Water-based colourful building coating and preparation method thereof

A kind of architectural paint and colorful technology, applied in the direction of multi-color effect paint, coating, etc., can solve the problems of easy aggregation of colored particles, uneven quality, easy breakage, etc., to improve the stability of color particles, make up for small cracks, recoatability Good results

Inactive Publication Date: 2014-12-17
SHANDONG QINHENG TECH
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the quality of most water-based colorful architectural coatings on the market is uneven. Some have poor storage stability, and some colored particles are easy to agglomerate and break; Popularization and Application of Waterborne Colorful Architectural Coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The composition of described base paint is:

[0044] Cellulose 0.8% Multifunctional additives 0.1%

[0045] Dispersant 0.1% Bactericide 0.1%

[0046] Titanium dioxide 2.0% Kaolin 2.0%

[0047] Defoamer 0.4% 3.0~5.0% Protective glue 10%

[0048] Coalescing agent 0.5% 20% modified bentonite 10%

[0049] Elastic emulsion 25% water 49%;

[0050] The base paint is prepared by mixing water-based colorants of different colors according to the requirements to form various base paints of different colors. The base paints of each color are dispersed in the protective glue system in strict accordance with the ratio to make different color particle systems.

[0051] The composition of described protective glue system is:

[0052] 5%~8% Protective glue 60% Wetting agent 1.0%

[0053] 4% T-935 protective glue 39%;

[0054] The composition of described color particle system is:

[0055] 50% of base paint of various colors, 50% of protective glue system;

[0056] The compositi...

Embodiment 2

[0084] The composition of described base paint is:

[0085] Cellulose 1.1% Multifunctional Auxiliary 0.2%

[0086] Dispersant 0.2% Bactericide 0.4%

[0087] Titanium dioxide 4.0% Kaolin 4.0%

[0088] Defoamer 0.4% 3.0~5.0% Protective glue 15%

[0089] Coalescing agent 0.7% 20% modified bentonite 15%

[0090] Elastic Emulsion 30% Water 29%;

[0091] The base paint is prepared by mixing water-based colorants of different colors according to the requirements to form various base paints of different colors. The base paints of each color are dispersed in the protective glue system in strict accordance with the ratio to make different color particle systems.

[0092] The composition of described protective glue system is:

[0093] 5%~8% Protective glue 62% Wetting agent 1.0%

[0094] 4% T-935 protective glue 37%;

[0095] The composition of described color particle system is:

[0096] 50% of base paint of various colors, 50% of protective glue system;

[0097] The compositi...

Embodiment 3

[0107] The composition of described base paint is:

[0108] Cellulose 0.8% Multifunctional additives 0.1%

[0109] Dispersant 0.2% Bactericide 0.2%

[0110] Titanium dioxide 3.0% Kaolin 3.0%

[0111] Defoamer 0.2% 3.0~5.0% Protective glue 13%

[0112] Coalescing agent 0.5% 20% modified bentonite 13%

[0113] Elastic Emulsion 25% Water 41%;

[0114] The base paint is prepared by mixing water-based colorants of different colors according to the requirements to form various base paints of different colors. The base paints of each color are dispersed in the protective glue system in strict accordance with the ratio to make different color particle systems.

[0115] The composition of described protective glue system is:

[0116] 5%~8% Protective glue 64% Wetting agent 1.0%

[0117] 4% T-935 protective glue 35%;

[0118] The composition of described color particle system is:

[0119] 50% of base paint of various colors, 50% of protective glue system;

[0120] The compositi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses water-based colourful building coating. The water-based colourful building coating is formed by mixing the following components in percentage by mass: 5-20% of water-based colour paste, 60-70% of colour chip system and 30-40% of emulsion binder. A preparation method of the water-based colourful building coating comprises the following steps: preparing basic paint, matching colour, preparing a protection glue system, preparing a colour chip system, preparing an emulsion binder, and adding the colour chip system into the prepared emulsion binder, thus the stable water-based colourful building coating is formed. The water-based colourful building coating has the advantages that the protection glue system and cellulose in the basic paint interact with each other, so that produced gel is firmly wrapped on the surface of the basic paint of each colour, and surface activity of negative ions provides negative charges to form stable colour chips in various colours; the water-based colourful building coating can improve colour chip stability and storage stability, can prevent precipitation, colour bleeding and muddy water of the water-based colourful particles, is moulded by spraying in one step, good in recoatability, realistic in natural marble imitating effect and simple to maintain, has certain elasticity and can be used for making up micro cracks of a wall body.

Description

technical field [0001] The invention relates to an architectural paint, in particular to a water-based colorful architectural paint and a preparation method thereof. Background technique [0002] At present, granite and marble are favored by architects and users for their serious texture and durable quality, and they are also one of the important symbols of the external image of buildings. However, with the protection of natural resources and the implementation of national building energy conservation in my country, the wide application of natural stone in the field of architectural decoration has been affected to a certain extent. The construction of granite as a building decoration material is relatively complicated, which not only increases the load bearing of the unit wall, but also has many unsafe factors such as the risk of falling off; some marble will release trace radioactive elements, which is harmful to human health. In addition, the continuous improvement of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12C09D5/29
Inventor 李冰石景信张丕华韩国涛袁文海
Owner SHANDONG QINHENG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap