Wear-resistant polyurethane glossy black finishing paint and preparation method thereof

A polyurethane and topcoat technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve problems such as difficulty in reaching a better level, production cost and time waste, paint gelation and scrapping, etc.

Inactive Publication Date: 2015-06-17
GUANGDONG LANYANG SCI & TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using 1 and 2 methods will lead to waste of production cost and time. Using the third method to use unsaturated polyester paint, although the surface hardness of unsaturated polyester paint is higher, but the use of unsaturated polyester paint There are higher requirements. After the paint is added with blue water cobalt isozincate and white water methyl ethyl ketone peroxide, it can be used for only 20 minutes. If it exceeds this time, the paint will be gelled and scrapped. Caution can lead to waste and quality issues
In terms of use and requirements, it is extremely difficult to achieve a good level

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0153] Embodiment 1, by weight percentage, the composition component of the polyurethane paint of the present embodiment is as follows:

[0154] A component:

[0155] Alkyd 80%,

[0156] Xylene 4%,

[0157] Butyl ester 5%,

[0158] Cyclohexanone 3%,

[0159] Dispersant 1%,

[0160] Carbon black 2%,

[0161] Wear-resistant powder 5%,

[0162] B component:

[0163] TDI trimethylolpropane adduct 60%,

[0164] Butyl ester 40%,

[0165] C component:

[0166] Xylene 50%,

[0167] n-Butyl acetate 20%,

[0168] PMA20%,

[0169] Cyclohexanone 10%,

[0170] According to the above preparation method, three components A, B and C are prepared. When using, mix the three components A, B, and C according to the ratio of 1:0.8-1:0.8-1, (the paint needs to be used up within 4 hours after the oil is mixed) spray or brush the adjusted paint on the Wood surface sprayed with primer; tested after 48 hours of drying at a temperature of 25 degrees, the hardness reached 2H, wiped 50 time...

Embodiment 2

[0171] Embodiment 2, by weight percentage, the composition component of the polyurethane paint of the present embodiment is as follows:

[0172] A component:

[0173] Alkyd 85%,

[0174] Xylene 2%,

[0175] Butyl ester 3%,

[0176] Cyclohexanone 2%,

[0177] Dispersant 1.5%,

[0178] Carbon black 1.5%,

[0179] Wear-resistant powder 5%,

[0180] B component:

[0181] TDI trimethylolpropane adduct 70%

[0182] Butyl ester 30%,

[0183] C component:

[0184] Xylene 45%,

[0185] Butyl fat 30%,

[0186] PMA 15%,

[0187] Cyclohexanone 10%,

[0188] According to the above preparation method, three components A, B and C are prepared. When using, mix the three components A, B, and C according to the ratio of 1:0.8-1:0.8-1, (the paint needs to be used up within 4 hours after the oil is mixed) spray or brush the adjusted paint on the The surface of the wood sprayed with primer; when the temperature is 25 degrees and it is dried for 48 hours, the hardness reaches 2H, and...

Embodiment 3

[0189] Embodiment 3, by weight percentage, the composition component of the polyurethane paint of the present embodiment is as follows:

[0190] A component:

[0191] Alkyd 90%,

[0192] Xylene 1%,

[0193] Butyl ester 1%,

[0194] Cyclohexanone 1%,

[0195] Dispersant 1%,

[0196] Carbon black 1%,

[0197] Wear-resistant powder 5%,

[0198] B component:

[0199] TDI trimethylolpropane adduct 80%,

[0200] Butyl ester 20%,

[0201] C component:

[0202] Xylene 45%,

[0203] n-Butyl acetate 20%,

[0204] PMA 20%,

[0205] Cyclohexanone 15%,

[0206] According to the above preparation method, three components A, B and C are prepared. When using, mix the three components A, B, and C according to the ratio of 1:0.8-1:0.8-1, (the paint needs to be used up within 4 hours after the oil is mixed) spray or brush the adjusted paint on the The surface of the wood sprayed with primer; when the temperature is 25 degrees and it is dried for 48 hours, the hardness reaches 2H,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a wear-resistant polyurethane glossy black finishing paint and a preparation method thereof; the finishing paint is composed of a component A, a component B and a component C; the three components are prepared and packaged respectively; therefore, the storage time is long; and chemical change is difficultly caused. When the wear-resistant polyurethane glossy black finishing paint is used, the solidification time can be adjusted by adjusting the proportion of the three components; and therefore, the wear-resistant polyurethane glossy black finishing paint has higher practicability and production adaptive capacity.

Description

technical field [0001] The invention relates to a high wear-resistant black finish paint, in particular to a wear-resistant polyurethane bright black finish paint. Background technique [0002] Black and white furniture is widely used in daily furniture products due to its eternal tone, such as living room board-type audio-visual furniture with black and white matching, speakers, bedroom furniture, etc., all of which use black and white light as the main products. The surface of polyurethane gloss paint has poor abrasion resistance and scratch resistance, while white paint and other colors of gloss paint are light in color, even if the surface paint film is scratched, it is difficult to see the scratch due to the refraction of light. Therefore, this type of products often use polyurethane paint to meet the requirements, but the products produced by black varnish paint are easy to be scratched by cloth during the process of producing and packaging dust on the products, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D7/12
CPCC09D175/14C08K3/04C08K13/02C09D7/61C09D175/04
Inventor 肖亚亮叶义英
Owner GUANGDONG LANYANG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com