Conveyer belt with high abrasion resistance

A conveyor belt, high wear-resistant technology, applied in the field of conveyor belts, can solve the problems of reducing the impact and wear strength of the covering rubber layer, the overall toughness and tear resistance, and the impact on the life of the conveyor belt, so as to avoid loss of belt core, Improve dispersion and good impact resistance

Active Publication Date: 2015-08-12
ZHEJIANG SANWEI RUBBER ITEM CO LTD
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the main defects of the high wear-resistant conveyor belt produced at home and abroad in the process of use: when conveying large and sharp materials, the covering rubber on the working surface of the belt is worn out early, cut into small rubber particles by the material and scrapped, and the service life is short
[0004] Chinese patent CN201485013U discloses a super wear-resistant conveyor belt, which includes an upper wear-resistant layer and a lower wear-resistant layer, both of which are made of polyurethane and smoked sheet glue. Rubber-dipped aramid cord fabric layer and metal spiral core layer, the conveyor belt with this structure has good impact resistance and wear resistance, but because the single layer covers the wear-resistant layer, the overall toughness and tear resistance are not strong, and the service life is still not long
Chinese patent CN203111941U discloses a high-temperature-resistant and wear-resistant conveyor belt, which includes an upper cover rubber layer, a belt core and a lower cover rubber layer, wherein the belt core is nylon mesh or steel cord mesh, which can reduce the impact of materials on the cover rubber layer. Impact wear strength, but the cushioning force is not enough, which has little effect on the life of the conveyor belt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conveyer belt with high abrasion resistance
  • Conveyer belt with high abrasion resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Such as figure 1Shown, a kind of high wear-resisting conveyer belt comprises upper cover adhesive layer 1, belt core (canvas) 2 and lower cover adhesive layer 3, and described upper cover adhesive layer 1 is made of anti-cut adhesive layer (thickness 3mm) 11 and resistant The wear-resistant rubber layer (thickness 3mm) 12 is composed of a tear-resistant skeleton layer 4 between the wear-resistant rubber layer 12 and the belt core 2 . The tear-resistant skeleton layer is composed of two layers of steel mesh with a thickness of about 2mm. The specification of the steel mesh is: the diameter of the steel wire is 1mm, and the mesh size of the steel mesh is 10mm×10mm. The lower cover adhesive layer 3 material is the same as the wear-resistant adhesive layer.

[0035] The material formulation of the anti-cut adhesive layer is as follows in parts by weight:

[0036] 85 parts of smoked sheet rubber, 35 parts of butadiene rubber (butadiene rubber br9000, commercially available...

Embodiment 2

[0044] Such as figure 1 Shown, a kind of high wear-resisting conveyer belt comprises upper cover adhesive layer 1, belt core (canvas) 2 and lower cover adhesive layer 3, and described upper cover adhesive layer 1 is made of anti-cut adhesive layer (thickness 3mm) 11 and resistant The wear-resistant rubber layer (thickness 6mm) 12 is composed of a tear-resistant skeleton layer 4 between the wear-resistant rubber layer 12 and the belt core 2 . The tear-resistant skeleton layer is composed of two layers of steel mesh with a thickness of about 2mm. The specification of the steel mesh is: the diameter of the steel wire is 1mm, and the mesh size of the steel mesh is 10mm×10mm. The lower cover adhesive layer 3 material is the same as the wear-resistant adhesive layer.

[0045] The material formulation of the anti-cut adhesive layer is as follows in parts by weight:

[0046] 95 parts of smoked sheet rubber, 25 parts of butadiene rubber, 50 parts of carbon black N110 (commercially av...

Embodiment 3

[0053] Such as figure 1 Shown, a kind of high wear-resisting conveyer belt comprises upper cover adhesive layer 1, belt core (canvas) 2 and lower cover adhesive layer 3, and described upper cover adhesive layer 1 is made of anti-cut adhesive layer (thickness 3mm) 11 and resistant The wear-resistant rubber layer (thickness 5mm) 12 is composed of a tear-resistant skeleton layer 4 between the wear-resistant rubber layer 12 and the belt core 2 . The tear-resistant skeleton layer is composed of two layers of steel mesh with a thickness of about 2mm. The specification of the steel mesh is: the diameter of the steel wire is 1mm, and the mesh size of the steel mesh is 10mm×10mm. The lower cover adhesive layer 3 material is the same as the wear-resistant adhesive layer.

[0054] The material formulation of the anti-cut adhesive layer is as follows in parts by weight:

[0055] 90 parts of smoked sheet rubber, 30 parts of butadiene rubber (butadiene rubber br9000, commercially availabl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a conveyer belt with high abrasion resistance. The conveyer belt comprises an upper covering adhesive layer, a belt core and a lower covering adhesive layer, wherein the upper covering adhesive layer is composed of a cutting-resistant adhesive layer and an abrasion-resistant adhesive layer; and an anti-tear skeleton layer is arranged between the abrasion-resistant adhesive layer and the belt core. The conveyer belt has good abrasion resistance, impact resistance and elasticity, and is long in service life and suitable for being used in mines and other occasions with relatively high abrasion.

Description

technical field [0001] The invention relates to a conveyor belt, in particular to a high wear-resistant conveyor belt. Background technique [0002] Belt conveyor is one of the most common and economical material conveying methods. In particular, the super wear-resistant conveyor belt has unique advantages that other products cannot replace due to its strong wear resistance, impact resistance and high elasticity. Therefore, it is widely used in metallurgy, mining, docks and other industries, showing super wear Abrasive conveyor belts have broad market prospects in material transportation and have significant social and economic benefits. [0003] At present, many conveyor belt manufacturers at home and abroad are developing and producing super wear-resistant conveyor belts, but there is no major progress. At present, the main defects of the high wear-resistant conveyor belt produced at home and abroad in the process of use: when conveying large and sharp materials, the cov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B65G15/34C08L7/00C08L9/00C08L23/06C08K13/06C08K9/06C08K9/02C08K7/14C08K7/24C08K7/08C08K3/04C08K3/22C08K5/09
CPCB65G15/34C08L7/00C08L9/00C08L2205/02C08L2205/025C08L2205/035C08L2205/16C08L2207/062C08L23/06C08L91/00C08L57/02C08L91/06C08K13/06C08K9/06C08K9/02C08K7/14C08K3/04C08K2003/2296C08K5/09C08K7/24C08K7/08C08K3/06
Inventor 吴兰友
Owner ZHEJIANG SANWEI RUBBER ITEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com