Polyvinyl chloride material for high-speed data cable

A polyvinyl chloride, data cable technology, applied in plastic/resin/wax insulators, organic insulators, etc., can solve the problem that the product index performance is difficult to meet the requirements, to improve the stability and service cycle, good mechanical stability, improve The effect of hydrophobicity

Active Publication Date: 2014-09-10
JIANGSU HENGTONG WIRE & CABLE TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, high-quality plasticizers are generally used, and fillers are reduced or not used, but the performance of product indicators is still difficult to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0020] Examples. The technical solutions of the present invention will be further described below in conjunction with specific examples, but the embodiments of the present invention are not limited thereto.

[0021] The polyvinyl chloride material used for high-speed data cables in the specific embodiment, raw materials include SG2 type PVC resin or SG3 type PVC resin: 100 parts by weight, TOTM: 32-38 parts, calcium zinc stabilizer or rare earth calcium zinc compound Stabilizer: 4-6 parts, antimony trioxide: 8-10 parts, water resistance modifier: 8-12 parts; and the water resistance modifier is composed of nano barium sulfate, calcined kaolin and nano silicon dioxide through silane Formed by coupling agent coating treatment, the parts by weight of nano-barium sulfate in the water-resistant modifier are 2-3 parts, the parts by weight of calcined kaolin are 4-7.5 parts, and the parts by weight of nano-silica 2-3 parts, and the silane coupling agent is 0.3-0.5 parts. In addition...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyvinyl chloride (PVC) material for a high-speed data cable. The polyvinyl chloride material is characterized by comprising the following components in parts by weight: 100 parts of PVC resin, 32 parts of trioctyl trimellitate, 5 parts of a calcium zinc stabilizer, 8 parts of antimony sesquioxide, 0.4 part of a lubricant, 0.2 part of an antioxidant and 10 parts of a water-resistant modifier, wherein the water-resistant modifier is formed by coating 2 parts of nano barium sulfate, 5.7 parts of calcined kaolin and 2 parts of nano silicon dioxide with 0.3 part of a silane coupling agent; and the lubricant is selected from one or more of stearic acid, barium stearate, calcium stearate, paraffin and polyethylene wax. According to the PVC material, the data cable can be used in a water-soaked environment for a long term; the mechanical stability is good, the electrical performance is stable, and the water ageing resistance performance and the water tree forming resistance performance are achieved in a wet environment, so that the stability of the data cable is further improved and the service cycle of the data cable is further prolonged.

Description

technical field [0001] The invention relates to the technical field of polyvinyl chloride materials used for high-speed data cables, more specifically, the invention relates to a sheath material used for high-speed data cables. Background technique [0002] PVC cable materials are mainly used as sheath materials for various cables such as power cables, control cables, and communication cables. Polyvinyl chloride cable materials can basically meet the requirements of insulation and sheathing, but with the continuous expansion of the application range of wire and cable, the performance requirements for PVC cable materials are also getting higher and higher, especially the polyvinyl chloride cable materials in the prior art. The water resistance and flame retardancy of vinyl cable materials need to be further improved. [0003] Due to the influence of the natural environment of the sun and rain, outdoor wires and cables have higher requirements on the physical and chemical ind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/10C08K9/06C08K3/30C08K3/34C08K3/36C08K5/12C08K3/22H01B3/44
Inventor 王惠兵陈夏裕吕秀云金春敏钱江华
Owner JIANGSU HENGTONG WIRE & CABLE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products