Cold rolled tin-plated steel plate for multiple printing and painting and manufacturing method thereof

A tin-coated steel sheet and a manufacturing method technology, which are applied to cold-rolled tin-coated steel sheets and their manufacture, cold-rolled tin-coated steel sheets that have been repeatedly printed and coated and their manufacturing fields, can solve the problems of easy peeling off of coating films, poor color rendering effect, and adhesion. Poor focus on problems such as poor acid resistance and corrosion resistance, simple implementation methods, and improved physical adhesion

Active Publication Date: 2015-06-17
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF7 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a cold-rolled tin-plated steel sheet for multiple printing and its manufacturing method, which solves the problem of poor adhesion and easy peeling of the coating film of the cold-rolled tin-plated steel sheet used for multiple printing in the prior art , the technical problem of poor color rendering effect after printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold rolled tin-plated steel plate for multiple printing and painting and manufacturing method thereof
  • Cold rolled tin-plated steel plate for multiple printing and painting and manufacturing method thereof
  • Cold rolled tin-plated steel plate for multiple printing and painting and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] The present invention will be further illustrated below in conjunction with specific embodiments, and it should be understood that the following specific embodiments are only used to illustrate the present invention and are not intended to limit the scope of the present invention.

[0038] A method for manufacturing a cold-rolled tin-plated steel sheet for multiple times of printing disclosed by the invention, the method comprising:

[0039] The steps of pickling, cold continuous rolling, continuous annealing, leveling, electro-tinning, passivation, coiling and obtaining finished products for the hot-rolled hard tin-plated original plate with a thickness of 1.8-2.3mm, wherein,

[0040] The chemical composition weight percent of the hot-rolled hard tin-plated raw plate is: C: 0.05%-0.09%, Si≤0.04%, Mn: 0.2%-0.4%, P≤0.02%, S≤0.02%, Alt0.02 %~0.05%, O≤0.004%%, N≤0.0035%, the balance is Fe and unavoidable impurity elements, the yield strength is 250~350MPa, and the tensile ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cold rolled tin-plated steel plate for multiple printing and painting and a manufacturing method thereof, and aims to solve the technical problems that in the prior art, the coating on the conventional cold rolled tin-plated steel plates for multiple printing and painting can be easily peeled off, the adhesive force between the coating and the steel plate is weak, and the color developing effect is bad after printing. The manufacturing method comprises the following steps: washing a hot-rolled hard tin-plated steel plate with a thickness of 1.8 to 2.3 mm by acid, performing continuous cold rolling, carrying out continuous annealing, flattening, electroplating tin on the steel plate, passivating the steel plate, and finally rolling the steel plate to obtain a finished product; wherein the cold rolling reduction ratio is 85 to 90%, the annealing temperature is 550 to 620 DEG C, the temperature is maintained for 60 to 120 seconds, the steel plate is flattened by two machines, the work roller of the first machine is an electro-discharge texturing roller with a Ra of 1.2 to 1.6 um, the rolling force is 500 to 700 t; the work roller of the second machine is a grinding roller with a Ra of 0.3 to 0.5 um, the rolling force is 250 to 350 t; the flattening elongation rate is 1 to 2%, and the passivation is carried out through an electrochemical method and a chemical method. The provided steel plate is mainly used to produce food / beverage cans, which have requirements on multi-color printing.

Description

technical field [0001] The invention relates to a cold-rolled tinned steel plate and a manufacturing method thereof, in particular to a cold-rolled tinned steel plate for multiple printing and a manufacturing method thereof, and belongs to the technical field of iron-based alloys. Background technique [0002] The tin layer of cold-rolled tin-plated steel sheet can provide surface properties such as beautiful metallic luster and good corrosion resistance, and can protect the iron substrate from corrosion under acidic conditions. At the same time, tin compounds are non-toxic and have no effect on the color, taste, and Nutritional value and no adverse effects on human health, so cold-rolled tinned steel sheets are widely used in food cans, beverage cans and other containers. Cold-rolled tinned steel sheets need to be printed many times before being made into food cans and beverage cans and bake. [0003] The manufacturing process of the three-piece can of cold-rolled tin-plat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/06C21D8/02B21D1/02C25D7/06C23F13/00
Inventor 许姣姣韩孝永丁志龙
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com