Heat-resistant and oil-resistant rubber material

An oil-resistant rubber and heat-resistant technology, applied in the field of rubber materials, can solve problems such as inability to meet demand, and achieve the effects of extending service life, reducing costs, and improving wear resistance.

Inactive Publication Date: 2014-10-22
安徽宁国尚鼎橡塑制品有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the heat-resistant and oil-resistant properties of rubber materials, people add various compounding components in the process of making rubber products from raw rubber to improve the heat-resistant and oil-resistant properties of rubber prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0011] Example 1

[0012] The heat-resistant and oil-resistant rubber material proposed by the present invention includes raw materials in parts by weight: 40 parts of EPDM, 40 parts of chloroprene rubber, 15 parts of nitrile rubber, 5 parts of benzothiazole disulfide, and 4 parts of zinc oxide. Parts, 5 parts of magnesium oxide, 9 parts of chopped glass fiber, 15 parts of wood powder, 30 parts of asbestos, 40 parts of mica powder, 15 parts of barite powder, 8 parts of titanate coupling agent, 5 parts of calcium zinc stabilizer, Synthetic vegetable ester 5 parts, paraffin wax 2 parts, environmentally friendly flame retardant FR-T8011.5 parts, antimony trioxide 5 parts, antioxidant SP3 parts, antioxidant H3 parts;

[0013] During the preparation process, put EPDM rubber, neoprene rubber, and nitrile rubber in an internal mixer for uniform plasticization, and continue to add chopped glass fiber, wood powder, asbestos, mica powder, barite powder, titanic acid After ester coupling age...

Example Embodiment

[0014] Example 2

[0015] The heat-resistant and oil-resistant rubber material proposed by the present invention includes raw materials in parts by weight: 50 parts of EPDM, 30 parts of chloroprene rubber, 25 parts of nitrile rubber, 2 parts of benzothiazole disulfide, and 6 parts of zinc oxide. Parts, 3 parts of magnesium oxide, 12 parts of chopped glass fiber, 10 parts of wood powder, 40 parts of asbestos, 20 parts of mica powder, 20 parts of barite powder, 6 parts of titanate coupling agent, 6 parts of calcium zinc stabilizer, Synthetic vegetable ester 4 parts, paraffin wax 3 parts, environmentally friendly flame retardant FR-T8011 parts, antimony trioxide 6 parts, antioxidant SP 2 parts, antioxidant H4 parts;

[0016] During the preparation process, put EPDM rubber, neoprene rubber, and nitrile rubber in an internal mixer for uniform plasticization, and continue to add chopped glass fiber, wood powder, asbestos, mica powder, barite powder, titanic acid After ester coupling age...

Example Embodiment

[0017] Example 3

[0018] The heat and oil resistant rubber material proposed by the present invention includes raw materials in parts by weight: 45 parts of EPDM, 35 parts of chloroprene rubber, 20 parts of nitrile rubber, 4 parts of benzothiazole disulfide, and 5 parts of zinc oxide. Parts, 4 parts of magnesium oxide, 10 parts of chopped glass fiber, 13 parts of wood powder, 35 parts of asbestos, 30 parts of mica powder, 18 parts of barite powder, 7 parts of titanate coupling agent, 5.5 parts of calcium zinc stabilizer, Synthetic vegetable ester 4.3 parts, paraffin wax 2.8 parts, environmentally friendly flame retardant FR-T8011.3 parts, antimony trioxide 5.7 parts, antioxidant SP2.9 parts, antioxidant H3.1 parts;

[0019] During the preparation process, put EPDM rubber, neoprene rubber, and nitrile rubber in an internal mixer for uniform plasticization, and continue to add chopped glass fiber, wood powder, asbestos, mica powder, barite powder, titanic acid After ester coupling ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat-resistant and oil-resistant rubber material. The heat-resistant and oil-resistant rubber material comprises raw materials by weight: 40-50 parts of ethylene propylene terpolymer, 30-40 parts of chloroprene rubber, 15-25 parts of nitrile rubber, 2-5 parts of disulfide benzothiazole, 4-6 parts of zinc oxide, 3-5 parts of magnesium oxide, 9-12 parts of chopped glass fibers, 10-15 parts of wood powder, 30-40 parts of asbestos, 20-40 parts of mica powder, 15-20 parts of barite powder, 6-8 parts of a titanate coupling agent, 5-6 parts of a calcium-zinc stabilizer, 4-5 parts of a synthetic plant ester, 2-3 parts of paraffin, 1-1.5 parts of an environment-friendly fire retardant FR-T801, 5-6 parts of antimonous oxide, 2-3 parts of an anti-aging agent SP and 3-4 parts of an anti-aging agent H. The heat-resistant and oil-resistant rubber material has excellent heat resistance, fire retardance, oil resistance and wear-resistant property.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a heat-resistant and oil-resistant rubber material. Background technique [0002] Rubber materials are non-polar substances. According to the principle of similar compatibility, rubber materials are often easily dissolved in oil, which is not conducive to the use of rubber materials in oil-filled environments, and some rubber materials need to be used in high-temperature environments at the same time. , such as rubber materials in automobile engines, the above two use environments will change the physical and mechanical properties of rubber materials. In order to improve the heat-resistant and oil-resistant properties of rubber materials, people add various compounding components in the process of making rubber products from raw rubber to improve the heat-resistant and oil-resistant properties of rubber products, but the current heat-resistant and oil-resistant rubber ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L11/00C08L9/02C08L97/02C08K13/04C08K7/14C08K7/12C08K5/47C08K3/22C08K3/34C08K5/10C08K5/01B29C35/02
CPCC08L23/16B29C35/02C08L11/00C08L2201/02C08L2201/08C08L2205/035C08L2312/00C08L9/02C08L97/02C08L91/06C08K13/04C08K7/14C08K7/12C08K5/47C08K2003/2296C08K2003/222C08K3/34C08K2003/3045C08K5/10C08K3/2279
Inventor 杨存俊
Owner 安徽宁国尚鼎橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap