of quartz stone, 20 parts of clay, and 100 parts of water were ground for 76 hours to obtain refined mud (the fineness was passed through a 500-mesh sieve);

[0040] (3) Filter the refined mud obtained in step (2) and put it in a pool to dry in the shade. After the refined mud is dehydrated by 70%, put the mud in the cellar, and after 180 days of decay, make the refined mud into an inkstone shape ;

[0041] (4) When the moist...

Embodiment 3

[0047] A method for making a stone powder inkstone, comprising the following steps:

[0048] (1) First select the relatively pure corner waste in the inkstone for pulverization, then pulverize the auxiliary materials dolomite, coal gangue and quartz stone into fine powder respectively;

[0049] (2) Raw materials: inkstone, dolomite, coal gangue, quartzite, clay, water are added in the ball mill together, the mass parts of each constituent in the described raw material are respectively: inkstone 70 parts, dolomite 8 parts, coal 5 parts of gangue, 7 parts of quartz stone, 20 parts of clay, and 100 parts of water were ground for 82 hours to obtain refined mud (the fineness of which was passed through a 600-mesh sieve);

[0050] (3) Filter the refined mud obtained in step (2) and put it in a pool to dry in the shade. After the refined mud is dehydrated by 70%, put the mud in the cellar, and after 180 days of decay, make the refined mud into an inkstone shape ;

[0051] (4) When ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing Chengni inkstone. The method comprises the following twenty-two process steps: selecting a stone, breaking the stone, ball-milling, cleaning, drying in the shade, corroding, forming, pressurizing, designing, shoveling the blank, carving, finely grinding, drying, roasting, finishing, drying finely, cooking in rice vinegar, fine and accurate grinding in water, maintaining, polishing, checking and packaging. The inkstone manufactured by the method is excellent in service performance and ink rising is easy.

Description

technical field [0001] The invention belongs to the technical field of stationery, and relates to a method for making stone powder inkstone. Background technique [0002] Inkstone is one of the four treasures of the study and one of the indispensable tools for literati to write and paint. There are many kinds of domestic inkstones, but they can be summed up into two categories. One is carved from various natural stones, called stone inkstones; It is refined by sixteen processes such as making. However, Shimo inkstone is not only different from stone inkstone, but also different from Chengni inkstone. Its raw material comes from stone, but its processing technology is similar to that of Chengni inkstone. It is fired by a process. During the Tang and Song Dynasties in ancient my country, Shimo inkstone was produced, and literati and inkmen gave it a high evaluation: [0003] "Public rights... the only treasures are brush and inkstone pictures, which are self-made. Often co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13B43L27/00
Inventor 惠东存
Owner 惠东存
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap