A kind of production method of billet continuous casting bearing steel

A billet continuous casting and production method technology, which is applied in the production field of billet continuous casting bearing steel, can solve problems such as internal cracks, high carbon content, and cracks, and achieve reduced occurrence probability, good surface quality, and no cracks. The effect of high cleaning rate

Inactive Publication Date: 2016-07-06
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this type of steel has high carbon content and high content of alloys such as chromium, and the following problems exist in the billet continuous casting production process: slag pits on the surface of the continuous casting slab, cracks on the surface and subcutaneous of the slab, slag inclusion and segregation of the slab, Quality defects such as porosity, shrinkage cavity, internal cracking, etc., especially when the equipment technology such as light pressure and electromagnetic stirring is not carried out at the end of solidification, quality defects such as segregation, porosity, shrinkage cavity, internal cracking and other quality defects of continuous casting billet are more difficult to control
However, this prior art does not disclose a specific pouring method, and this prior art aims to improve the service life of the bearing by reducing the oxygen content in the steel, but cannot overcome the continuous Slag pits on the surface of the slab, cracks, slag inclusions, and segregation, porosity, shrinkage cavities, internal cracks and other quality defects on the surface and subcutaneous surface of the slab
[0005] Instead of denaturing molten steel inclusions, control the continuous casting process to reduce the probability of tundish nozzle clogging and overcome the slag pits on the surface of the continuous casting slab, the surface of the slab and the skin under the skin during the billet continuous casting production process. Cracks, slab segregation, porosity and other quality defects have not been reported in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment is used to illustrate a production method of billet continuous casting bearing steel provided by the present invention.

[0036] What this embodiment adopts is a 200mm×200mm six-machine six-strand billet continuous casting machine.

[0037] Send the refined molten steel to the continuous casting platform. The main components of this molten steel are: carbon 1.0%, silicon 0.27%, manganese 0.37%, chromium 1.50%, phosphorus 0.012%, sulfur 0.004%, T[O]: 0.0006%, Aluminum 0.02%, Calcium 0.0001%, the balance is iron and trace impurities. The temperature of the molten steel in the tundish was measured to be 1474°C, and the superheat of the molten steel was 26°C.

[0038] Turn on the electromagnetic stirring of the crystallizer, the current intensity is 380A, and the frequency is 3Hz. When molten steel is injected into the mold and reaches 2 / 3 of the height of the mold, mold powder is added, and the composition of the mold powder is SiO 2 : 32%, CaO: 23%, Al ...

Embodiment 2

[0045] This embodiment is used to illustrate a production method of billet continuous casting bearing steel provided by the present invention.

[0046] What this embodiment adopts is a 200mm×200mm six-machine six-strand billet continuous casting machine.

[0047] The molten steel after refining is sent to the continuous casting platform. The molten steel is mainly composed of 0.96% carbon, 0.28% silicon, 0.36% manganese, 1.48% chromium, 0.011% phosphorus, 0.003% sulfur, T[O]: 0.0005%, aluminum 0.03%, calcium 0.0001%, the balance is iron and trace impurities. The temperature of the molten steel in the tundish was measured to be 1472°C, and the superheat of the molten steel was 32°C.

[0048] The electromagnetic stirring of the crystallizer is turned on, the current intensity is 370A, and the frequency is 2.8Hz. When molten steel is injected into the mold and reaches 2 / 3 of the height of the mold, mold powder is added. The composition of the mold powder is: SiO 2 : 36.5%, CaO...

Embodiment 3

[0055] This embodiment is used to illustrate a production method of billet continuous casting bearing steel provided by the present invention.

[0056] What this embodiment adopts is a 200mm×200mm six-machine six-strand billet continuous casting machine.

[0057] The molten steel after refining is sent to the continuous casting platform. The main components of the molten steel are: carbon 0.98%, silicon 0.28%, manganese 0.40%, chromium 1.46%, phosphorus 0.010%, sulfur 0.002%, T[O]≤0.0005%, Aluminum 0.03%, Calcium 0.0001%, the balance is iron and trace impurities. The temperature of the molten steel in the tundish was measured to be 1473°C, and the superheat of the molten steel was 38°C.

[0058] The electromagnetic stirring of the crystallizer is turned on, the current intensity is 390A, and the frequency is 3.2Hz. When molten steel is injected into the mold and reaches 2 / 3 of the height of the mold, mold powder is added, and the composition of the mold powder is SiO 2 : 34...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of billet continuous casting bearing steel. The method comprises: (1) injecting molten steel after refining into a tundish, and controlling the superheat degree of the molten steel injected into the tundish to be 25-45°C; (2) Under the electromagnetic stirring of the mold, inject the molten steel in the tundish into the mold for crystallization, and add mold slag into the mold; (3) Pull out the crystallized continuous casting slab from the mold , and the continuous casting slab is cooled through the secondary cooling zone and the air cooling zone in turn. The production method of the billet continuous casting bearing steel provided by the present invention can reduce the occurrence probability of tundish nozzle clogging, overcome the slag pits on the surface of the continuous casting billet, cracks on the surface and subcutaneous of the billet, and the occurrence of the billet continuous casting production process. Quality defects such as slab segregation and porosity.

Description

technical field [0001] The invention relates to a production method of billet continuous casting bearing steel. Background technique [0002] Bearing steel is widely used in automobile bearings and is in great demand. High-carbon chromium bearing steel (GCr15) is currently the most widely used in various industries, accounting for about 80%. However, this type of steel has high carbon content and high content of alloys such as chromium, and the following problems exist in the billet continuous casting production process: slag pits on the surface of the continuous casting slab, cracks on the surface and subcutaneous of the slab, slag inclusion and segregation of the slab, Quality defects such as porosity, shrinkage cavities, and internal cracks, especially when equipment technologies such as light pressure and electromagnetic stirring are not carried out at the end of solidification, quality defects such as segregation, porosity, shrinkage cavities, and internal cracks in co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/16
Inventor 陈亮李扬洲陈天明杨文中黎建全曾建华陈永杨森祥潘红杨洪波
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP