Multifunctional vulcanized rubber containing polyvinylpyrrolidone-modified graphene oxide and preparation method of multifunctional vulcanized rubber

A technology of polyvinylpyrrolidone and stone oxide, which is applied in the field of rubber polymer composite materials and its preparation, to achieve the effect of simple and convenient preparation steps and excellent mechanics

Active Publication Date: 2015-04-29
NANJING UNIV OF SCI & TECH +1
View PDF5 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, there have been no reports of functionalized rubber vulcanizates containing polyvinylpyrrolid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional vulcanized rubber containing polyvinylpyrrolidone-modified graphene oxide and preparation method of multifunctional vulcanized rubber
  • Multifunctional vulcanized rubber containing polyvinylpyrrolidone-modified graphene oxide and preparation method of multifunctional vulcanized rubber
  • Multifunctional vulcanized rubber containing polyvinylpyrrolidone-modified graphene oxide and preparation method of multifunctional vulcanized rubber

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A kind of preparation method of the multifunctional rubber vulcanizate containing modified graphene oxide of the present invention comprises the following steps:

[0026] Step 1: Preparation of polyvinylpyrrolidone-modified graphene oxide: Add graphite oxide to the aqueous solution, ultrasonically disperse, ultrasonic time 0.5-1h, power 100-300W, add polyvinylpyrrolidone, continue ultrasonic stirring, ultrasonic time 0.5 -1h, power 100-300W, obtain polyvinylpyrrolidone modified graphene oxide aqueous solution;

[0027] Step 2: mixing and stirring the polyvinylpyrrolidone-modified graphene oxide aqueous solution prepared in step 1 with rubber latex, adding a gelling agent, washing and drying the gel to obtain a rubber mixture containing polyvinylpyrrolidone-modified graphene oxide;

[0028] Step 3: After mixing the rubber mixture containing polyvinylpyrrolidone modified graphene oxide obtained in step 2 with zinc oxide, stearic acid, anti-aging agent, accelerator and vul...

Embodiment 1

[0040] Disperse 1 part of graphite oxide in the aqueous solution, 100W ultrasonic 1h, add 1 part of polyvinylpyrrolidone, power 100W ultrasonic stirring 1h, obtain polyvinylpyrrolidone modified graphene oxide aqueous solution, wherein the size of polyvinylpyrrolidone modified graphene oxide is as follows figure 2; Add it dropwise to natural rubber latex, mix and stir, and add a gel agent, wash and dry the gel to obtain a rubber mixture containing 1 part of modified graphene oxide; further mix it with 3 parts of zinc oxide, 1 part of Stearic acid, 2 parts of RD, 0.5 parts of DM and 3 parts of sulfur are mixed on the open mill, parked, and the vulcanization time is measured with a vulcanizer, and then the rubber vulcanizate is obtained with a flat vulcanizer. Among them, the XRD diffraction of vulcanized rubber is as follows figure 1 shown. The detailed properties of the vulcanizate are shown in Table 1.

Embodiment 2

[0042] Repeat the method of Example 1 according to the specified content of each component, but adopt 2 parts of polyvinylpyrrolidone-modified graphene oxide in the formula. The detailed properties of the vulcanizate are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average lengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses multifunctional vulcanized rubber containing polyvinylpyrrolidone-modified graphene oxide and a preparation method of the multifunctional vulcanized rubber. The multifunctional vulcanized rubber comprises the following components in parts by mass: 100 parts of rubber matrix, 1-4 parts of polyvinylpyrrolidone-modified graphene oxide, 2-5 parts of an anti-aging agent, 3-10 parts of zinc oxide, 1-3 parts of stearic acid, 0.5-1 part of a vulcanizing accelerator and 1-3 parts of a vulcanizing agent. The multifunctional vulcanized rubber prepared by the method has a plurality of functions, such as a mechanical function, a heat-conducting function and a solvent-resistant function.

Description

technical field [0001] The invention belongs to rubber-like polymer composite materials and a preparation method thereof, in particular to a multifunctional rubber vulcanizate containing polyvinylpyrrolidone-modified graphene oxide and having excellent mechanical properties, heat conduction and solvent resistance, and a preparation method thereof. Background technique [0002] Multifunctional rubber vulcanizates, that is, rubber vulcanizates with excellent mechanical properties, thermal conductivity and solvent resistance, are one of the research hotspots in the rubber industry. Graphene oxide, a two-dimensional material, has the characteristics of high mechanical strength (63GPa), high modulus, large specific surface area and good barrier properties, and is easy to prepare and low cost. It has received extensive attention as a new carbon-based material. However, since the surface of graphene oxide contains a large number of oxygen-containing functional groups, graphene oxid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L9/00C08L9/06C08K13/06C08K9/04C08K3/04C08K3/22C08K5/09C08K5/18C08K5/3437
CPCC08K2201/014C08L7/00C08L9/00C08L9/06C08L2205/03C08L39/06C08K13/06C08K9/04C08K3/04C08K2003/2296C08K5/09C08K5/3437C08K5/47C08K3/06C08K5/18
Inventor 贾红兵张旭敏刘鹏章王经逸熊晓刚张佳佳何俊宽徐子钦殷标
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap