Method for manufacturing high-conductivity corrosion-resistant pure copper special cable

A corrosion-resistant, high-conductivity technology, applied in cable/conductor manufacturing, circuits, electrical components, etc., to achieve both corrosion resistance and tensile strength, low cost, and increased strength

Inactive Publication Date: 2015-04-29
ANHUI CHUJIANG HIGH TECH ELECTRIC WIRE CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing submarine cables include their wrapping and protective outer cladding, which are subject to microbial adsorption on the surface and cause corrosion, which cannot avoid the problem of microorganisms entering the outer cladding and causing cable core pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be further described below in conjunction with specific embodiments.

[0023] A method for preparing a special cable made of highly conductive and corrosion-resistant pure copper, characterized in that it comprises the following steps:

[0024] (1) The material for high-strength and high-conductivity pure copper wire is based on high-purity cathodic electrolytic copper with a purity of more than 99.957%;

[0025] (2) Strictly remove surface dirt and preheat to 80-100°C by baking;

[0026] (3) Using a power frequency electromagnetic melting furnace for melting, integrating melting and electromagnetic stirring, and controlling the melting temperature within the range of 1150±10°C to ensure that the electrolytic copper is fully melted and mixed evenly;

[0027] (4) The molten copper that has been completely smelted by the power frequency electromagnetic melting furnace overflows from the power frequency electromagnetic melting furnac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for manufacturing a high-conductivity corrosion-resistant pure copper special cable, and belongs to the technical field of material processing. High-purity cathode electrolytic copper is adopted as a substrate of a wire, and the cable is formed through mixing and preheating, smelting, heat preservation, traction, wire drawing, crystallization, annealing and cooling and oxide layer plating treatment. The TR specification volume resistivity of the cable is smaller than or equal to 0.01707omega.cm<3>, and the tensile strength of the cable is more than 420 MPa. The method can meet the requirement of submarine cables for high-conductivity corrosion-resistant materials well, and can be used for the field requiring high-conductivity high-strength materials. The method has the advantages of being simple in process and low in cost.

Description

technical field [0001] The invention belongs to the technical field of material processing, and more specifically relates to a preparation method of a special cable made of high-conductivity and corrosion-resistant pure copper. Background technique [0002] Pure copper has high electrical and thermal conductivity, high plastic deformation ability, and good corrosion resistance. It is widely used in industry as a good conductor. However, although pure copper has the advantage of high electrical conductivity, its tensile strength is extremely low, usually only 120-160MPa. In addition, pure copper has high plastic deformation ability, but it is easy to work harden due to its extremely low static recrystallization temperature, thereby inhibiting further plastic deformation. Therefore, pure copper materials are mostly used in wires, conductors and coolers, etc., and it is difficult to meet various application requirements as a structural material. Generally, the conductivity o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/22H01B13/00C22F1/08B21C1/00
Inventor 任结
Owner ANHUI CHUJIANG HIGH TECH ELECTRIC WIRE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap