EVA composite foam material and preparation method thereof

A composite foaming and blowing agent technology, applied in the field of industrial materials, can solve problems affecting human health, etc., and achieve the effects of excellent elasticity, excellent physical properties, and low compression

Active Publication Date: 2015-03-25
ANTA CHINA
View PDF2 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Ammonia is an inorganic compound. It is a gas at room temperature. It is colorless and has a pungent odor. Excessive ammonia content will affect human heal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • EVA composite foam material and preparation method thereof
  • EVA composite foam material and preparation method thereof
  • EVA composite foam material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0048] Correspondingly, the present invention also provides a preparation method of the EVA composite foam material, including the following steps:

[0049] Step 1: Weigh the following components in parts by weight: 50 to 90 parts of ethylene-vinyl acetate copolymer, 0 to 30 parts of polyolefin thermoplastic elastomer, 0 to 30 parts of EPDM, 0 to 20 parts of filler, 0.7 to 2.5 parts of odorless crosslinking agent, 1 to 8 parts of foaming agent and 5 to 10 parts of ammonia removal agent.

[0050] Step 2: Pour all the ingredients weighed in step 1 except for the odorless crosslinking agent, ammonia removal agent, and foaming agent into an internal mixer for mixing. The mixing time can preferably be 8 minutes to 10 minutes , The temperature can preferably be 110℃~115℃;

[0051] Step 3: Add the odorless crosslinking agent, ammonia removal agent, and foaming agent weighed in step 1 to the mixed materials for mixing. The mixing time can be preferably 5 minutes to 8 minutes, and the temper...

Example

[0056] Examples 1~3

[0057]

[0058] Table 1: Blending formula of EVA composite foam material (parts)

[0059] 1) Weigh the raw materials according to the composition of the raw materials in Table 1 and the weight parts of each component;

[0060] 2) Pour all the raw materials weighed in step 1 except for the crosslinking agent and foaming agent into an internal mixer for mixing. The mixing time is 8 minutes and the temperature is 110-115°C.

[0061] 3) Add odorless crosslinking agent, ammonia removal agent, and foaming agent to the material mixed in step two for mixing, mixing time 6 minutes, temperature 115-120°C.

[0062] 4) Pour the obtained mixture into a granulator for granulation, and then foam by molding or one-shot injection to obtain a foamed material for sports shoe soles.

[0063] After the foamed material for the sports shoe sole obtained in step 4 is cooled, it is processed to be rough through the semi-finished product treatment, and then molded and formed to obtain a fini...

Example

[0065] Examples 4~6

[0066]

[0067] Table 2: Blending formula of EVA composite foam material (parts)

[0068] 1) Weigh the raw materials according to the composition of the raw materials in Table 1 and the weight parts of each component;

[0069] 2) Pour all the raw materials weighed in step 1 except for the crosslinking agent and foaming agent into an internal mixer for mixing. The mixing time is 8 minutes and the temperature is 110-115°C.

[0070] 3) Add odorless crosslinking agent, ammonia removal agent, and foaming agent to the material mixed in step two for mixing, mixing time 6 minutes, temperature 115-120°C.

[0071] 4) Pour the obtained mixture into a granulator for granulation, and then foam by molding or one-shot injection to obtain a foamed material for sports shoe soles.

[0072] After the foamed material for the sports shoe sole obtained in step 4 is cooled, it is processed to be rough through the semi-finished product treatment, and then molded and formed to obtain a fini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an EVA composite foam material and a preparation method thereof. The EVA composite foam material comprises the following components in parts by weight: 50-90 parts of an ethylene-vinyl acetate copolymer, 0-30 parts of a polyolefin thermoplastic elastomer, 0-30 parts of ethylene propylene diene monomer, 0-20 parts of a filler, 0.7-2.5 parts of a tasteless crosslinking agent, 1-8 parts of a foaming agent and 5-10 parts of a deammoniation agent. The EVA composite foam material is free of ammonia gas flavor and peculiar smell, good in elasticity and good in physical property. The preparation method of the EVA composite foam material comprises the following steps: (1) weighing the components of the EVA composite foam material; (2) pouring all the components excluding the tasteless crosslinking agent, the deammoniation agent and the foaming agent into an internal mixer for mixing; (3) adding the crosslinking agent, the deammoniation agent and the foaming agent into the mixed materials for mixing; (4) pouring the obtained mixture into a granulator for granulation and then foaming to obtain the EVA composite foam material free of ammonia flavor.

Description

technical field [0001] The invention relates to the field of industrial materials, in particular to an EVA composite foam material and a preparation method thereof. Background technique [0002] EVA foam material is ethylene-vinyl acetate (vinyl acetate) copolymer, which is made by copolymerization of ethylene (English name: Ethylene) and vinyl acetate (English name: Vinyl Acetate). The full English name is: Ethylene Vinyl Acetate, referred to as EVA, or E / VAC. Among them, the vinyl acetate content is generally 5% to 40%. Because of its low cost, and compared with polyethylene, EVA has reduced crystallinity and improved flexibility, impact resistance, filler compatibility, and heat sealing performance due to the introduction of vinyl acetate monomer in the molecular chain, so It is widely used in various fields, such as: shoe industry, building materials industry, luggage industry, toy industry and so on. [0003] The EVA foam material used in the field of shoe materials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L23/00C08L23/16C08K13/02C08K3/34C08K5/14C08J9/10
CPCC08J9/103C08J2203/04C08J2205/052C08J2323/08C08J2423/00C08J2423/08C08J2423/16C08L23/0853C08L23/00C08L23/16C08K13/02C08K3/34C08K5/14C08L23/0815
Inventor 刘成柯育发成升良陈爱民
Owner ANTA CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap