PC/PA6 composition and preparation method for same

A composition and polycarbonate technology, applied in the field of materials, can solve the problems of poor compatibility, affecting the performance and application of the blending system, and achieve easy control, high flame retardancy, chemical resistance and good processing performance. Effect

Active Publication Date: 2014-07-30
SINOPLAST NEW MATERIAL
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Due to the huge difference in the crystallization properties of the two components in the PC/PA6 ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC/PA6 composition and preparation method for same
  • PC/PA6 composition and preparation method for same
  • PC/PA6 composition and preparation method for same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] In this example, a PC / PA6 composition is prepared by an in-situ reaction compatibilization method, which is prepared from the following raw materials:

[0085]

[0086] The preparation method of above-mentioned PC / PA6 composition, comprises the following steps:

[0087] (1) Place the polycarbonate (PC) and polyamide 6 (PA6) at 110° C., dry for 4 hours, and after cooling, add the polycarbonate and polyamide 6 to a high-speed mixer for pre-mixing;

[0088] (2) Toluene diisocyanate (TDI), 2,2'-(1,3-phenylene)-bisoxazoline (PBO), styrene-maleic anhydride copolymer B (SMA), anti-dripping Agent, hindered phenolic antioxidant, phosphite antioxidant and lubricant join in another high-speed mixer and mix, then join the obtained mixture in the high-speed mixer in step (1) and mix;

[0089] (3) Place the pre-mixture mixed in step (2) in a parallel twin-screw extruder to melt and extrude, and granulate. The process parameters are as follows: the temperature of the first zone is...

Embodiment 2

[0092] In this example, a PC / PA6 composition is prepared by an in-situ reaction compatibilization method, which is prepared from the following raw materials:

[0093]

[0094] The preparation method of above-mentioned PC / PA6 composition, comprises the following steps:

[0095] (1) Place the polycarbonate (PC) and polyamide 6 (PA6) at 110° C., dry for 4 hours, and after cooling, add the polycarbonate and polyamide 6 to a high-speed mixer for pre-mixing;

[0096](2) Toluene diisocyanate (TDI), 2,2'-(1,3-phenylene)-bisoxazoline (PBO), styrene-maleic anhydride copolymer A (SMA), anti-dripping Agent, hindered phenolic antioxidant, phosphite antioxidant and lubricant join in another high-speed mixer and mix, then join the obtained mixture in the high-speed mixer in step (1) and mix;

[0097] (3) Place the pre-mixture mixed in step (2) in a parallel twin-screw extruder to melt and extrude, and granulate. The process parameters are as follows: the temperature of the first zone is ...

Embodiment 3

[0100] In this example, a PC / PA6 composition is prepared by an in-situ reaction compatibilization method, which is prepared from the following raw materials:

[0101]

[0102]

[0103] The preparation method of above-mentioned PC / PA6 composition, comprises the following steps:

[0104] (1) Place the polycarbonate (PC) and polyamide 6 (PA6) at 110° C., dry for 4 hours, and after cooling, add the polycarbonate and polyamide 6 to a high-speed mixer for pre-mixing;

[0105] (2) Toluene diisocyanate (TDI), 2,2'-(1,3-phenylene)-bisoxazoline (PBO), styrene-maleic anhydride copolymer B (SMA), anti-dripping Agent, hindered phenolic antioxidant, phosphite antioxidant and lubricant join in another high-speed mixer and mix, then join the obtained mixture in the high-speed mixer in step (1) and mix;

[0106] (3) Place the pre-mixture mixed in step (2) in a parallel twin-screw extruder to melt and extrude, and granulate. The process parameters are as follows: the temperature of the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Molecular weightaaaaaaaaaa
Number average molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a PC/PA6 composition and a preparation method for the same. The PC/PA6 composition is prepared from the following raw materials in parts by weight: 65-90 parts of polycarbonate, 10-35 parts of polyamide 6, 0.1-3 parts of toluene diisocynate, 0.1-3 parts of 2,2'-(1,3-phenylene)-dioxazoline, 0.1-6 parts of styrene-maleic anhydride copolymer, 0.1-2 parts of anti-drip agent, 0.1-1 part of hindered phenol antioxidant, 0.1-1 part of phosphite ester antioxidant and 0.1-1 parts of lubricant, wherein the sum of the parts by weight of polycarbonate and polyamide 6 is 100 parts. The PC/PA6 composition disclosed by the invention, which is good in mechanical property, and high in flame retardance, chemical resistance and processability, is prepared by a method of in-situ reactive compatibilization, and can be applied to the industries such as automobiles and electronics and electrical appliances.

Description

technical field [0001] The invention relates to the field of materials, in particular to a PC / PA6 composition and a preparation method thereof. Background technique [0002] The rapid development of China's industry in recent years has continuously expanded the application of polycarbonate (PC), and its demand has also continued to increase. However, with the rapid advancement of science and technology and the continuous upgrading of industrial products, the requirements for material performance are becoming more and more stringent. Conventional polycarbonate can no longer meet the requirements of various types of products in terms of product performance, and PC has a melt viscosity. Large size, poor fluidity, easy hydrolysis at high temperature, poor solvent resistance, high sensitivity to notches, prone to swelling and stress cracking, and large friction coefficient, high melting temperature, high price of special grades, etc., which directly affect its further application...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L77/02C08L35/06C08L27/18C08K5/134C08K5/526C08K5/103C08K5/29C08K5/353B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/625B29C48/92B29C2948/9259B29C2948/92704B29C2948/92895
Inventor 朱怀才王忠强钟毅文许环杰陈列
Owner SINOPLAST NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap