Decalcified dental matrix of mammal and preparation method thereof

A technology for mammals and production methods, applied in the field of decalcified mammalian tooth matrix and its production, can solve the problems of insufficient size of osteoinductive materials, wrong use of deciduous teeth, failure to obtain valuable experimental results, etc., to achieve enhanced growth firmness, The source is easy and the effect of improving the stability of the stay

Inactive Publication Date: 2014-11-19
李成林
View PDF1 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, looking at the research process at home and abroad for more than 30 years, it is found that the reason why there is no major progress in the use of teeth as raw materials to make osteoinductive materials is because people have been making mistakes in choosing raw teeth and using deciduous teeth as raw materials by mistake. No valuable experimental results can be obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A decalcified mammalian tooth matrix. The selected raw material is the permanent tooth of a mammal bovine.

[0022] A method for making a decalcified mammalian tooth matrix, comprising the following steps:

[0023] (1) Preserve the collected mammal bovine permanent teeth at low temperature for subsequent use;

[0024] (2) raw material teeth are soaked and sterilized with 50% of 84 disinfectant solution, soaking time of 84 disinfectant solution is 45 minutes, and the temperature is 35-40°C;

[0025] (3) Use mechanical methods to remove the useless parts of the tooth body;

[0026] (4) The dental tissue is pulverized into granules by means of mechanical pulverization;

[0027] (5) soak and sterilize with 50% of the 84 disinfectant solution and pulverize into granular tooth tissue, the soaking time of the 84 disinfectant solution is 45 minutes, and the temperature is 35-40°C;

[0028] (6) Soak the treated tooth tissue particles in 0.65-0.72 equivalent hydrochloric acid ...

Embodiment 2

[0032] A decalcified mammalian tooth matrix. The selected raw material is the permanent tooth of mammal sheep.

[0033] A method for making a decalcified mammalian tooth matrix, comprising the following steps:

[0034] (1) Preserve the collected mammalian permanent teeth at low temperature for subsequent use;

[0035] (2) 50% 84 disinfectant solution is used for raw teeth, the best soaking time is 45 minutes, and the best temperature is 36 degrees Celsius;

[0036] (3) Use mechanical methods to remove the useless parts of the tooth body;

[0037] (4) The dental tissue is pulverized into granules by means of mechanical pulverization;

[0038] (5) soak and sterilize with 50% of 84 disinfectant again and pulverize it into granular tooth tissue. The optimal soaking time of 84 disinfectant is 45 minutes, and the optimum temperature is 36 degrees Celsius;

[0039] (6) Put the treated tooth tissue particles into 0.65-0.72 equivalent hydrochloric acid solution for soaking, the opti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a decalcified dental matrix of a mammal and a preparation method thereof. The raw material is from permanent teeth of the mammal. The preparation method comprises the following steps: (1) collecting permanent teeth of the mammal for later use; (2) soaking the permanent teeth in a 50% 84 disinfectant for sterilizing, wherein the time for sterilizing is 45 minutes and the temperature is 35-40DEG C; (3) removing useless parts of the teeth; (4) smashing tooth tissues into particles; (5) sterilizing the smashed tooth tissue particles, wherein the time for sterilizing is 45 minutes and the temperature is 35-40DEG C; (6) putting the treated tooth tissue particles into 0.65-0.72 equivalent weight of hydrochloric acid liquid for soaking for 10-16 hours at 34-38DEG C to finish decalcification; and (7) drying at low temperature, soaking in hydrogen peroxide for 30 minutes, so as to obtain the decalcified dental matrix of the mammal. The decalcified dental matrix of the mammal has better inductive bone regenerative action, and does not carry any pathogenic factor after being prepared into final products.

Description

technical field [0001] The invention relates to a medical material and a manufacturing method thereof, in particular to a decalcified mammalian tooth matrix and a manufacturing method thereof. Background technique [0002] A scholar in the United States put forward the theory of osteoinduction, thinking that in animals and human hard tissues (bone and teeth), there is a bone morphogenetic protein (BMP), which has the function of inducing bone regeneration in the body. Choose fresh, healthy animal or human hard tissue as raw material, remove the soft tissue through mechanical processing, crush it into granules, wash it with water and then go through chemical processing to remove fat, and then put the hard tissue fragments into 0.6 equivalent hydrochloric acid solution for constant temperature decalcification Prepare hard tissue matrix. After this kind of hard tissue matrix is ​​transplanted into the body, the bone morphogenetic protein contained in it can produce directional...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/36A61L27/54A61L31/00A61L31/16
Inventor 李成林
Owner 李成林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com