Glazed porcelain polished tile and production method thereof

A production method and a technology of polishing bricks, which are applied in the field of architectural ceramics, can solve problems such as the inability to control the distribution of flashing spots on the surface of finished products, the monotonous decoration of patterns on the surface of mechanical fabrics, and the inability to achieve color gradient effects, etc., to achieve diversified decoration methods and delicate decorative patterns. , various layers of effects

Inactive Publication Date: 2015-02-04
DEQING NABEL CERAMIC
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Limited by equipment technology, there are not many ways to fabricate porcelain polished tiles, and the pattern decoration on the surface of mechanical fabrics is monotonous, and the decorative effect is not rich enough
Chinese patent CN200410050914.5A discloses a process for producing porcelain polished tiles in the form of overall mixing, which is to add a certain proportion of monocrystalline silicon to the body powder and then press it to form a metallic flash spot effect on the surface of the product. Mechanical mixing can not control the distribution of flash spots on the surface of the finished product, and the r

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] [Example 1] The production method of glazed porcelain polished tiles of the present invention comprises the following steps:

[0024] 1) Preparation of ordinary porcelain tile formula powder;

[0025] 2) Pattern formation

[0026] ① It is formed by large-grain cloth of porcelain polished tiles;

[0027] ② Inkjet printing pattern with ceramic digital inkjet machine in cooperation with step ①;

[0028] 3) Apply transparent glaze: glaze thickness 0.5mm;

[0029] 4) Firing: The firing temperature is 1150°C, and the firing cycle is 60 minutes;

[0030] 5) Edge grinding and polishing.

Embodiment 2

[0031] [Example 2] The production method of glazed porcelain polished tiles of the present invention comprises the following steps:

[0032] 1) Preparation of ordinary porcelain tile formula powder;

[0033] 2) Pattern formation

[0034] ① Formed with porcelain polished brick micro-powder cloth;

[0035] ② Rubber roller printing pattern matched with step ①;

[0036] 3) Apply transparent glaze: glaze thickness 0.7mm;

[0037] 4) Firing: The firing temperature is 1180°C, and the firing cycle is 55 minutes;

[0038] 5) Edge grinding and polishing.

Embodiment 3

[0039] [Example 3] The production method of glazed porcelain polished tiles of the present invention comprises the following steps:

[0040] 1) Preparation of ordinary porcelain tile formula powder;

[0041] 2) Pattern formation

[0042] ① It is formed by multi-tube cloth of porcelain polished tiles;

[0043] ② screen printing pattern matched with step ①;

[0044] 3) Apply transparent glaze: glaze thickness 1.0mm;

[0045] 4) Firing: The firing temperature is 1200°C, and the firing cycle is 45 minutes;

[0046] 5) Edge grinding and polishing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a glazed porcelain polished tile and a production method thereof. The method comprises: a) preparation of ordinary porcelain tile formula powder; b) transparent glaze application to a thickness of 0.5-1.0mm; c) firing at a temperature of 1100-1200DEG C; and d) edging polishing. The method is characterized in that: it also includes a pattern forming step between the step a) and step b). And the pattern forming step is realized through coordination of cloth molding and pattern printing. Due to combination of distribution, ink jetting, rubber rolls, silk-screen printing and other decoration means, the surface pattern of the glazed porcelain polished tile prepared by the method provided by the invention has more exquisite and vivid effects and richer layering than single mechanical mixing and distribution ways, thus realizing technical innovation of traditional porcelain polished tiles.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a glazed porcelain polished tile and a production method thereof. Background technique [0002] With the improvement of living standards and changes in lifestyles, consumers have higher and higher aesthetic requirements for building decoration materials, which has effectively promoted the development of the building decoration materials industry. [0003] Wall and floor tiles are one of the main materials of building decoration materials, which are mainly divided into two categories: polished tiles and glazed tiles. The surface pattern of the existing porcelain polished tiles is mainly formed by overall mixing, multi-tube cloth, bleed, and micropowder cloth, etc., and products ranging from solid colors to particles, bleed, micropowder and line micropowder porcelain polished tiles are prepared. Limited by equipment technology, there are not many ways to fabricate p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C1/00B28B13/02C04B41/89
Inventor 李华云樊叶利夏昌奎钟金明彭西洋王广山郑为兵许家祥邓国庆
Owner DEQING NABEL CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap