Novel golf gloves made of similar suede nap and preparation method thereof

A golf and suede technology, applied in the field of golf glove preparation, can solve problems such as poor air permeability, and achieve the effects of increasing high-density acupuncture process, speeding up the grinding speed, and improving dimensional stability.

Active Publication Date: 2015-07-15
重庆瑞美服装有限公司
View PDF13 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] It can be seen from the above-mentioned prior art that the glove leather is obtained by using superfine fiber and polyurethane resin as raw materials through processes such as compounding, grinding and network lines. Although this method uses elastic fabric as the base cloth to ensure the feel and softness of the finished product, but Add resin as the top layer, poor air permeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel golf gloves made of similar suede nap and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) 0.5dtex superfine fiber is used as warp thread, 40dtex polyurethane fiber is used as weft thread, and the warp density is 65 / cm ​​and weft density is 25 / cm to weave to obtain 35g / m 2 elastic woven fabric.

[0031] (2) Use the elastic woven fabric as the base fabric, vacuum impregnate it in polyurethane resin, impregnate it for 1 minute, remove the excess resin on the surface with a scraper, solidify it with an aqueous solution of dimethyl diamide at 35°C for 3 minutes, wash and dry it with water at 50°C, An impregnated woven cloth is obtained.

[0032] (3) The impregnated woven fabric is subjected to high-density needling at a speed of 3 m / min, and the needling density is 2500 needles / cm 2 , the needle punching speed was 300 times / min, and the needle punched woven fabric was obtained, and the needle punched woven fabric was subjected to heat-setting tentering treatment at 100° C. for 2 min, to obtain a shaped woven fabric.

[0033] (4) The two sides of the shaped ...

Embodiment 2

[0036] (1) With 0.8dtex microfiber as warp and 45dtex polyurethane fiber as weft, weaving with warp density 85 / cm and weft density 30 / cm to obtain 55g / m 2 elastic woven fabric.

[0037] (2) Use the elastic woven fabric as the base fabric, vacuum impregnate it in polyurethane resin for 2 minutes, remove the excess resin on the surface with a scraper, solidify and solidify it with an aqueous solution of dimethyl diamide at 40°C for 5 minutes, wash and dry it with water at 60°C, An impregnated woven cloth is obtained.

[0038] (3) The impregnated woven fabric is subjected to high-density needling at a speed of 5 m / min, and the needling density is 3000 needles / cm 2 , the needle punching speed was 300 times / min, and the needle punched woven fabric was obtained, and the needle punched woven fabric was subjected to heat-setting tentering treatment at 100° C. for 5 min, to obtain a shaped woven fabric.

[0039] (4) The two sides of the shaped woven cloth are subjected to grinding tr...

Embodiment 3

[0042] (1) The superfine fiber of 0.67dtex is used as the warp thread, the polyurethane fiber of 42dtex is used as the weft thread, and the warp density is 70 / cm and the weft density is 27 / cm to weave to obtain 40g / m2 elastic woven fabric.

[0043] (2) Use the elastic woven fabric as the base fabric, vacuum impregnate it in polyurethane resin for 2 minutes, remove the excess resin on the surface with a scraper, solidify and solidify it with an aqueous solution of dimethyl diamide at 40°C for 3 minutes, wash and dry it with water at 50°C, An impregnated woven cloth is obtained.

[0044] (3) The impregnated woven fabric is subjected to high-density needle punching at a speed of 4 m / min, and the needle density is 2800 needles / cm 2 , the needle punching speed was 300 times / min, and the needle punched woven fabric was obtained, and the needle punched woven fabric was subjected to heat setting tentering treatment at 100° C. for 3 minutes, to obtain a shaped woven fabric.

[0045] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
thicknessaaaaaaaaaa
dimensional stabilityaaaaaaaaaa
Login to View More

Abstract

The invention provides a pair of novel golf gloves made of similar suede nap and a preparation method thereof. The preparation method comprises the following steps of preparing elastic base fabrics by adopting superfine island fibers and elastic fibers as raw materials and by virtue of combining a needling technology and a suede nap technology, impregnating the elastic base fabrics in a polyurethane resin solution, and solidifying so as to obtain semi-finished products; then performing high-density needling and tentering thermoforming on the semi-finished products; finally raising, roughing and dedusting, thereby obtaining a pair of golf gloves made of the similar suede nap. The pair of novel golf gloves prepared by the preparation method has the characteristics of suede nap, and is fine, dense and soft in fuzz, good in dimensional stability, excellent in air permeability and relatively excellent in comfort. The preparation method is simple and convenient, high in production efficiency and suitable for industrial production.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, and in particular relates to a method for preparing a suede-like golf glove. Background technique: [0002] Suede-like fabrics are widely used in decoration and clothing because of their good velvet feel, fine and soft fluff and waxy texture, and light and thin fabric texture. The suede-like fabric is made of ultra-fine sea-island silk as a raw material, which is spun and woven at high speed to form a suede base fabric, coated with polyurethane, dried, shaped and sanded to obtain a suede-like fabric. The main performance of the fluff of the suede-like fabric is determined by the ultra-fine island-in-the-sea silk raw material and the sanding process. The ultra-fine island-in-the-sea silk contains multiple layers of fibers, and the pores between the fibers are many and dense. , with soft plump, comfortable soft and anti-fouling and other excellent properties. [0003] Golf gloves are o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41D19/00D03D15/00D06B15/00D06B3/10D06C7/02D06M15/564D06M101/38D03D15/283D03D15/33D03D15/56
CPCA41D19/00D06B3/10D06B15/00D06C7/02D06M15/564D06M2101/38D06M2200/50D03D15/56
Inventor 倪勇
Owner 重庆瑞美服装有限公司