A kind of anti-oxidation vehicle lubricating oil and preparation method thereof

A lubricating oil and oxidation car technology, applied in the direction of lubricating composition, petroleum industry, additives, etc., can solve the problems of poisonous exhaust gas conversion device catalyst, short service life of lubricating oil, polluting the atmospheric environment, etc., and achieve excellent adsorption and chemical reaction Activity, life extension, high activity effect

Active Publication Date: 2016-10-05
江苏宝捷科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this compound is hard but very brittle, it will continue to fall off and form continuously during the friction process, which not only corrodes the machine parts, but also consumes additives. The service life of both machinery and lubricating oil is very short.
The anti-wear components in traditional lubricating oils, such as zinc dialkyldithiophosphate (T202 anti-oxidant and anti-corrosion agent), contain sulfur, phosphorus, and zinc, which not only corrode silver bearings, poison the catalyst of the exhaust gas conversion device, but also pollute the atmospheric environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An anti-oxidation vehicle lubricating oil is prepared from the following components in parts by weight: 30 parts of modified nano-diamond, 50 parts of base oil, 20 parts of organic molybdenum mixture, 10 parts of antioxidant, and 15 parts of friction modifier. The modified nano-diamond is obtained by modifying CTM1 and CTM2. The base oil is a base oil with a viscosity index of 100. The organic molybdenum mixture is oxymolybdenum dialkyldithiophosphate. The antioxidant is ZDDP. The friction modifier is an organic fatty acid. The particle size of the modified nano-diamond is 5nm.

[0017] The preparation method of the above-mentioned anti-oxidation vehicle lubricating oil comprises the following steps: adding base oil, organic molybdenum mixture, antioxidant, modified nano-diamond and friction modifier into the dissolution kettle according to the above-mentioned parts by weight, and heating with heat-conducting oil to 155°C, so that the above raw materials are complet...

Embodiment 2

[0019] An anti-oxidation vehicle lubricating oil is prepared from the following components in parts by weight: 50 parts of modified nano-diamond, 70 parts of base oil, 30 parts of organic molybdenum mixture, 20 parts of antioxidant, and 30 parts of friction modifier. The modified nano-diamond is obtained by modifying CTM1 and CTM2. The base oil is a base oil with a viscosity index of 110. The organic molybdenum mixture is molybdenum thiophosphate. Antioxidants are aromatic amines. The friction modifier is an organic fatty acid. The particle size of the modified nano-diamond is 10nm.

[0020] The preparation method of the above-mentioned anti-oxidation vehicle lubricating oil comprises the following steps: adding base oil, organic molybdenum mixture, antioxidant, modified nano-diamond and friction modifier into the dissolution kettle according to the above-mentioned parts by weight, and heating with heat-conducting oil to 165°C, so that the above raw materials are completel...

Embodiment 3

[0022] An anti-oxidation vehicle lubricating oil is prepared from the following components in parts by weight: 40 parts of modified nano-diamond, 60 parts of base oil, 25 parts of organic molybdenum mixture, 15 parts of antioxidant, and 20 parts of friction modifier. The modified nano-diamond is obtained by modifying CTM1 and CTM2. The base oil is a base oil with a viscosity index of 105. The organic molybdenum mixture is an organic acid molybdenum salt. The antioxidants are ZDDP and aromatic amines. The friction modifier is an organic fatty acid. The particle size of the modified nano-diamond is 7nm.

[0023] The preparation method of the above-mentioned anti-oxidation vehicle lubricating oil comprises the following steps: adding base oil, organic molybdenum mixture, antioxidant, modified nano-diamond and friction modifier into the dissolution kettle according to the above-mentioned parts by weight, and heating with heat-conducting oil to 160°C, so that the above raw mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses anti-oxidation automobile lubricating oil. The anti-oxidation automobile lubricating oil is composed of, by weight, 30-50 parts of modified nano-diamonds, 50-70 parts of base oil, 20-30 parts of an organic molybdenum mixture, 10-20 parts of an antioxidant and 15-30 parts of a friction improver. The invention further discloses a preparation method for the anti-oxidation automobile lubricating oil. The antioxidant is applied to the automobile lubricating oil so that oxygenolysis of effective constituents in the lubricating oil can be restrained and oil viscosity indexes can also be improved. Meanwhile, the friction improver is also added, so that friction performance is improved, and the service life of an automobile is prolonged.

Description

technical field [0001] The invention relates to the technical field of lubricating oil for vehicles, in particular to an anti-oxidation lubricating oil for vehicles and a preparation method thereof. Background technique [0002] At present, there are many solid lubricants with good performance, but due to their high density, they cannot be suspended in the oil, and the particle size is too coarse to get into the friction pair. The agglomeration is serious, and the oil passage is blocked after a long time, so they cannot be used in lubricating oil. The extreme pressure and antiwear agents in traditional lubricating oils are often some sulfur, phosphorus, and chloride compounds. Through boundary lubrication, instantaneous high temperature and high pressure and frictional pairs form metal compounds to improve hardness and wear resistance. Although this compound is hard but very brittle, it will continue to fall off and form continuously during the friction process, which not on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M141/10C10M177/00
Inventor 李勇
Owner 江苏宝捷科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com