Calcium oxide material for clean steel smelting and preparation method thereof

A calcium material and clean steel technology, applied in the field of clean steel smelting calcium oxide material and its preparation, can solve the problems of spalling, increasing the amount of oxide inclusions, increasing phosphorus content, etc., to achieve high activity, uniform distribution, strong The effect of adsorption capacity

Active Publication Date: 2015-11-11
山东产研中科高端化工产业技术研究院有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the amount of water added during construction is about 20wt%, cracks and spalling often occur in the early stages of use, thereby increasing the amount of oxide inclusions in the steel
At the same time, in the continuous casting process, since mineral materials such as soft clay, silicon oxide powder, and sodium silicate are acidic oxides, they have a high oxygen supply potential to molten steel and will continue to increase the total oxygen content in molten steel; Phosphate minerals such as sodium tripolyphosphate used in the process of contacting molten steel will increase the content of phosphorus in steel, which is not conducive to the improvement of steel quality; moreover, the main chemical component of magnesia is magnesium oxide, which can affect the inclusion of molten steel The adsorption capacity is not strong
In short, the mineral composition and preparation process of existing tundish coatings can no longer meet the increasingly demanding needs of clean steel smelting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A calcium oxide material for clean steel smelting and a preparation method thereof. Mix 35-38wt% of limestone particles, 33-35wt% of fine limestone powder, 17-22wt% of magnesia-aluminum sol and 5-10wt% of the mixture, stir evenly, smear or cast it to obtain clean steel smelting Calcium oxide material.

[0025] The mixture is made by mixing alumina powder: magnesia powder: calcium lignosulfonate with a mass ratio of 10: (3 to 4): (0.7 to 0.9).

Embodiment 2

[0027] A calcium oxide material for clean steel smelting and a preparation method thereof. Mix 38-40wt% of limestone particles, 30-33wt% of fine limestone powder, 12-17wt% of magnesia-aluminum sol and 10-15wt% of the mixture, stir evenly, smear or cast it to obtain clean steel smelting Calcium oxide material.

[0028] The mixture is made by mixing alumina powder: magnesia powder: calcium lignosulfonate with a mass ratio of 10: (4-5): (0.9-1.1).

Embodiment 3

[0030] A calcium oxide material for clean steel smelting and a preparation method thereof. Mix 38-40wt% of limestone particles, 30-33wt% of fine limestone powder, 8-12wt% of magnesia-aluminum sol and 15-20wt% of the mixture, stir evenly, smear or cast it to obtain clean steel smelting Calcium oxide material.

[0031] The mixture is made by mixing alumina powder: magnesia powder: calcium lignosulfonate with a mass ratio of 10: (3 to 4): (1.1 to 1.3).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a calcium oxide material for clean steel smelting and a preparation method thereof. The technical scheme is as follows: the preparation method comprises the following steps: mixing 35-40 wt% of limestone particle, 30-35 wt% of limestone fine powder, 8-22 wt% of magnesium aluminum sol and 5-20 wt% of mixture, stirring uniformly, and painting or casting to form, thereby obtaining the calcium oxide material for clean steel smelting. The mixture is formed by mixing alumina micropowder, magnesite fine powder and calcium lignosulphonate in a mass ratio of 10:(3-5):(0.7-1.5); the particle size of the limestone particle is 7-0.1mm, the particle size of the limestone fine powder is 0.05-100 mu m, and the CaCO3 content of the limestone particle and limestone fine powder is greater than or equal to 92 wt%; and the mole ratio of magnesium to aluminum in the magnesium aluminum sol is 1:(0.4-2.2). The calcium oxide material has the advantages of low impurity content, proper strength and almost no influence on total oxygen content of molten steel, can adsorb oxide inclusions in the steel, and is suitable for preparing the working line of a tundish for clean steel smelting.

Description

Technical field [0001] The invention belongs to the technical field of calcium oxide materials. In particular, it relates to a calcium oxide material for smelting clean steel and a preparation method thereof. Background technique [0002] In accordance with the requirements for innovation and development in the "Twelfth Five-Year Plan" of the iron and steel industry, the state will intensify the upgrading and development of special steel products, strive to replace imports and meet the increased market demand of the domestic equipment manufacturing industry. Therefore, it is particularly important to strictly control the quality of molten steel in the steel smelting process. The tundish is the last container for molten steel before continuous casting of molten steel. The composition, structure and performance of the refractory material of the working layer are of great significance to ensure the quality of molten steel. [0003] Most of the existing tundish working linings are co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 魏耀武叶昌松姜亚清
Owner 山东产研中科高端化工产业技术研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products