Pearl nickel electroplating additive, pearl nickel electroplating solution and electroplating method

A technology of pearl nickel and additives, applied in the field of pearl nickel, can solve the problems of non-softness and poor bright effect of pearl nickel coating, and achieve the effects of soft brightness, good sanding effect and reasonable formula

Inactive Publication Date: 2015-07-22
南京宁美新材料科技有限公司
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are mainly two kinds of pearl nickel coatings: composite electroplating method and emulsifier method. Among them, the emulsifier method is widely used, but the bright effect of the pearl nickel coating obtained by adding the existing emulsifier is not good and not soft.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The additive for pearl nickel electroplating of present embodiment 1 comprises brightener and sand-producing agent; Wherein, described brightener comprises the sodium saccharin of 50g / L and the sodium allyl sulfonate of 30g / L; Described sand-producing agent comprises 0.5g / L of succinate surfactant and 1g / L of carboxylate surfactant.

[0025] The additive for pearl nickel electroplating of this embodiment 1 has good dispersibility in the basic electroplating nickel solution, and the sand-generating agent and the brightener cooperate well, so that in the pearl nickel electroplating process, the surface of the pre-plated part can be evenly sanded and sanded. Good effect, reduce internal stress.

Embodiment 2

[0027] The additive for pearl nickel electroplating of present embodiment 2 comprises brightener and sand producing agent; Wherein, described brightener comprises the sodium saccharin of 40g / L and the sodium allyl sulfonate of 20g / L; Described sand producing agent comprises 0.1g / L of succinate surfactant and 0.5g / L of carboxylate surfactant.

[0028] The additive for pearl nickel electroplating of this embodiment 2 has good dispersibility in the basic electroplating nickel solution, and the sand-generating agent and the brightener cooperate well, so that in the pearl nickel electroplating process, the surface of the pre-plated part can be evenly sanded and sanded. Good effect, reduce internal stress.

Embodiment 3

[0030] The additive for pearl nickel electroplating of present embodiment 3 comprises brightener and sand-producing agent; Wherein, described brightener comprises the sodium saccharin of 60g / L and the sodium allyl sulfonate of 40g / L; Described sand-producing agent comprises 0.6g / L of succinate surfactant and 1.5g / L of carboxylate surfactant.

[0031] The additive for pearl nickel electroplating of present embodiment 3 has good dispersibility in the basic electroplating nickel solution, and the sanding agent and the brightener cooperate well, so that in the pearl nickel electroplating process, the surface of the pre-plated part can evenly sand and sand Good effect, reduce internal stress.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a pearl nickel electroplating additive, a pearl nickel electroplating solution and an electroplating method. The pearl nickel electroplating additive comprises a brightening agent and a frosting agent, wherein the brightening agent comprises saccharin sodium and sodium allylsulfonate, and the frosting agent comprises succinate salt type surfactants and carboxylate type surfactants. The pearl nickel electroplating solution comprises a basic electronickelling solution and the pearl nickel electroplating additive. The electroplating method comprises the following steps: preparingthe pearl nickel electroplating solution; regulating the pH value and the temperature of the electroplating solution, and then performing electronickelling by using a preplating piece as a cathode. The pearl nickel electroplating additive disclosed by the invention is reasonable in formula, the dispersibility of the basic electronickelling solution is good, the frosting agent and the brightening agent mutually cooperate and act to enable the surface of the preplating piece to be uniformly frostedin a pearl nickel electroplating process, the frosting effect is good, the internal stress is ecreased, and the obtained pearl nickel plate is glossy, good in brightness and gentle.

Description

technical field [0001] The invention relates to the technical field of pearl nickel, in particular to an additive for pearl nickel electroplating, a pearl nickel electroplating solution and an electroplating method. Background technique [0002] Pearl nickel, also known as satin nickel, satin nickel, pitted nickel, is a coating with gorgeous appearance, fine and soft color, low internal stress, good corrosion resistance, and is a good protective decorative coating. The pearl nickel electroplating process first appeared in the 1950s and developed rapidly after the 1990s. Pearl nickel can be directly used as a protective decorative coating, and other metals, such as chromium, gold, silver, etc., can also be plated on pearl nickel, which has a stronger protective decorative effect. At present, pearl nickel coating has been widely used in automobile decoration, electronic products, daily hardware, stationery and other industries. [0003] At present, there are mainly two kinds...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D3/12
Inventor 许荣国
Owner 南京宁美新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com