Polyethylene powder for anti-corrosive pipeline and preparation method for polyethylene powder

A polyethylene powder and polyethylene technology, applied in powder coatings, anti-corrosion coatings, coatings, etc., can solve the problems of inconsistent anti-corrosion ideas, inconsistency in anti-corrosion effects of steel pipes, and high energy consumption, so as to improve the anti-corrosion effect and achieve good dry powder. Liquidity, the effect of simplifying the production process

Active Publication Date: 2015-05-13
GUANGZHOU LUSHAN NEW MATERIALS +1
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 3PE anti-corrosion also has its own defects, mainly as follows: First, traditionally, the three-layer PE coating of steel pipes at home and abroad is formed by extruders to extrude the middle binder and the outer layer of polyethylene respectively to make it coated On the outside of the epoxy primer, for each set of production molding equipment, two extrusion equipment are required, and the energy consumption is relatively large
Although the patent CN1865379A adopts a two-

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene powder for anti-corrosive pipeline and preparation method for polyethylene powder
  • Polyethylene powder for anti-corrosive pipeline and preparation method for polyethylene powder
  • Polyethylene powder for anti-corrosive pipeline and preparation method for polyethylene powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A polyethylene powder for anti-corrosion pipelines, prepared from the following raw materials by weight percentage: 7% polyethylene graft adhesive resin, 55% polyolefin matrix resin, 23% polyolefin reinforced resin, toughened Agent 10%, polyacrylate (leveling agent) 0%, carbon black masterbatch 4.5%, antioxidant 0.5%.

[0030] Wherein, the formula (100%) of polyolefin matrix resin:

[0031] HDPE 70%;

[0032] LDPE 30%;

[0033] Wherein, the composition of toughening agent is (100%):

[0034] POE 75%;

[0035] SEBS 25%;

[0036] Wherein the composition of antioxidant is (100%):

[0037] Antioxidant 1010 30%;

[0038] Antioxidant 168 60%;

[0039] Light stabilizer 10%.

[0040] A preparation method of polyethylene powder for anticorrosion pipelines, comprising the following steps:

[0041] 1) Add the raw materials into the high-speed blender according to the formula ratio, and after mixing evenly, extrude and granulate through the twin-screw extruder at a tempera...

Embodiment 2

[0044]A polyethylene powder for anti-corrosion pipelines, prepared from the following raw materials by weight percentage: 8% polyethylene graft adhesive resin, 50% polyolefin matrix resin, 22% polyolefin reinforced resin, toughened Agent 10%, polyacrylate leveling agent 5%, carbon black masterbatch 4.6%, antioxidant 0.4%.

[0045] Wherein, the formula (100%) of polyolefin matrix resin:

[0046] HDPE 60%;

[0047] Low density polyethylene 40%;

[0048] Wherein, the composition of toughening agent is (100%):

[0049] POE 100%;

[0050] Wherein the composition of antioxidant is (100%):

[0051] Antioxidant B245 80%;

[0052] Light stabilizer 20%;

[0053] A preparation method of polyethylene powder for anticorrosion pipelines, comprising the following steps:

[0054] 1) Add the raw materials into the high-speed blender according to the formula ratio, and after mixing evenly, extrude and granulate through the twin-screw extruder at a temperature of 190°C to obtain polyethyl...

Embodiment 3

[0057] A polyethylene powder for anti-corrosion pipelines, prepared from the following raw materials by weight percentage: 10% polyethylene graft adhesive resin, 50% polyolefin matrix resin, 25% polyolefin reinforced resin, toughened Agent 5%, polyacrylate leveling agent 5%, carbon black masterbatch 4.6%, antioxidant 0.4%.

[0058] Wherein, the formula (100%) of polyolefin matrix resin:

[0059] HDPE 50%;

[0060] LDPE 50%;

[0061] Wherein, the toughening agent is composed of:

[0062] POE 50%;

[0063] EVA 50%;

[0064] Wherein the composition of antioxidant is:

[0065]

[0066] A preparation method of polyethylene powder for anticorrosion pipelines, comprising the following steps:

[0067] 1) Add the raw materials into the high-speed blender according to the formula ratio, and after mixing evenly, extrude and granulate through the twin-screw extruder at a temperature of 220°C to obtain polyethylene pellets; the screw speed of the extruder is 400rpm, and the twin-s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses polyethylene powder for an anti-corrosive pipeline and a preparation method for the polyethylene powder. A double-screw extrusion process is adopted for extrusion blending and granulation, and mechanical grinding is carried out to obtain the polyethylene powder; the polyethylene powder is prepared from the following raw materials by weight percent: 5-10% of polyethylene bonding resin, 25-65% of polyolefin matrix resin, 15-30% of polyethylene reinforced resin, 5-20% of a flexibilizer, 0-10% of a leveler, 4-6% of carbon black masterbatch and 0.1-0.5% of an antioxidant. The powder is good in dry powder fluidity and leveling property, excellent in mechanical property, environmental stress crack resistance, ultraviolet aging resistance and pressure resistance, corrosion-resistant and suitable for a powder spreading process and a flame spraying process, and has very high bonding strength with epoxy powder.

Description

technical field [0001] The invention belongs to the field of coatings and relates to the application of functionalized polyethylene and blends thereof, in particular to a polyethylene powder for anti-corrosion pipelines and a preparation method thereof. Background technique [0002] Pipeline and component anticorrosion plays an important role in the overall structure of the national economy, and is related to the safety of use and service life of facilities in fields such as oil transportation, gas transportation, and coal mines. Since the 1990s, the pipeline anti-corrosion field has mostly adopted a three-layer (three-PE) structure, which mainly includes an inner epoxy powder layer, an intermediate adhesive layer, and an outer polyethylene protective layer. In the three-layer structure, the epoxy powder plays the most critical anti-corrosion function, and the middle adhesive layer and the outer polyethylene layer protect the epoxy powder to ensure that the epoxy powder can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D123/06C09D123/08C09D151/06C09D123/16C09D153/02C09D7/12C09D5/08C09D5/46C08F255/02F16L58/10
CPCC08L2201/08C08L2205/025C08L2205/035C08L2207/062C08L2207/066C09D5/03C09D5/08C09D7/40C09D7/61C09D7/63C09D7/65C09D123/06F16L58/10C08L23/06C08L23/0815C08L53/025C08L51/06C08K13/02C08K5/1345C08K3/04C08K5/526C08L33/04C08L23/0853
Inventor 张阳阳伍金奎唐舫成杜壮
Owner GUANGZHOU LUSHAN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap