A kind of energy-storage and temperature-regulating microcapsule phase-change thermal insulation material for clothing and its preparation method

A technology of phase change thermal insulation materials and microcapsules, which is applied in the field of thermal insulation materials to achieve the effects of large phase change enthalpy, good thermal insulation effect adjustment, and convenient operation

Active Publication Date: 2017-01-11
太仓市金锚新材料科技有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main technical problem to be solved by the present invention is to provide an energy-storage temperature-regulating phase-change thermal insulation material for clothing and its preparation method, which can solve the shortcomings of existing clothing thermal insulation materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Preparation of core material: Add 6mol polyethylene glycol and 4mol polyoctadecyl methacrylate into an electric heating stirring container, stir and mix evenly at a speed of 120r / min at 50°C, and then add 2.5mol Concentration is 10% emulsifier and 1.5mol concentration is 10% dispersant, stir and mix for 60min, set aside;

[0021] (2) Preparation of wall material prepolymer: Add the chitosan and the silica gel into a container with a stirring device at a molar ratio of 1:1, and then put the stirring container into a 70 In a water bath at ℃, stir evenly at a speed of 120r / min for later use;

[0022] (3) Preparation of microcapsule phase change thermal insulation material: Put the core material solution prepared in step (1) into a 60°C constant temperature water bath for heating and distillation, and add the condensed reflux liquid dropwise to step (2) at a rate of 0.3mL / min In the wall material prepolymer, stir at a speed of 500r / min while adding dropwise. After the ...

Embodiment 2

[0025] (1) Preparation of core material: Take 7mol polyethylene glycol and 3mol polyoctadecyl methacrylate and add them into an electric heating stirring container, stir and mix evenly at a speed of 120r / min at 80°C, then add 2.5mol Concentration is 10% emulsifier and 1.5mol concentration is 10% dispersant, stir and mix for 30min, set aside;

[0026] (2) Preparation of wall material prepolymer: Add the chitosan and the silica gel into a container with a stirring device at a molar ratio of 1:1, and then put the stirring container into a 60 In a water bath at ℃, stir evenly at a speed of 120r / min for later use;

[0027] (3) Preparation of microcapsule phase change thermal insulation material: Put the core material solution prepared in step (1) into a 50°C constant temperature water bath for heating and distillation, and add the condensed reflux liquid dropwise to step (2) at a rate of 0.3mL / min In the wall material prepolymer, stir at a speed of 500r / min while adding dropwise. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
phase transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses an energy-storage temperature-regulating microcapsule phase-change thermal insulation material for clothing and a preparation method of the material. The thermal insulation material comprises a core material and a wall material, wherein the core material is a mixture which is mixed by organic alcohol and organic ester in a molar ratio of (6-7) to (3-4); the wall material is a mixture which is mixed by chitosan and silicon dioxide gel in a molar ratio of 1 to 1; a dosage proportion of the wall material to the core material is 1 to 3; the wall material is 1 mu m-2 mu m thick; average particle diameter of the microcapsule thermal insulation material is 5 mu m-6 mu m. The preparation method comprises the following steps: (1), preparing the core material; (2), preparing a wall material prepolymer; (3), preparing a microcapsule phase-change thermal insulation material; and (4), separating and purifying. The preparation method disclosed by the invention is simple and convenient to operate; the prepared microcapsule phase-change thermal insulation material is moderate in phase-change temperature, great in enthalpy of phase change, and has the advantages of good regulation and thermal insulation effect, long thermal insulation time, no influences on clothing wearing comfort, and the like, and has a better using effect.

Description

technical field [0001] The invention relates to the field of thermal insulation materials, in particular to an energy storage temperature-regulating microcapsule phase-change thermal insulation material for clothing and a preparation method thereof. Background technique [0002] Phase Change Material (PCM - Phase Change Material) refers to a substance that changes shape with temperature and can provide latent heat. The process of a phase change material changing from solid to liquid or from liquid to solid is called a phase change process. At this time, the phase change material will absorb or release a large amount of latent heat to keep the temperature of the material constant. Since the energy latent heat of the phase change material is very large, the temperature can be maintained for a long time to achieve the purpose of heat preservation. [0003] Most of the traditional clothing insulation materials use fiber fabrics as insulation materials, and achieve a certain ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K5/06B01J13/02
Inventor 施兆武
Owner 太仓市金锚新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap