A kind of high-strength cable material for rail vehicle and preparation method thereof

A rail vehicle, high-strength technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve unsatisfactory problems, achieve good thermal stability, good heat aging resistance, and excellent electrical insulation performance

Active Publication Date: 2016-05-11
ANHUI KANGLIYA CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the mechanical strength of cable materials on the market can no longer meet the performance requirements of rail vehicle cables with faster and faster speeds. Therefore, it is urgent to change the formula of traditional cable materials and develop a high-strength cable material to improve the safety performance of rail vehicle cables.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength cable material for rail vehicle and preparation method thereof
  • A kind of high-strength cable material for rail vehicle and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-strength cable material for rail vehicles is prepared from the following raw materials in parts by weight: polyphenylene sulfide 95, aromatic polycarbonate 50, ethylene-methyl acrylate-glycidyl methacrylate terpolymer 30, Diphenylmethane diisocyanate 6, bis(4-carboxyphenyl)phenylphosphine oxide 14, zinc aluminate 12, magnesium hydroxide 25, basalt staple fiber 10, methacryloxypropyltrimethoxysilane 2.5 , Tris(mercaptoethyl stearate) antimony 4, calcium stearate 2, barium stearate 2, erucamide 6, polyethylene wax 4, calcined clay 18, basic magnesium chloride whisker 12, precipitated silica 25. Modified stone powder 16, methyl epoxy acetyl ricinoleate 12, antioxidant 12222.5;

[0014] The preparation method of the modified stone powder is as follows: (1) Weigh the coke gemstone, volcanic stone, and attapulgite in a weight ratio of 5:3:2, mix evenly, calcinate at 780° C. for 1.5 hours, naturally cool to room temperature, pulverize, and pass sieve, stand-by; (2) tak...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength cable material used for a railway vehicle, and a preparation method thereof. The high-strength cable material is prepared from the following raw materials by weight: 85-105 parts of polyphenylene sulfide, 40-60 parts of aromatic polycarbonate, 25-35 parts of ethylene-methyl acrylate-glycidyl methacrylate terpolymer, 4-8 parts of diphenyl-methane-diisocyanate, 12-16 parts of bis(4-carboxyphenyl)phenyl-phosphine oxide, 10-15 parts of zinc aluminate, 20-30 parts of magnesium hydroxide,8-12 parts of basalt short fibers, 2-3 parts of methacryloyloxy propyltrimethoxysilane, 3-5 parts of tri-(stearic mercaptoacetate)antimonium, 2-3 parts of calcium stearate, 1.5-2.5 parts of barium stearate, 4-8 parts of erucyl amide, 3-6 parts of polyethylene wax, 15-20 parts of calcined clay, 10-15 parts of basic magnesium chloride whiskers, 20-30 parts of precipitated white carbon black, 14-18 parts of modified stone powder, 10-15 parts of epoxidized methyl acetorieinoleate and 2-3 parts of an antioxidant 1222. The cable material provided by the invention has the advantages of high mechanical strength, high flame retardance, fire resistance, good thermal stability, excellent electrical insulation property, wide usage temperature range, etc.

Description

technical field [0001] The invention relates to a high-strength cable material for rail vehicles and a preparation method thereof, belonging to the field of cable materials. Background technique [0002] In recent years, with the rapid development of national rail transit, the control of EMU units and high-speed units has become more and more complex, and the number of electrical control equipment has increased. The demand for cables will inevitably increase, and the performance requirements for cable materials will also increase getting stricter. At present, the mechanical strength of cable materials on the market can no longer meet the performance requirements of rail vehicle cables that are traveling faster and faster. Therefore, it is urgent to change the traditional cable material formula and develop a high-strength cable material to improve the safety performance of rail vehicle cables. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L81/02C08L69/00C08L23/08C08K13/06C08K9/04C08K9/02C08K3/34C08K3/36C08K7/04C08K7/10C08K3/22H01B3/30
Inventor 李训祥王新祥周志梅李贻凤胡云昌
Owner ANHUI KANGLIYA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com