800 MPa grade cold-rolled double-phase steel and production method thereof

A production method and 800mpa technology, applied in the field of metallurgical sheet production, can solve the problems of reduced smelting castability, insignificant effect, unfavorable continuous production, etc., and achieve the effects of good production continuity, reduced production cost and low cost.

Inactive Publication Date: 2015-02-04
HBIS COMPANY LIMITED HANDAN BRANCH COMPANY
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nb can stabilize and enhance the stability of austenite and refine grains, but for cold-rolled dual-phase steel, the effect is not obvious
Al has a significant effect on improving the stability of auste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 800 MPa grade cold-rolled double-phase steel and production method thereof
  • 800 MPa grade cold-rolled double-phase steel and production method thereof
  • 800 MPa grade cold-rolled double-phase steel and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～10

[0013] Embodiments 1 to 10: The 800MPa grade cold-rolled dual-phase steel is produced by converter smelting, LF refining, RH refining, continuous casting, hot rolling and cold rolling and continuous annealing processes; the final chemical composition and process conditions of the production method are as follows stated.

[0014] (1) Converter smelting, LF refining, RH refining and continuous casting process:

[0015] Requirements for molten iron in the converter smelting process: S ≤ 0.040wt%, desulfurization target S ≤ 0.010wt%, scrap steel added accounts for 4-8wt% of the total mass of molten iron, and the ratio of molten iron ≥ 85wt%.

[0016] In the LF refining process, the alkalinity is controlled at 4.0-4.5, and the end target C≤0.055wt%, P<0.007wt%, S≤0.02wt%.

[0017] LF Ladle Bottom Blowing Ar is opened to a flow rate of 80Nm 3 / h, the processing time is controlled within 40 minutes, under the premise of burying the arc, the positive pressure is guaranteed throughou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses 800 MPa grade cold-rolled double-phase steel and a production method thereof. The production method comprises a hot rolling process and a cold rolling continuous annealing process. The chemical compositions of a casting entering the hot rolling process comprise, in percent by mass, 0.14-0.17% of C, 0.45-0.55 of Si, 1.6-1.8 of Mn, 0.55-0.65% of Cr, P<=0.016%, S<=0.008%, 0.02-0.05% of Als, N<=0.004%, and the balance Fe. In the double-phase steel, the Si content is increased and the Mn content is reduced on the basis of the compositions of C-Si-Mn-Cr, so that the strength is increased without adding Al, Nb, Mo, Ti and other high-cost elements, and the purposes of reducing production difficulty and production cost while not influencing smelting castability are realized. The method improves the Si content, reduces the Mn content, improves the composition system of the C-Si-Mn-Cr system and realizes the purpose of reducing production cost. By improving the smelting, hot rolling and cold-rolling continuous annealing technologies, the cold-rolled double-phase steel with the tensile strength of 800-850 MPa, the yield strength of 450-550 MPa and the elongation percentage of 15-17% is produced, and the production method has the characteristics of simple technology, low cost and stable product quality.

Description

technical field [0001] The invention belongs to the technical field of metallurgical plate production, in particular to an 800MPa grade cold-rolled dual-phase steel and a production method thereof. Background technique [0002] At present, the composition systems of cold-rolled dual-phase steel are mainly C-Si-Mn-Cr series, C-Si-Mn-Cr-Mo, C-Si-Mn-Nb and C-Al-Mn-Mo series, etc. . The difficulty in producing cold-rolled dual-phase steel lies in the need to control a high cooling rate and a low final cooling temperature during annealing, so that there are two phases of ferrite and martensite in the cold-rolled finished product. When the cooling rate is slow or the final cooling temperature is high, the volume fraction of martensite formed is insufficient, or even martensite cannot be formed, resulting in low tensile strength of the finished product and affecting product quality. However, the high cooling rate and low final cooling temperature require higher equipment. Theref...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/38C21D8/02
CPCC21D8/0205C21D8/0221C21D2211/005C21D2211/008C22C38/02C22C38/04C22C38/06C22C38/18
Inventor 郭景瑞邓建军谷凤龙何方刘守显徐斌蒋建朋程迪郭振国
Owner HBIS COMPANY LIMITED HANDAN BRANCH COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap