Hydrophilic pressure-sensitive adhesive containing garlic volatile oil and preparation method thereof

A technology of garlic volatile oil and pressure-sensitive adhesive, which is applied to medical preparations containing active ingredients, medical preparations without active ingredients, and pharmaceutical formulas, etc., to achieve obvious economic benefits and promote wound healing

Active Publication Date: 2016-09-28
邳州奇威食品科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there is no report yet to point out that garlic volatile oil is used to prepare pressure-sensitive adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Preparation of polyurethane

[0021] Add polytetrahydrofuran diol into the reactor, melt at 100°C to remove water under reduced pressure, and at 65°C and normal pressure, add isophorone diisocyanate at a molar ratio of isocyanate group / alcohol hydroxyl group of 115:210 , and add butanone as a solvent, react at 80°C for 1.5h, then add an amine chain extender dissolved in butanone to the system, react for 2h, remove the butanone solvent under reduced pressure, and discharge to obtain a crude polyurethane. spare;

[0022] (2) Preparation of hydrophilic polyurethane pressure-sensitive adhesive containing garlic volatile oil

[0023] Mix 30 parts of polyurethane crude product prepared in step (1) with 40 parts of alginate in an open mill for 30 minutes, then add 10 parts of chitosan, 0.1 part of garlic volatile oil and 2 parts of tributyl citrate to continue Knead for 10 minutes to disperse evenly, and then use a flat vulcanizer to hot-press the pressure-sensitive adhe...

Embodiment 2

[0025] (1) Preparation of polyurethane

[0026] Add polytetrahydrofuran diol into the reactor, melt at 105°C to remove water under reduced pressure, and at 66°C and normal pressure, add isophorone diisocyanate at a molar ratio of isocyanate group / alcohol hydroxyl group of 115:210 , and add butanone as a solvent, react at 82°C for 1.6h, then add an amine chain extender dissolved in butanone to the system, react for 2h, remove the butanone solvent under reduced pressure, and discharge to obtain a crude polyurethane product, spare;

[0027] (2) Preparation of hydrophilic polyurethane pressure-sensitive adhesive containing garlic volatile oil

[0028] Mix 32 parts of polyurethane crude product prepared in step (1) with 45 parts of alginate in an open mixer for 32 minutes, then add 15 parts of chitosan, 1 part of garlic volatile oil and 3 parts of tributyl citrate to continue Knead for 13 minutes to make it evenly dispersed, and then use a flat vulcanizer to heat-press the pressu...

Embodiment 3

[0030] (1) Preparation of polyurethane

[0031] Add polytetrahydrofuran diol into the reactor, melt at 110°C to remove water under reduced pressure, and at 68°C and normal pressure, add isophorone diisocyanate at a molar ratio of isocyanate group / alcohol hydroxyl group of 115:210 , and add butanone as a solvent, react at 84°C for 1.8h, then add an amine chain extender dissolved in butanone to the system, react for 2h, remove the butanone solvent under reduced pressure, and discharge to obtain a crude polyurethane product, spare;

[0032] (2) Preparation of hydrophilic polyurethane pressure-sensitive adhesive containing garlic volatile oil

[0033] Mix 36 parts of polyurethane crude product prepared in step (1) with 50 parts of alginate in an open mixer for 35 minutes, then add 20 parts of chitosan, 5 parts of garlic volatile oil and 4 parts of tributyl citrate to continue Knead for 16 minutes to disperse evenly, and then use a flat vulcanizer to hot-press the pressure-sensit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hydrophilic pressure-sensitive adhesive containing garlic volatile oil and a preparation method thereof. The pressure-sensitive adhesive comprises the following components in parts by weight: 30 to 40 parts of polyurethane, 40 to 55 parts of alginate, 10 to 25 parts of chitosan, 0.1 to 10 parts of garlic volatile oil, and 1 to 5 parts of tributyl citrate. The polyurethane is prepared through the condensation reactions between polytetramethylene glycol and isophorone diisocyanate. The preparation method comprises the following steps: (1) preparing polyurethane; (2) preparing a hydrophilic polyurethane pressure-sensitive adhesive containing garlic volatile oil. The hydrophilic pressure-sensitive adhesive has the curative functions of preventing infection and promoting injury heal, has the advantages of non-toxicity, non-irritant property, and no allergy or peeling reactions, is a safe and reliable medical pressure-sensitive adhesive, and has a prominent economic profit.

Description

technical field [0001] The invention relates to the field of biomedical pressure-sensitive adhesives, in particular to a hydrophilic pressure-sensitive adhesive containing garlic volatile oil and a preparation method thereof. Background technique [0002] With the advancement of medicine, the clinical requirements for the effect of surgical techniques and auxiliary materials are getting higher and higher. The philosophy of modern medicine is to minimize the suffering of patients. To recover the patient as quickly as possible, and while restoring function to the greatest extent, it is hoped that the appearance will also be restored perfectly. Therefore, the continuous increase of clinical demand has promoted the development of adhesives and the application of adhesive technology in clinic. [0003] Pressure-sensitive adhesive is a kind of adhesive that produces viscosity under pressure and leaves no residue after pressure loss, and is the main auxiliary material of transder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/44A61L15/28A61L15/26A61L15/20C08G18/75C08G18/66C08G18/48
CPCA61K9/7023A61K9/7069A61K36/8962A61K47/34A61K47/36A61L24/0015A61L24/06A61L24/08A61L26/0019A61L26/0023A61L26/0066A61L2300/30A61L2300/404A61L2300/412C08G18/4854C08G18/6685C08G18/755C08L75/04
Inventor 邱东成刘乐峰郭玉芹
Owner 邳州奇威食品科技有限公司