Novel antiknock fireproof plate and preparation method thereof

A fireproof board, a new type of technology, is applied in the direction of chemical instruments and methods, layered products, metal layered products, etc. It can solve the problems that cannot meet the requirements of explosion resistance and fire protection engineering, and achieve the effect of improving the impact penetration resistance

Active Publication Date: 2014-10-15
江苏爵格工业集团有限公司
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it still cannot meet the anti-explosion and fire protection projects of higher resistance level, such as anti-explosion protection projects in the fields of military industry, national defense, medium and high resistance civil air defense projects, and industrial boiler rooms.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel antiknock fireproof plate and preparation method thereof
  • Novel antiknock fireproof plate and preparation method thereof
  • Novel antiknock fireproof plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] In order to make the above objects, features and advantages of the present invention more comprehensible, specific implementations of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0018] In the following description, a lot of specific details are set forth in order to fully understand the present invention, but the present invention can also be implemented in other ways different from those described here, and those skilled in the art can do it without departing from the meaning of the present invention. By analogy, the present invention is therefore not limited to the specific examples disclosed below.

[0019] Secondly, the present invention is described in detail in combination with schematic diagrams. When describing the embodiments of the present invention in detail, for the convenience of explanation, the cross-sectional view showing the device structure will not be partially enlarged according to the gener...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel antiknock fireproof plate and a preparation method thereof. The plate comprises a punching plate and an active powder concrete slab, wherein the active powder concrete slab comprises the following raw materials by weight percentage: 29.62-31.40% of aluminate cement, 32.60-34.55% of quartz sands, 4.11-8.72% of steel fiber, 0.14-0.20% of basalt fiber, 0.15-0.21% of plastic steel fiber, 10.37-11.0% of silica fume, 8.89-9.42% of quartz powders, 0.74-0.79% of high-efficiency water reducing agents and 8.38-8.89% of water. The flexural strength, antiknock performance, fire insulation performance, impact resistance and penetration resistance of the plate are all significantly improved, and the plate is suitable for the antiknock fireproof projects in high resistance.

Description

technical field [0001] The invention relates to a novel anti-explosion and fireproof board capable of resisting explosion shock waves, fire and heat insulation, sound insulation and noise reduction, and impact resistance and a preparation method thereof. Background technique [0002] At present, the production technology of ordinary anti-explosion fireproof board is quite mature, and its structure is a sandwich composite structure of punched galvanized steel plate and fiber cement board. Fiber cement boards are usually produced by the scissoring process and do not require autoclaving after molding. At present, there are about 10 domestic manufacturers of anti-explosion and fireproof boards, and many building board manufacturers are investing and launching, and the competition is very fierce. The specifications of anti-explosion and fireproof panels produced by various manufacturers are relatively standardized, but the quality varies greatly. The fiber cement board can be m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B13/06B32B15/04C04B28/06C04B14/06C04B14/48C04B14/38
Inventor 吴平安卞凤华
Owner 江苏爵格工业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap