Epoxy resin-base film for flexible or thin-film solar cells and preparation method thereof

A technology of epoxy resin base film and solar cell, which is applied in the direction of circuits, photovoltaic power generation, electrical components, etc., can solve the problem of low shrinkage, achieve the effect of improving power generation efficiency and light absorption efficiency

Inactive Publication Date: 2014-07-02
ZHONGYUAN ENGINEERING COLLEGE
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) 8Kg glycidyl ether epoxy resin solution (solid content of epoxy resin is 10%) (Zhejiang Kaihua Chengxin Resin Co., Ltd.), 20 Kg N,N-dimethylformamide, 10Kg toluene to prepare a solution , the epoxy resin-based solution; 61.9999 Kg tetrahydrofuran was stirred and blended evenly at a temperature of 0°C with an emulsifier;

[0025] (2) Add 0.0001Kg nano-aluminum powder to the above solution at room temperature and mix it with an emulsifier, and use ultrasonic treatment to obtain a uniformly mixed colloidal blend;

[0026] (3) Import the above blend into the screw mixing extruder for blending and extrusion, the temperature is controlled at 80-90 ° C, the extruded product is filtered through a 150-mesh filter, the pressure difference between the inlet and outlet of the metering pump is 1 MPa, metered, extruded, and cast A film thickness of 100 UM, 10 degrees air cooling, 2 times the drafting ratio drawing, pulling, coiling and other processes, to obtain a flexible or thi...

Embodiment 2

[0029] (1) Mix 9Kg glycidyl ester epoxy resin solution (solid content of epoxy resin is 8%) (Foshan Longxiang Resin Raw Materials Co., Ltd.), with 10 Kg N,N-dimethylformamide, 10Kg acetone, 10Kg tetrahydrofuran and 10Kg butyl acetate were prepared into a solution; the epoxy resin-based solution; 50.9Kg tetrahydrofuran was stirred and blended evenly at a temperature of 140°C with an emulsifier;

[0030](2) Add 0.1Kg of nano-aluminum powder to the above solution at room temperature and mix it with an emulsifier, and use ultrasonic treatment to obtain a uniformly mixed colloidal blend;

[0031] (3) Import the above blend into a screw mixing extruder for blending and extrusion, the temperature is controlled at 80°C, the extrudate is filtered through a 150-mesh filter, the pressure difference between the inlet and outlet of the metering pump is 1MPa, metered and extruded, and the cast film thickness 100UM, 10 degrees air cooling, 2 times the drafting ratio, drawing, pulling, coilin...

Embodiment 3

[0034] (1) Mix 10Kg glycidylamine epoxy resin solution (solid content of epoxy resin is 5%) (Foshan Longxiang Resin Raw Material Co., Ltd.), with 10 Kg N,N-dimethylformamide, 10Kg benzene, 10Kg tetrahydrofuran and 10Kg butyl acetate were prepared into a solution, and the epoxy resin-based solution and 49.999% benzene were stirred and blended evenly at a temperature of 100°C with an emulsifier;

[0035] (2) Add 0.001Kg nano-aluminum powder to the above solution at room temperature and mix it with an emulsifier, and use ultrasonic treatment to obtain a uniformly mixed colloidal blend;

[0036] (3) Import the above blend into a screw mixing extruder for blending and extrusion, the temperature is controlled at 90°C, the extrudate is filtered through a 150-mesh filter, the pressure difference between the inlet and outlet of the metering pump is 1MPa, metered and extruded, and the cast film thickness 100UM, 10 degrees air cooling, 2 times the drafting ratio, drawing, pulling, coilin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an epoxy resin-base film for flexible or thin-film solar cells and a preparation method thereof. The film is prepared from the following components in percentage by mass: 8-12% of epoxy resin-base resin solution (the solid content of epoxy resin is 1-10%), 0.0001-0.1% of nano aluminum powder and the balance of solvent. The preparation method comprises the following steps: blending the materials, filtering, introducing into a running die head, cooling, drawing, coiling and the like to obtain the epoxy resin-base film for solar cells. The product is attached to the photic surface of the thin-film solar cell or used as an upper packaging film of the solar cell to directly enhance the generating efficiency of the flexible or thin-film solar cell.

Description

technical field [0001] The invention relates to an epoxy resin base film for flexible or thin-film solar cells and a preparation method thereof. By using the film to encapsulate the light-incident surface of the flexible or thin-film solar cell, the efficiency of the flexible or thin-film solar cell can be directly improved. Background technique [0002] Among the projects of effective utilization of solar energy: photovoltaic utilization is the fastest growing and most dynamic research field in recent years. Generally, the production of solar cells is mainly based on semiconductor materials, which use photoelectric materials to absorb light energy and generate photoelectric conversion reactions to generate electricity. According to the different materials used, solar cells can be divided into: 1. Silicon solar cells; 2. Solar cells made of inorganic salts such as gallium arsenide III-V compounds, cadmium sulfide, copper indium selenide and other multi-component compounds; 3...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K3/08H01L31/048
CPCY02E10/50
Inventor 张迎晨吴红艳
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com