A kind of electrode pitch and preparation method thereof

A kind of asphalt and electrode technology, which is applied in the field of electrode asphalt and its preparation, can solve the problems of unsatisfactory requirements and high softening point of asphalt, and achieve the effects of low QI content, high coking value, and reduced interfacial tension

Active Publication Date: 2016-08-10
CHNA ENERGY INVESTMENT CORP LTD +1
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the softening point of direct coal liquefaction bitumen is relatively high, which cannot meet the requirements of bitumen for impregnating agent and bitumen for binder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of electrode pitch and preparation method thereof
  • A kind of electrode pitch and preparation method thereof
  • A kind of electrode pitch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The method for preparing electrode pitch of the present invention comprises:

[0029] (1) Extract the coal direct liquefaction residue with an organic solvent to obtain extracted pitch, wherein the organic solvent is a mixture of one or more of the following compounds: alicyclic hydrocarbons, aromatic hydrocarbons, chlorinated aromatic compounds, chlorine Aliphatic hydrocarbons, alcohols, aldehydes, ketones, sulfones, sulfoxides, ethers, carbon disulfide, pyridine, amides, petroleum distillates and liquefied oils produced during the direct liquefaction of coal; and

[0030] (2) Treat the extracted pitch at 350-420°C in an inert atmosphere to obtain electrode pitch.

[0031] Each step is detailed below.

[0032] step 1)

[0033] In the step (1) of the method of the present invention, the coal direct liquefaction residue is extracted with an organic solvent, and the obtained extract is removed from the solvent to obtain the extracted pitch. The organic solvent can be ...

Embodiment 1

[0061] (1) First, the above-mentioned coal direct liquefaction residue and the IBP-110°C liquefied oil produced during the coal direct liquefaction process were subjected to primary extraction at a volume ratio of 1:3 for 50 minutes; the mixture obtained by the primary extraction was separated into solid and liquid , the obtained solid part and the 220-260 °C liquefied oil produced during the direct coal liquefaction process were subjected to secondary extraction for 60 minutes at a volume of 1:3, and the soluble part obtained from the two-stage extraction was recovered to obtain the extracted pitch.

[0062] (2) Put the extracted pitch and coal tar in a ratio of 1:0.8 into a closed autoclave, raise the temperature to 380°C at a rate of 2°C / min under a nitrogen atmosphere, and keep the temperature for 8 hours to obtain electrode pitch.

[0063] The indexes of the extraction pitch, coal tar, and electrode pitch in Example 1 are shown in Table 1 below.

[0064] Table 1 Character...

Embodiment 2

[0068] (1) Obtain the extracted pitch through the step (1) in Example 1.

[0069] (2) Put the extracted pitch and coal tar in a ratio of 1:0.8 into a closed autoclave, and raise the temperature to 400°C at a rate of 3°C / min under a nitrogen atmosphere and keep the temperature constant for 6 hours to obtain electrode pitch.

[0070] The indicators of the obtained electrode pitch are shown in Table 2 below.

[0071] Table 2 Properties of electrode pitch

[0072]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
densityaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing electrode pitch by using coal direct liquefaction residue as raw material, comprising the following steps: (1) extracting coal direct liquefaction residue with an organic solvent to obtain extracted pitch; Treat the extracted pitch at ‑420°C to obtain electrode pitch. The electrode pitch of the present invention has a softening point of 90-120°C, a QI content of <0.2%, and a coking value of >50%. The invention provides a method and a product for preparing relatively cheap electrode pitch by using cheap coal direct liquefaction residue pitch as raw material.

Description

technical field [0001] The invention relates to an electrode pitch and a preparation method thereof, more specifically, to a method for preparing electrode pitch by using coal direct liquefaction residue as a raw material and the electrode pitch obtained therefrom. Background technique [0002] Coal direct liquefaction residue is a by-product other than oil produced by hydrogenation in the process of direct coal liquefaction. Although the composition of the residue varies depending on the liquefaction method, it is generally divided into organic matter and inorganic matter. Organic matter is generally condensed aromatic structural units and partially hydrogenated hydrogenated aromatic structures, and contains a series of normal alkanes in the form of side chains of aromatic structural units. Inorganic substances are generally inorganic substances in unreacted coal and catalysts for direct coal liquefaction. The coal direct liquefaction residue is the coal direct liquefacti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10C1/18C10C1/19
Inventor 盛英赖世耀宫晓颐梁文斌张胜振张大伟王梦瑶
Owner CHNA ENERGY INVESTMENT CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap