Method for processing quasi-polyester-peach-skin fabric

A technique of imitating peach skin and processing methods, applied in fabric surface trimming, biochemical treatment of enzymes/microbes, textiles, etc., to achieve the effects of increased efficiency, low temperature, and improved skin-friendliness

Active Publication Date: 2015-01-07
浙江泉能纺织股份有限公司
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Such a technical solution has not yet been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Pre-treatment: Singeing, whitening and drying soybean fiber and cotton fiber blended fabrics to obtain material A;

[0030] (2) Grinding: use metal abrasive grains for dry grinding;

[0031] (3) Polishing: After the two-step treatment with complex enzymes, the intermittent rope overflow dyeing equipment is used for polishing;

[0032] (4) dyeing, dyeing according to conventional methods;

[0033] (5) finalize the shape, dry, and obtain the finished product;

[0034] In the preferred step (1), the blending ratio of the soybean fiber and the cotton fiber is 2:8 by weight percentage;

[0035] In preferred step (1), the concentration of the caustic soda that adopts when described singeing is 120g / L;

[0036] In the preferred step (1), the whitening is to adopt oxygen bleaching;

[0037] In the preferred step (2), the grinding of the metal abrasive grains is as follows: rubbing the surface of the fabric with sandpaper covered with metal particles coated on a grinding...

Embodiment 2

[0044] (1) Pre-treatment: Singeing, whitening and drying soybean fiber and cotton fiber blended fabrics to obtain material A;

[0045] (2) Grinding: use metal abrasive grains for dry grinding;

[0046] (3) Polishing: After the two-step treatment with complex enzymes, the intermittent rope overflow dyeing equipment is used for polishing;

[0047] (4) dyeing, dyeing according to conventional methods;

[0048] (5) finalize the shape, dry, and obtain the finished product;

[0049] In the preferred step (1), the blending ratio of the soybean fiber and the cotton fiber is 2:8 by weight percentage;

[0050] In preferred step (1), the concentration of the caustic soda that adopts when described singeing is 130g / L;

[0051] In the preferred step (1), the whitening is to adopt oxygen bleaching;

[0052] In the preferred step (2), the grinding of the metal abrasive grains is as follows: rubbing the surface of the fabric with sandpaper covered with metal particles coated on a grinding...

Embodiment 3

[0059] (1) Pre-treatment: Singeing, whitening and drying soybean fiber and cotton fiber blended fabrics to obtain material A;

[0060] (2) Grinding: use metal abrasive grains for dry grinding;

[0061] (3) Polishing: After the two-step treatment with complex enzymes, the intermittent rope overflow dyeing equipment is used for polishing;

[0062] (4) dyeing, dyeing according to conventional methods;

[0063] (5) finalize the shape, dry, and obtain the finished product;

[0064] In the preferred step (1), the blending ratio of the soybean fiber and the cotton fiber is 2:8 by weight percentage;

[0065] In preferred step (1), the concentration of the caustic soda that adopts when described singeing is 125g / L;

[0066] In the preferred step (1), the whitening is to adopt oxygen bleaching;

[0067] In the preferred step (2), the grinding of the metal abrasive grains is as follows: rubbing the surface of the fabric with sandpaper covered with metal particles coated on a grinding r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for processing quasi-polyester-peach-skin fabric. The method includes the steps that (1) pre-processing is carried out, wherein singeing, whitening and drying are carried out on soybean fiber and cotton fiber blended fabric; (2) sueding is carried out, wherein metal abrasive grains are used for dry-method sueding; (3) polishing is carried out, wherein intermittent rope-form overflow dyeing equipment is used for polishing after two steps of complex enzyme processing; (4) dyeing is carried out according to a conventional method; (5) shaping and drying are carried out to obtain a finished product.

Description

technical field [0001] The invention relates to a processing method of imitation jeanette fabric. Background technique [0002] The trade name of Lyocell fiber is Tencel, and the Chinese trade name is "Tencel". Ordinary Lyocell fiber fabrics are processed in a wet state, and the surface will produce obvious fibrillation, that is, the fibers will be split along the longitudinal direction to produce microfibers with a diameter of less than 4 μm. These microfibers are close to transparent and form a "frost" effect on the surface of the fabric , also known as jeanette style. Fibrillation can not only endow Tencel fabrics with aesthetic effects, but also provide special handle. [0003] Cotton and Lyocell fibers are both cellulose fibers. Through carefully designed dyeing and finishing processes, the surface of cotton woven fabrics can also produce peach skin style, which is also called "tencel-like" processing of cotton fabrics. The cotton woven fabric with peach skin style i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D06C11/00D06C15/14D06C9/00D06L3/02D06M16/00D06M101/06D03D15/217D03D15/233D03D15/47D06L4/10
CPCD03D15/00D06B3/28D06C11/00D06L4/18D06M16/003D06M2101/06D10B2403/0111D10B2211/26D10B2201/02
Inventor 王爱泉
Owner 浙江泉能纺织股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More