A kind of water-repellent composite mineral rock wool board for roofing

A technology of composite mineral and rock wool boards, which is applied to roofs, roof coverings, roofs using flat/curved panels, etc., can solve the problems of high cost and rising costs, and achieve moisture isolation, improve integrity, and ensure thermal insulation performance Effect

Active Publication Date: 2016-09-07
河北华能耐火保温材料股份有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the imported product is relatively expensive, which will bring about a huge increase in cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-repellent composite mineral rock wool board for roofing
  • A kind of water-repellent composite mineral rock wool board for roofing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Production method of hydrophobic composite rock wool board for roofing:

[0022] (1) Raw material preparation: mix basalt, fly ash, gabbro, iron ore, bauxite, wollastonite, and melt them into a liquid mixture;

[0023] (2) Hydrophobic liquid preparation, according to weight percentage: SILRES BS 104 20.3%, methyl cellulose 5%, polyacrylamide solution 1%, the rest is phenolic resin and mixed evenly;

[0024] (3) Fiber preparation: The liquid mixture is continuously flowed into the high-speed rotating centrifugal roller, and the liquid mixture is condensed into filamentous filaments under the action of centrifugal throwing and air cooling, and the filaments are collected and formed under the action of the blower. , spray the hydrophobic liquid evenly on the rock wool fiber;

[0025] The (1) raw material components are calculated by weight percentage: basalt 10%, fly ash 25%, gabbro 1.3%, iron ore 2.7%, bauxite 25%, wollastonite 36%.

[0026] (4) fiber body preparation: ...

Embodiment 2

[0029] Production method of hydrophobic composite rock wool board for roofing:

[0030] (1) Raw material preparation: mix basalt, fly ash, gabbro, iron ore, bauxite, wollastonite, and melt them into a liquid mixture;

[0031] (2) Preparation of hydrophobic liquid, according to weight percentage: SILRES BS 1042 0.5%, methyl cellulose 8%, polyacrylamide solution 2%, and the rest is phenolic resin and mixed evenly;

[0032] (3) Fiber preparation: The liquid mixture is continuously flowed into the high-speed rotating centrifugal roller, and the liquid mixture is condensed into filamentous filaments under the action of centrifugal throwing and air cooling, and the filaments are collected and formed under the action of the blower. , spray the hydrophobic liquid evenly on the rock wool fiber;

[0033] The (1) raw material components are calculated by weight percentage: basalt 15%, fly ash 20%, gabbro 5.8%, iron ore 1.2%, bauxite 20%, wollastonite 38%.

[0034] (4) fiber body prepar...

Embodiment 3

[0037] Production method of hydrophobic composite rock wool board for roofing:

[0038] (1) Raw material preparation: mix basalt, fly ash, gabbro, iron ore, bauxite, wollastonite, and melt them into a liquid mixture;

[0039] (2) Hydrophobic liquid preparation, according to weight percentage: SILRES BS 1042 0.4%, methyl cellulose 6%, polyacrylamide solution 1.5%, and the rest is phenolic resin and mixed evenly;

[0040] (3) Fiber preparation: The liquid mixture is continuously flowed into the high-speed rotating centrifugal roller, and the liquid mixture is condensed into filamentous filaments under the action of centrifugal throwing and air cooling, and the filaments are collected and formed under the action of the blower. , spray the hydrophobic liquid evenly on the rock wool fiber;

[0041] The (1) raw material components are calculated by weight percentage: basalt 12%, fly ash 14%, gabbro 2.8%, iron ore 1.2%, bauxite 30%, wollastonite 40%.

[0042] (4) fiber body prepara...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method for a hydrophobic composite mineral wool board for a roof. The production method comprises the following steps of (1) preparing raw materials, namely mixing graystone, fly ash, gabbro, iron ore, bauxite and wollastonite, and melting the raw materials into a liquid mixture; (2) preparing hydrophobic liquid, namely uniformly mixing 0.3 to 0.5 weight percent of SILRES BS 1042, 5 to 8 weight percent of methylcellulose, 1 to 2 weight percent of polyacrylamide solution and the balance of phenolic resin phase; (3) preparing fibers, namely uniformly spraying the hydrophobic liquid onto mineral wool fibers; (4) preparing a fibrous body; (5) preparing a finished product, namely compounding a hard fireproof board on the upper layer of the fibrous body and compounding a dampproof aluminum foil veneer on the lower layer of the fibrous body.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a hydrophobic composite mineral rock wool board for roofing. Background technique [0002] At present, domestic standard buildings lack thermal insulation and fireproof materials with better performance, so fires occur frequently. The existing inorganic fiber cotton products belong to the flat fiber layered structure and cannot be directly used for external wall insulation: First, the fireproof basis of inorganic fiber The performance is very good, but the environmental protection performance and construction performance are very poor, and the fibers flying with the wind directly affect the health of the on-site personnel; secondly, its layered structure causes the mortar and cementitious materials applied on the surface of the product to only fix the surface layer, and the middle layer Will slowly sag over time, causing the insulation to form cavities, crack, and fall off. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04D3/18
Inventor 潘高峰
Owner 河北华能耐火保温材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap