CPE pattern isolating membrane of glass interlayer PVB membrane and production method thereof

A technology of isolation film and interlayer, which is applied in the field of CPE isolation film, to achieve the effect of good surface smoothness and smoothness, not easy to absorb dust, and high authenticity rate

Active Publication Date: 2014-06-25
TIANTAI JIUDING PLASTIC CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After retrieval and market research, no CPE isolation film and its production method w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CPE pattern isolating membrane of glass interlayer PVB membrane and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1 (composition of corresponding embodiment in the comparison table and the proportioning value thereof by weight):

[0023] First prepare the calcium carbonate mixture, mix well with 25 parts of this material, 50 parts of high-pressure low-density PE, 50 parts of low-pressure high-density PE, 100 parts of linear PE, 2.13 parts of antistatic agent, 2.13 parts of decrystallization agent, and 2.1 parts of metallocene Finally, bake at 80°C for 2 hours until the moisture content is ≤ 2%, put it into the screw extruder, and extrude it in hot melt until it becomes jelly. Pressed into a wide film, then drawn, coiled and slitting. After passing the inspection, it is packaged, put into storage and stacked or leaves the factory.

[0024] Among the nine embodiments, the products in the first 1-4 items are suitable for the needs of domestic consumers, and the products in the latter 5-9 items are suitable for export. Wherein preferred with embodiment 2,3,7.

[0025] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a CPE pattern isolating membrane of a glass interlayer PVB membrane. The CPE pattern isolating membrane is prepared from the following components in parts by weight: 12.5 or 25 parts of calcium carbonate mixed material, 50 parts of high pressure low density polyethylene, 50 parts of low pressure high density polyethylene, 100 parts of linear high pressure low density polyethylene, 2.13-6.38 or 2.3-6.8 parts of PE antistatic agent, 2.13-10.62 or 2.3-11.3 parts of PE-A crystal point removing agent and 2.1-21.3 or 2.3-22.5 parts of metallocene. The rolled isolating membrane product is colorless and semitransparent, the thickness is 20+/-2 mu m, the gram per square meter is less than or equal to 20+/-2, the surface detail height is less than 100 mu m, the vertical strength is greater than 10MPa, the vertical or lateral elongation is greater than 150%, and the lateral strength is greater than 8MPa. The product is prepared by the following six steps: preparation of the calcium carbonate mixed material; stocking; mixing; casual inspection; drying; feeding. The isolating membrane prepared is weak in static electricity, unremarkable in hitting people, difficult in dust collection and impurity absorption, high in rate of graded product, few in crystal point, flat and smooth in surface, high in membrane strength and good in malleability.

Description

technical field [0001] The invention relates to a production method of a plastic film, in particular to a production method of a CPE isolation film with concavo-convex patterns on the surface of a PVB film (polyvinyl butyral intermediate film) used in laminated glass for automobiles or building doors and windows. Background technique [0002] There are many types of interlayer films in laminated glass, which can prevent the fragments from splashing and hurting people when they are hit or broken by falling. Such as CN201110291114.2 Zhejiang Agriculture and Forestry University has authorized the patent right of "high tensile strength multi-mixed PVB membrane and its production method", due to the different components, content and process, the membrane is different from the two layers The glass is pasted into one body, flat and transparent, and there is no need to use an isolation film. If the PVB interlayer film is pasted between the two layers of glass, it is difficult to ach...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L23/06C08K13/02C08K3/26C08K5/09C08K5/098
CPCC08J5/18C08J2323/08C08J2423/06C08K2201/017C08L23/0815C08L2203/16C08L2205/025C08L2205/035C08L2207/062C08L2207/066C08L23/06C08K13/02C08K2003/265C08K5/09C08K5/098
Inventor 朱丰裕林坚杨庆辉吴伟飞
Owner TIANTAI JIUDING PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap