A kind of waterborne polyurethane resin for pressure-sensitive adhesive and preparation method thereof

A water-based polyurethane and pressure-sensitive adhesive technology, applied in the field of water-based polyurethane pressure-sensitive adhesives, can solve the problems of poor water resistance of hydrophilic polyurethane pressure-sensitive adhesives, and achieve simple and easy preparation methods, good process controllability, and water resistance good effect

Active Publication Date: 2018-01-30
XIANGYANG SUNVALOR AEROSPACE FILMS CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Publication No. CN1456630 of Chinese invention patent application publication provides a kind of "hydrophilic polyurethane pressure-sensitive adhesive and its preparation method"; the hydrophilic polyurethane pressure-sensitive adhesive provided by this specification has poor water resistance; Chinese invention patent application publication publication No. CN103031103A (a nano-modified water-based polyurethane pressure-sensitive adhesive for protective film and its preparation method), the disadvantage is that it is necessary to add nano-modified ions to improve the performance of the adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Put 600Kg of hydroxyl-terminated polyester polyol with a hydroxyl content of 0.8mmol / g into the reactor, heat up to 100-120°C, dehydrate under reduced pressure for 120 minutes, cool down to 60-70°C, add 100.22kg of TDI, and keep warm at 80°C for 110-120min , add 100 kg of N-methylpyrrolidone solution of dimethylolpropionic acid, continue to keep warm at 80°C for 110-120min, cool down to 50-55°C, add 21.48Kg of triethylamine, stir fully for 10min, stop stirring, and quickly Inject 1055Kg of deionized water into the reaction kettle, turn on the stirring and emulsifying machine, add 47.08Kg ethylenediamine solution after emulsifying for 10 minutes, continue emulsifying for 10 minutes, stop emulsifying, continue stirring for 120 minutes, filter the material, and pack it in a plastic barrel. The reactant is Waterborne Polyurethane Resin for Pressure Sensitive Adhesives, 180 o Peel strength 300g.

Embodiment 2

[0030] Put 600Kg of hydroxyl-terminated polyester polyol with a hydroxyl content of 0.8mmol / g into the reactor, heat up to 100-120°C, dehydrate under reduced pressure for 120 minutes, cool down to 60-70°C, add 100.22kg of TDI, and keep warm at 80°C for 110-120min , add 110 kg of N-methylpyrrolidone solution of dimethylolpropionic acid, continue to keep warm at 80°C for 110-120min, cool down to 50-55°C, add 22.38Kg of triethylamine, fully stir for 10min, stop stirring, and quickly Inject 1028Kg of deionized water into the reaction kettle, turn on the stirring and emulsifying machine, add 34.45Kg ethylenediamine solution after emulsifying for 10 minutes, continue emulsifying for 10 minutes, stop emulsifying, continue stirring for 120 minutes, filter the material, and pack it in a plastic barrel. The reactant is Waterborne Polyurethane Resin for Pressure Sensitive Adhesives, 180 o Peel strength 270g.

Embodiment 3

[0032] Put 600Kg of hydroxyl-terminated polyester polyol with a hydroxyl content of 0.8mmol / g into the reactor, heat up to 100-120°C, dehydrate under reduced pressure for 120 minutes, cool down to 60-70°C, add 100.22kg of TDI, and keep warm at 80°C for 110-120min , add 120 kg of N-methylpyrrolidone solution of dimethylol propionic acid, continue to keep warm at 80°C for 110-120min, cool down to 50-55°C, add 23.06Kg of triethylamine, fully stir for 10min, stop stirring, and quickly go to Inject 1032Kg of deionized water into the reaction kettle, turn on the stirring and emulsifying machine, add 24.24Kg ethylenediamine solution after emulsifying for 10 minutes, continue emulsifying for 10 minutes, stop emulsifying, continue stirring for 120 minutes, filter and discharge the material, and pack it in a plastic barrel. The reactant is Waterborne Polyurethane Resin for Pressure Sensitive Adhesives, 180 o Peel strength 240g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses aqueous polyurethane resin for a pressure-sensitive adhesive and a preparation method thereof. The preparation method comprises the following steps of carrying out pressure reduction dehydration on hydroxyl-terminated polyester polyol, carrying out cooling, adding diisocyanate into a reactor, carrying out a reaction process at a temperature of 70-90 DEG C for 110-120min, adding a dimethylolpropionic acid solution into the reaction product, carrying out a reaction process for 110-120min, cooling the reaction product to 50-55 DEG C, adding triethylamine into the reaction product for neutralization, carrying out full stirring for 8-10min, stopping stirring, fast pouring deionized water into the reactor, starting stirring and emulsification devices, carrying out emulsification for 8-10min, adding an ethanediamine solution into the emulsion, sequentially carrying out emulsification for 8-10min, stopping emulsification, sequentially carrying out stirring for 90-120min, carrying out filtration and discharging the product. The aqueous polyurethane resin has 180 degree peel strength of 30-300g / 25mm. Through coating machine-based coating, a plurality of the pressure-sensitive adhesive products with excellent performances are obtained and can be widely used for all industries. The preparation method is simple and easy.

Description

technical field [0001] The invention relates to a water-based polyurethane pressure-sensitive adhesive, in particular to a water-based polyurethane resin used for pressure-sensitive adhesives and a preparation method thereof. Background technique [0002] The full name of pressure-sensitive adhesive is pressure-sensitive adhesive, commonly known as self-adhesive, which is a type of adhesive system. According to the curing method and properties, pressure-sensitive adhesives can be divided into: solvent-based pressure-sensitive adhesives, emulsion-type pressure-sensitive adhesives, water-soluble pressure-sensitive adhesives, hot-melt pressure-sensitive adhesives, UV-curable pressure-sensitive adhesives, and electron beam-cured pressure-sensitive adhesives. Type pressure sensitive adhesive, etc. According to the composition and structure of the main resin, pressure-sensitive adhesives can be divided into: rubber pressure-sensitive adhesives, polyacrylate pressure-sensitive adh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/76C08G18/66C08G18/42C08G63/181C09J175/06
CPCC08G18/10C08G18/3228C08G18/348C08G18/6659C08G18/721C08G18/7614C08G63/181C09J175/06
Inventor 丁温娜洪晓忠
Owner XIANGYANG SUNVALOR AEROSPACE FILMS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com