A kind of non-ionic liquid crystal asphalt warm mix agent and preparation method thereof

A warm mix agent and non-ionic technology, applied in building insulation materials, building components, climate change adaptation, etc., can solve the problems of reducing the performance of asphalt mixture, water damage of asphalt mixture, generating a large amount of water vapor, etc., and achieve stable performance , Reduce high temperature viscosity, reduce human hazards and environmental pollution effects

Active Publication Date: 2017-01-25
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is inevitable that some water will remain between the asphalt and aggregate interface during the production process, making the asphalt mixture potentially water-damaged
Moreover, if the amount of water added is too large, a large amount of water vapor will be generated or bumping will occur. If the amount of water is too small, the foaming effect will be poor.
[0005] At present, the domestically developed warm mix asphalt additive products are mainly organic and surface active, such as the published patent CN102093731A, patent CN102408602A, patent CN101899218A, patent CN101831187A, patent CN102795801A, etc. Although domestically developed warm mix asphalt additive products are basically It can achieve the cooling effect of similar foreign products and can successfully produce warm mix asphalt mixture, but there are inevitably defects such as complex production process, high energy consumption, and reduced performance of asphalt mixture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of non-ionic liquid crystal asphalt warm mix agent and preparation method thereof
  • A kind of non-ionic liquid crystal asphalt warm mix agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Polyglyceryl Laurate: 12 parts

[0027] Lauryl alcohol: 2.5 parts

[0028] Water: 84.5 parts.

[0029] Add polyglyceryl laurate and deionized water into the container according to the proportion, and stir at 40°C for 1 hour; add lauryl alcohol, stir at a constant temperature of 40°C for 1 hour, and stand at room temperature for 3 hours to obtain a non-ionic liquid crystal asphalt warm mix agent .

Embodiment 2

[0031] Polyglycerol monooleate: 30 parts

[0032] Stearyl alcohol: 1.7 parts

[0033] Water: 68.3 parts.

[0034] Add polyglycerol monooleate and deionized water into the container according to the ratio, and stir at 50°C for 1 hour; add stearyl alcohol, stir at a constant temperature of 50°C for 1.5 hours, and stand at room temperature for 3.5 hours to obtain non-ionic liquid crystal pitch Mixture.

Embodiment 3

[0036] Polyglyceryl Laurate: 41 parts

[0037] n-octanol: 2.5 parts

[0038] Water: 56.5 parts.

[0039] Add polyglycerol laurate and deionized water into the container according to the ratio, and stir at 60°C for 1 hour; add n-octanol, stir at a constant temperature of 60°C for 1.5 hours, and stand at room temperature for 4 hours to obtain non-ionic liquid crystal type asphalt. agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a non-ionic liquid crystal asphalt warm mixing agent and a preparation method thereof. The asphalt warm mixing agent comprises the following components in parts by weight: 3.5-55.5 parts of polyglycerol fatty acid ester, 0.1-20 parts of fatty alcohol and 24.5-96.4 parts of water. The preparation method comprises the following steps: (1) uniformly mixing water and polyglycerol fatty acid ester in a container according to the ratio; (2) adding fatty alcohol into the mixture obtained in the step (1) for uniform mixing, and leaving the mixture to stand for a period of time to obtain the non-ionic liquid crystal asphalt warm mixing agent. The non-ionic liquid crystal asphalt warm mixing agent disclosed by the invention can effectively reduce the high-temperature viscosity of asphalt and has the advantages of stable performance, available raw material, simple and convenient preparation method, wide application range and the like.

Description

technical field [0001] The invention relates to an asphalt warm mix agent and a preparation method thereof, in particular to a non-ionic liquid crystal type asphalt warm mix agent and a preparation method thereof. Background technique [0002] Since asphalt was used in roads, the mature asphalt mixture is mainly hot mix asphalt mixture. However, hot mix asphalt mixture has defects such as high mixing temperature and paving temperature, high emission of harmful gases, and easy aging of asphalt mixture. , resulting in many ecological and environmental problems. Warm mix asphalt mixture is a new material that is environmentally friendly and energy-saving. It has the same or even better road performance as the corresponding hot mix asphalt mixture, but it can be mixed and paved at a lower temperature, which greatly reduces the The energy consumption and soot emission in the production process have significantly improved the economic benefits and ecological value. Compared with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L71/08C08K5/05C04B26/26C04B24/08
CPCY02A30/30
Inventor 宣根海徐青柏陈杰石君章宁爱民李志军
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products