Ionic liquid filtering and recycling method
A process method and ionic liquid technology, applied in the field of filtration and recovery of new materials, using diatomaceous earth to filter and recover ionic liquids, can solve the problems of difficult filtration and recovery of high-viscosity ionic liquids, achieve light film color, increase filtration speed, and solve Difficult effect of filtration recovery
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] A process for filtering and recovering ionic liquids, comprising the following steps:
[0026] 1. Preparation of diatomite pre-coating
[0027] Add 200-mesh diatomite with a permeability of 12 Darcy to the pre-coating tank, prepare a diatomite solution with a mass concentration of 3% with ionic liquid, pass the diatomite solution through a closed plate filter, and put it on the filter plate. Diatomite coating is formed on the surface, and the amount of diatomite is 1.5kg / m 2 .
[0028] 2. Filter
[0029] The ionic liquid with a concentration of 90%, a temperature of 25°C, and a viscosity of 100mpa.s is filtered through the closed plate filter in step 1. The filtration speed is 2-3t / h, and the filtration pressure is 0-0.4MPa, which greatly improves the Filtration rate of ionic liquids.
[0030] The turbidity of the filtered ionic liquid was determined to be 20 degrees, and the filtered ionic liquid was concentrated for a dissolution and film pulling test. After the f...
Embodiment 2
[0033] A process for filtering and recovering ionic liquids, comprising the following steps:
[0034] 1. Preparation of diatomite pre-coating
[0035] Add 600-mesh diatomite with a permeability of 12 Darcy to the pre-coating tank, prepare a diatomite solution with a mass concentration of 3% with ionic liquid, pass the diatomite solution through a closed plate filter, and put it on the filter plate. Diatomite coating is formed on the surface, and the amount of diatomite is 1.5kg / m 2 .
[0036] 2. Filter
[0037] The ionic liquid with a mass concentration of 90%, a temperature of 25°C, and a viscosity of 100mpa.s is filtered through the closed plate filter in step 1. The filtration speed is 2-3t / h, and the filtration pressure is 0-0.4MPa, which greatly improves the filtration rate of ionic liquids.
[0038] The turbidity of the filtered ionic liquid was determined to be 100 degrees, the filtered ionic liquid was concentrated, and the dissolution and film pulling test was don...
Embodiment 3
[0041] A process for filtering and recovering ionic liquids, comprising the following steps:
[0042] 1. Preparation of diatomite pre-coating
[0043] Add 200-mesh diatomite with a permeability of 12 Darcy to the pre-coating tank, prepare a diatomite solution with a mass concentration of 3% with ionic liquid, pass the diatomite solution through a closed plate filter, and put it on the filter plate. Diatomite coating is formed on the surface, and the amount of diatomite is 1.5kg / m 2 .
[0044] 2. Filter
[0045] The ionic liquid with a mass concentration of 90%, a temperature of 80°C, and a viscosity of 40mpa.s is filtered through the closed plate filter in step 1. The filtration speed is 2-3t / h, and the filtration pressure is 0-0.4MPa, which greatly improves the filtration rate of ionic liquids.
[0046] The turbidity of the filtered ionic liquid was measured to be 50 degrees, and the filtered ionic liquid was concentrated, and the film dissolution test was done. After the...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
degree of polymerization | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap